Radiation-Induced Modifications in Copper Oxide Growth
Radiation-induced effects and their influence on oxidation processes were evaluated for their use as a forensic tool for special nuclear material (SNM). A beam of 10 MeV Au³⁺ ions was used to mimic the accumulation of microstructural damage from self-irradiation through the decay of radionuclides. Several copper samples were irradiated as suitable surrogate materials at 200 °C with a flux of 1x10¹² ions/cm·s to damage levels of 5, 10, and 15 displacements per atom (dpa). This corresponds to about 50, 100, and 150 years, respectively, of accumulated α-decay damage in a PuGa alloy assuming a damage rate of 0.1 dpa/year. After irradiation, all samples were exposed to an accelerated aging process induced by thermal treatment at 350 °C for 1 hour in air. This resulted in the growth of a mixed oxide layer (Cu₂O and CuO) which was characterized in detail using several complementary analytical techniques: Scanning Electron Microscopy, Raman spectroscopy, Synchrotron X-ray diffraction (transmission mode), and Grazing Incidence X-ray diffraction. The oxide layer growth of irradiated Cu at 350°C is distinctly modified as a result of the ion irradiation. Most notably, the growth of the CuO phase is suppressed with increasing radiation damage on the Cu substrate, and structural changes occurred in the Cu₂O phase. These results indicate that damage from self-irradiation over time can cause quantifiable modifications in the oxidation process of metals that could be harnessed for their use as a novel forensic tool.