NASA NTRS2018

Study of Skin-Stringer Separation in Postbuckled Composite Aeronautical Structures

Aeronautical composite stiffened structures have the capability to carry loads deep into postbuckling, yet they are typically designed to operate below the buckling load to avoid potential issues with durability and structural integrity. Large out-of-plane postbuckling deformation of the skin can result in the opening of the skin-stringer interfaces, especially in the presence of defects, such as impact damage. To ensure that skin-stringer separation does not propagate in an unstable mode that can cause a complete collapse of the structure, a deeper understanding of the interaction between the postbuckling deformation and the development of damage is required. The present study represents a first step towards a methodology based on analysis and experiments to assess and improve the strength, life, and damage tolerance of stiffened composite structures subjected to postbuckling deformations. Two regions were identified in a four-stringer panel in which skin-stringer separation can occur, namely the region of maximum deflection and the region of maximum twisting. Both regions have been studied using a finite element model of a representative single-stringer specimen. For the region of maximum deflection, a seven-point bending configuration was used, in which five supports and two loading points induce buckling waves to the specimen. The region of maximum twisting was studied using an edge crack torsion configuration, with two supports and two loading points. These two configurations were studied by changing the positions of the supports and the loading points. An optimization procedure was carried out to minimize the error between the out-of-plane deformation of the representative single-stringer specimen and the corresponding region of the four-stringer panel.

Kootte, Lucas J.↗

NASA NTRS2018

Scaling Methodology for Buckling of Sandwich Composite Cylindrical Structures

The study of the buckling behavior of large shell structures through full-size tests can be complex and expensive. Therefore, scaled structures are often preferred to investigate the buckling behavior efficiently. However, it can be difficult to design scaled structures that are representative of the full-scale structures. Herein, an analytical scaling methodology for compression-loaded sandwich composite cylinders based on the nondimensionalization of the buckling equations is presented. The methodology is used to develop scaled configurations that show a similar buckling response. Both the baseline and the scaled configurations are verified by finite-element analysis. Limitations of the methodology are discussed and are a result of neglecting the flexural anisotropy and the transverse shear compliance.

Balbin, Ines Uriol↗

NASA NTRS2017

Fatigue Life and Damage Tolerance of Postbuckled Composite Stiffened Structures with Indentation Damage

The fatigue life and damage tolerance of composite stiffened panels with indentation damage are investigated experimentally using single-stringer compression specimens. The indentation damage was induced to one of the two flanges of the stringer of every panel. The advantages of indentation compared to impact are the simplicity of application, less dependence on boundary conditions, better controllability, and repeatability of the imparted damage. The tests were conducted using advanced instrumentation, including digital image correlation, passive thermography, and in situ ultrasonic scanning. Specimens with initial indentation damage ranging between 32 and 56 mm in length were tested quasi-statically and in fatigue, and the effects of cyclic load amplitude and damage size were studied. A means of comparison of the damage propagation rates and collapse loads based on a stress intensity measure and the Paris law is proposed. The stress intensity measure provides the means to compare the collapse loads of specimens with different damage types and damage sizes, while the Paris law is used to compare the damage propagation rates in specimens subjected to different cyclic loads. This approach enables a comparison of different tests and the potential identification of the effects that influence the fatigue lives and damage tolerance of postbuckled structures with defects.

Davila, Carlos G.↗

NASA NTRS2016

Fatigue Life of Postbuckled Structures with Indentation Damages

The fatigue life of composite stiffened panels with indentation damage was investigated experimentally using single stringer compression specimens. Indentation damage was induced on one of the two flanges of each stringer. The experiments were conducted using advanced instrumentation, including digital image correlation, passive thermography, and in-situ ultrasonic scanning. Specimens with initial indentation damage lengths of 32 millimeters to 56 millimeters were tested quasi-statically and in fatigue, and the effects of cyclic load amplitude and damage size were studied. A means of comparison of the damage propagation rates and collapse loads based on a stress intensity measure and the Paris law is proposed.

Davila, Carlos G.↗

NASA NTRS2016

Fatigue Life of Postbuckled Structures with Indentation Damage

The fatigue life of composite stiffened panels with indentation damage was investigated experimentally using single stringer compression specimens. Indentation damage was induced on one of the two flanges of the stringer. The experiments were conducted using advanced instrumentation, including digital image correlation, passive thermography, and in-situ ultrasonic scanning. Specimens with initial indentation damage lengths of 37 millimeters to 56 millimeters were tested in fatigue and the effects of cyclic load amplitude and damage size were studied. A means of comparison of the damage propagation rates and collapse loads based on a stress intensity measure and the Paris law is proposed.

