Evaporated CdSe for Efficient Polycrystalline CdSeTe Thin-Film Solar Cells

Recent progress has shown that alloying cadmium telluride (CdTe) with cadmium selenide (CdSe) to create a CdSexTe1-x (CdSeTe) gradient region can significantly boost the performance of polycrystalline CdSeTe thin-film solar cells. However, improper CdSeTe alloying might introduce problematic band alignment and deleterious voids at the front interface, limiting the benefit maximization of this technique. Here, we show that the CdSe layers deposited by thermal evaporation result in CdSeTe cells with a higher performance than the sputtered CdSe. This is because evaporated CdSe can avoid the formation of voids at the front interface, producing improved front junction quality with suppressed front junction nonradiative recombination. The champion cell using evaporated CdSe demonstrated a power conversion efficiency (PCE) of 19.7%, much higher than 18.1% in the cell using sputtered CdSe.

cadmium selenide↗
DOE OSTI2023

Oxygen Management to Avoid Photo-Inactive Cd(S,Se) for Efficient Cd(Se,Te) Solar Cells

Our previous work has demonstrated that the formation of a penternary cadmium chalcogenide Cd(O,S,Se,Te) region can significantly reduce the front interface recombination in Cd(Se,Te)-based thin-film solar cells. In this work, we have shown that oxygen management during the device fabrication is crucial to form this region. While both the CdS and CdSe layer depositions and the postdeposition CdCl2 treatment should be conducted in the presence of oxygen, the CdTe deposition should be conducted in an oxygen-free atmosphere. Improper oxygen management leads to low device performance due to the formation of a photoinactive Cd(S,Se) region and reduced absorber quality. Additionally, we investigated the carrier transport and collection properties in devices with photoinactive Cd(S,Se) and photoactive Cd(O,S,Se,Te) at the front interface to gain comprehensive understanding of the mechanisms that resulted in improved efficiencies approaching 20%.

CdTe deposition↗
DOE OSTI2022

Post‐Annealing Treatment on Hydrothermally Grown Antimony Sulfoselenide Thin Films for Efficient Solar Cells

Herein, antimony sulfoselenide (Sb 2 (S, Se) 3 ) thin‐film solar cells are fabricated by a hydrothermal method followed by a post‐deposition annealing process at different temperatures and the impact of the annealing temperature on the morphological, structural, optoelectronic, and defect properties of the hydrothermally grown Sb 2 (S, Se) 3 films is investigated. It is found that a proper annealing temperature leads to high‐quality Sb 2 (S, Se) 3 films with large crystal grains, high crystallinity, preferred crystal orientation, smooth and uniform morphology, and reduced defect density. These results show that suppressing deep‐level defects is crucial to enhance solar cell performance. After optimizing the annealing process, Sb 2 (S, Se) 3 solar cells with an improved power conversion efficiency 2.04 to 8.48% are obtained.

14 SOLAR ENERGY↗
DOE OSTI2022

20%-efficient polycrystalline Cd(Se,Te) thin-film solar cells with compositional gradient near the front junction

Bandgap gradient is a proven approach for improving the open-circuit voltages (V OC s) in Cu(In,Ga)Se 2 and Cu(Zn,Sn)Se 2 thin-film solar cells, but has not been realized in Cd(Se,Te) thin-film solar cells, a leading thin-film solar cell technology in the photovoltaic market. Here, we demonstrate the realization of a bandgap gradient in Cd(Se,Te) thin-film solar cells by introducing a Cd(O,S,Se,Te) region with the same crystal structure of the absorber near the front junction. The formation of such a region is enabled by incorporating oxygenated CdS and CdSe layers. We show that the introduction of the bandgap gradient reduces the hole density in the front junction region and introduces a small spike in the band alignment between this and the absorber regions, effectively suppressing the nonradiative recombination therein and leading to improved VOCs in Cd(Se,Te) solar cells using commercial SnO 2 buffers. A champion device achieves an efficiency of 20.03% with a V OC of 0.863 V.

