JWST Near-Infrared Detector Degradation: Finding the Problem, Fixing the Problem, and Moving Forward
The James Webb Space Telescope (JWST) is the successor to the Hubble Space Telescope. JWST will be an infrared optimized telescope, with an approximately 6.5 m diameter primary mirror, that is located at the Sun-Earth L2 Lagrange point. Three of JWST's four science instruments use Teledyne HgCdTe HAWAII-2RG (H2RG) near infrared detector arrays. During 2010, the JWST Project noticed that a few of its 5 micron cutoff H2RG detectors were degrading during room temperature storage, and NASA chartered a "Detector Degradation Failure Review Board" (DD-FRB) to investigate. The DD-FRB determined that the root cause was a design flaw that allowed indium to interdiffuse with the gold contacts and migrate into the HgCdTe detector layer. Fortunately, Teledyne already had an improved design that eliminated this degradation mechanism. During early 2012, the improved H2RG design was qualified for flight and JWST began making additional H2RGs. In this article we present the two public DD-FRB "Executiye Summaries" that: (1) determined the root cause of the detector degradation and (2) defined tests to determine whether the existing detectors are qualified for flight. We supplement these with a brief introduction to H2RG detector arrays, and a discussion of how the JWST Project is using cryogenic storage to retard the degradation rate of the existing flight spare H2RGs.
Rauscher, Bernard J.↗
Upgrades to Electronic Speckle Interferometer (ESPI) Operation and Data Analysis at NASA's Goddard Space Flight Center
The authors report operational upgrades and streamlined data analysis of a commissioned electronic speckle interferometer (ESPI) in a permanent in-house facility at NASA's Goddard Space Flight Center. Our ESPI was commercially purchased for use by the James Webb Space Telescope (JWST) development team. We have quantified and reduced systematic error sources, improved the software operability with a user-friendly graphic interface, developed an instrument simulator, streamlined data analysis for long-duration testing, and implemented a turn-key approach to speckle interferometry. We also summarize results from a test of the JWST support structure (previously published), and present new results from several pieces of test hardware at various environmental conditions.
Connelly, Joseph↗
Development of a Cryogenic Thermal Distortion Measurement Facility for Testing the James Webb Space Telescope Instrument Support Integration Module 2-D Test Assemblies
The James Webb Space Telescope Instrument Support Integration Module (ISIM) is being designed and developed at the Goddard Space Flight Center. The ISM Thermal Distortion Testing (ITDT) program was started with the primary objective to validate the ISM mechanical design process. The ITDT effort seeks to establish confidence and demonstrate the ability to predict thermal distortion in composite structures at cryogenic temperatures using solid element models. This-program's goal is to better ensure that ISIM meets all the mechanical and structural requirements by using test results to verify or improve structural modeling techniques. The first step to accomplish the ITDT objectives was to design, and then construct solid element models of a series 2-D test assemblies that represent critical building blocks of the ISIM structure. Second, the actual test assemblies consisting of composite tubes and invar end fittings were fabricated and tested for thermal distortion. This paper presents the development of the GSFC Cryo Distortion Measurement Facility (CDMF) to meet the requirements of the ISIM 2-D test. assemblies, and other future ISIM testing needs. The CDMF provides efficient cooling with both a single, and two-stage cryo-cooler. Temperature uniformity of the test assemblies during thermal transients and at steady state is accomplished by using sapphire windows for all of the optical ports on the radiation shields and by using .thermal straps to cool the test assemblies. Numerical thermal models of the test assemblies were used to predict the temperature uniformity of the parts during cooldown and at steady state. Results of these models are compared to actual temperature data from the tests. Temperature sensors with a 0.25K precision were used to insure that test assembly gradients did not exceed 2K lateral, and 4K axially. The thermal distortions of two assemblies were measured during six thermal cycles from 320K to 35K using laser interferometers. The standard deviation for all of the distortion measurements is less than 0.5 microns, which falls within the ISIM requirement of 3 microns.
Miller, Franklin↗
Cryogenic System for Interferometric Measurement of Dimensional Changes at 40 K: Design and Performance
This report describes the facility, experimental methods, characterizations, and uncertainty analysis of the Cryo Distortion Measurement Facility (CDMF) at the Goddard Space Flight Center (GSFC). This facility is designed to measure thermal distortions of structural elements as the temperature is lowered from 320K to below 40 K over multiple cycles, and is capable of unattended running and data logging. The first measurement is to be the change in length and any bending of composite tubes with Invar end-fittings. The CDMF includes a chamber that is efficiently cooled with two cryo-coolers (one single-stage and one two-stage) rather than with liquid cryogens. Five optical ports incorporate sapphire radiation shields - transparent to the interferometer - on each of two shrouds and a fused silica vacuum-port window. The change in length of composite tubes is monitored continuously with displacement-measuring interferometers; and the rotations, bending, and twisting are measured intermittently with theodolites and a surface-figure interferometer. Nickel-coated invar mirrors and attachment mechanisms were developed and qualified by test in the CDMF. The uncertainty in measurement of length change of 0.4 m tubes is currently estimated at 0.9 micrometers.