Davila, Carlos G.↗

NASA NTRS2015

Effect of Buckling Modes on the Fatigue Life and Damage Tolerance of Stiffened Structures

The postbuckling response and the collapse of composite specimens with a co-cured hat stringer are investigated experimentally and numerically. These specimens are designed to evaluate the postbuckling response and the effect of an embedded defect on the collapse load and the mode of failure. Tests performed using controlled conditions and detailed instrumentation demonstrate that the damage tolerance, fatigue life, and collapse loads are closely tied with the mode of the postbuckling deformation, which can be different between two nominally identical specimens. Modes that tend to open skin/stringer defects are the most damaging to the structure. However, skin/stringer bond defects can also propagate under shearing modes. In the proposed paper, the effects of initial shape imperfections on the postbuckling modes and the interaction between different postbuckling deformations and the propagation of skin/stringer bond defects under quasi-static or fatigue loads will be examined.

Davila, Carlos G.↗

NASA NTRS2014

Experimental Evaluation of Fatigue Damage Progression in Postbuckled Single Stringer Composite Specimens

The durability and damage tolerance of postbuckled composite structures are not yet completely understood, and remain difficult to predict due to the nonlinearity of the geometric response and its interaction with local damage modes. A research effort was conducted to investigate experimentally the quasi-static and fatigue damage progression in a single-stringer compression (SSC) specimen. Three specimens were manufactured with a hat-stiffener, and an initial defect was introduced with a Teflon film embedded between one flange of the stringer and the skin. One of the specimens was tested under quasi-static compressive loading, while the remaining two specimens were tested by cycling in postbuckling. The tests were performed at the NASA Langley Research Center under controlled conditions and with instrumentation that allows a precise evaluation of the postbuckling response and of the damage modes. Three-dimensional digital image correlation VIC-3D systems were used to provide full field displacements and strains on the skin and the stringer. Passive thermal monitoring was conducted during the fatigue tests using an infrared camera that showed the location of the delamination front while the specimen was being cycled. The live information from the thermography was used to stop the fatigue tests at critical stages of the damage evolution to allow detailed ultrasonic scans.

Bisagni, Chiara↗

NASA NTRS2013

Modeling Delamination in Postbuckled Composite Structures Under Static and Fatigue Loads

The ability of the Abaqus progressive Virtual Crack Closure Technique (VCCT) to model delamination in composite structures was investigated for static, postbuckling, and fatigue loads. Preliminary evaluations were performed using simple Double Cantilever Beam (DCB) and Mixed-Mode Bending (MMB) specimens. The nodal release sequences that describe the propagation of the delamination front were investigated. The effect of using a sudden or a gradual nodal release was evaluated by considering meshes aligned with the crack front as well as misaligned meshes. Fatigue simulations were then performed using the Direct Cyclic Fatigue (DCF) algorithm. It was found that in specimens such as the DCB, which are characterized by a nearly linear response and a pure fracture mode, the algorithm correctly predicts the Paris Law rate of propagation. However, the Abaqus DCF algorithm does not consider different fatigue propagation laws in different fracture modes. Finally, skin/stiffener debonding was studied in an aircraft fuselage subcomponent in which debonding occurs deep into post-buckling deformation. VCCT was shown to be a robust tool for estimating the onset propagation. However, difficulties were found with the ability of the current implementation of the Abaqus progressive VCCT to predict delamination propagation within structures subjected to postbuckling deformations or fatigue loads.

Bisagni, Chiara↗

NASA NTRS2012

Simplified Models for the Study of Postbuckled Hat-Stiffened Composite Panels

The postbuckling response and failure of multistringer stiffened panels is analyzed using models with three levels of approximation. The first model uses a relatively coarse mesh to capture the global postbuckling response of a five-stringer panel. The second model can predict the nonlinear response as well as the debonding and crippling failure mechanisms in a single stringer compression specimen (SSCS). The third model consists of a simplified version of the SSCS that is designed to minimize the computational effort. The simplified model is well-suited to perform sensitivity analyses for studying the phenomena that lead to structural collapse. In particular, the simplified model is used to obtain a deeper understanding of the role played by geometric and material modeling parameters such as mesh size, inter-laminar strength, fracture toughness, and fracture mode mixity. Finally, a global/local damage analysis method is proposed in which a detailed local model is used to scan the global model to identify the locations that are most critical for damage tolerance.

Vescovini, Riccardo↗

NASA NTRS2010

Assessment of the Damage Tolerance of Postbuckled Hat-Stiffened Panels Using Single-Stringer Specimens

A procedure is proposed for the assessment of the damage tolerance and collapse of stiffened composite panels using a single-stringer compression specimen. The dimensions of the specimen are determined such that the specimen s nonlinear response and collapse are representative of an equivalent multi-stringer panel in compression. Experimental tests are conducted on specimens with and without an embedded delamination. A shell-based finite element model with intralaminar and interlaminar damage capabilities is developed to predict the postbuckling response as well as the damage evolution from initiation to collapse.

Bisagni, Chiara↗