14 SOLAR ENERGY↗
DOE OSTI2021

Templated Growth and Passivation of Vertically Oriented Antimony Selenide Thin Films for High-Efficiency Solar Cells in Substrate Configuration

Antimony selenide (Sb 2 Se 3 ) is a promising low-cost photovoltaic material with a 1D crystal structure. The grain orientation and defect passivation play a critical role in determining the performance of polycrystalline Sb 2 Se 3 thin-film solar cells. In this work, a seed layer is introduced on a molybdenum (Mo) substrate to template the growth of a vertically oriented, columnar Sb 2 Se 3 absorber layer by closed space sublimation. By controlling the grain orientation and compactness of the Sb 2 Se 3 seeds, obtain high-quality Sb 2 Se 3 absorber layers with passive Sb 2 Se 3 /Mo interfaces is obtained, which in turn improve the transport of photoexcited charge carriers through the absorber layer and its interfaces. Post-deposition annealing of absorber layers in ambient air is further utilized to passivate the defects in Sb 2 Se 3 and enhance the quality of the front heterojunction. As a result of systematic processing optimization, Sb 2 Se 3 planar heterojunction solar cells are fabricated in substrate configuration with a champion power conversion efficiency of 8.5%.

14 SOLAR ENERGY↗
DOE OSTI2020

Effects of post-deposition CdCl 2 annealing on electronic properties of CdTe solar cells

The effects of post-deposition CdCl 2 annealing temperature on the electronic properties of CdTe solar cells were investigated. CdTe devices incorporate Mg doped ZnO as a buffer layer and selenization using a CdSe interlayer for reducing the buffer/absorber interface recombination and increasing solar energy absorption respectively. The post-deposition CdCl 2 annealing treatments were done under separate, inert atmospheres of nitrogen and helium across the temperature range 380 to 430 °C. Electrical characterization of devices is carried out including temperature dependent current-voltage characteristics, admittance spectroscopy, and Shockley-Read-Hall recombination analysis. Here, the best improvements in device efficiency are obtained upon annealing at temperature 410 °C. This anneal correlated with reduced back contact barrier in CdTe and reduced grain-boundary barrier height which is beneficial for enhanced charge transport.

14 SOLAR ENERGY↗
DOE OSTI2020

Semi-transparent p-type barium copper sulfide as a back contact interface layer for cadmium telluride solar cells

Optically transparent p-type materials play a critical role in transparent electronics including photovoltaic (PV) devices. P-type sulfide materials offer an alternative to oxides for PV application due to improved hole transport properties. Here, we report the solution-based synthesis of earth-abundant p-type transparent conducting barium copper sulfide (α-BaCu 4 S 3 , BCS) thin films. These films were characterized using scanning electron microscopy, X-ray diffraction, UV–Vis–NIR spectrophotometry, Raman spectroscopy, and spectroscopic ellipsometry. BCS films of ~100 nm thickness transmit >70% of visible light. We report on tests of the hole transport properties of these BCS films for cadmium telluride (CdTe) photovoltaics, finding that the BCS deposition process forms a beneficial tellurium (Te) rich surface on CdTe by selectively removing Cd from the surface. Based on our study, the BCS interface layer plays dual functions for CdTe PV devices as a hole transport material and as an etchant, enhancing the resulting device performance. We observed a significant increase in open-circuit voltage of CdTe solar cells with the BCS buffer layer. Furthermore, we discuss semitransparent CdTe solar cells with BCS as a hole transport layer and indium tin oxide as a finishing electrode. Semitransparent CdTe solar cells shows 13.3% conversion efficiency for the front side illumination and 1.2% efficiency for back side illumination, indicating high recombination of charge carriers generated close to the rear CdTe/BCS/ITO contact.

36 MATERIALS SCIENCE↗