Blake, Peter↗
Minimizing Uncertainty in Cryogenic Surface Figure Measurement
A new facility at the Goddard Space Flight Center is designed to measure with unusual accuracy the surface figure of mirrors at cryogenic temperatures down to 12 K. The facility is currently configured for spherical mirrors with a radius of curvature (ROC) of 600 mm, and apertures of about 150 mm or less. The goals of the current experiment were to 1) Obtain the best possible estimate of test mirror surface figure, S(x,y) at 87 K and 20 K; 2) Obtain the best estimate of the cryo-change, Delta (x,y): the change in surface figure between room temperature and the two cryo-temperatures; and 3) Determine the uncertainty of these measurements, using the definitions and guidelines of the ISO Guide to the Expression of Uncertainty in Measurement. A silicon mirror was tested, and the cry-change from room temperature to 20K was found to be 3.7 nm rms, with a standard uncertainty of 0.23 nm in the rms statistic. Both the cryo-change figure and the uncertainty are among the lowest such figures yet published. This report describes the facilities, experimental methods, and uncertainty analysis of the measurements.
Blake, Peter↗
Surface Figure Measurement of Silicon Carbide Mirrors at Cryogenic Temperatures
The surface figure of a developmental silicon carbide mirror, cooled to 87 K and then 20 K within a cryostat, was measured with unusually high precision at the Goddard Space Flight Center (GSFC). The concave spherical mirror, with a radius of 600 mm and a clear aperture of 150 mm, was fabricated of sintered silicon carbide. The mirror was mounted to an interface plate representative of an optical bench, made of the material Cesic@, a composite of silicon, carbon, and silicon carbide. The change in optical surface figure as the mirror and interface plate cooled from room temperature to 20 K was 3.7 nm rms, with a standard uncertainty of 0.23 nm in the rms statistic. Both the cryo-change figure and the uncertainty are among the lowest such figures yet published. This report describes the facilities, experimental methods, and uncertainty analysis of the measurements.
Blake, Peter↗
Surface Figure Measurement at 20K: Silicon Carbide and Cesic Mirrors
This report presents the facility, methods, and results of testing cryogenically-cooled spherical mirrors, using standard phase-shifting interferometry, at the Goddard Space Flight Center (GSFC). Two mirrors were supplied to GSFC by the European Space Technology Center, so that GSFC could render a second, independent cryo-measurement of their surface figures at 20K. These mirrors, produced by Galileo Avionica and its partners, demonstrate the technology of silicon carbide and SiC-composite lightweighted mirrors, designed for high accuracy (10 nm rms surface figure error) at both room temperature and 20K. The two mirrors provided for testing at GSFC include one made of sintered silicon carbide (mirror blank by Bettini), and a second made of the C/Si/SiC composite known as Cesic (supplied by ECM). Both mirrors are f/2 spheres with 150 mm clear aperture, and with integral mounts. At GSFC, the mirrors will be measured first at at room temperature, making use of standard techniques, with a predicted uncertainty of 2 nm. Then each mirror will be tested in the cryostat, down to 20K: first freely supported and, second, mounted to a Cesic plate that models a Cesic optical bench. The uncertainty of the resultant surface figure error is predicted to be about 5 nm rms. Details of the uncertainty budget are discussed in a related poster. GSFC's techniques and results can be usefully compared to the measurements performed on the same two mirrors by and for Galileo Avionica, who used a somewhat different test configuration and alignment approach.
Blake, Peter↗
High-Accuracy Surface Figure Measurement of Silicon Mirrors at 80 K
This report describes the equipment, experimental methods, and first results at a new facility for interferometric measurement of cryogenically-cooled spherical mirrors at the Goddard Space Flight Center Optics Branch. The procedure, using standard phase-shifting interferometry, has an standard combined uncertainty of 3.6 nm rms in its representation of the two-dimensional surface figure error at 80, and an uncertainty of plus or minus 1 nm in the rms statistic itself. The first mirror tested was a concave spherical silicon foam-core mirror, with a clear aperture of 120 mm. The optic surface was measured at room temperature using standard absolute techniques; and then the change in surface figure error from room temperature to 80 K was measured. The mirror was cooled within a cryostat. and its surface figure error measured through a fused-silica window. The facility and techniques will be used to measure the surface figure error at 20K of prototype lightweight silicon carbide and Cesic mirrors developed by Galileo Avionica (Italy) for the European Space Agency (ESA).