Engineering topics
Boehlert, Carl J.
Publications and source records attributed to Boehlert, Carl J..
Strengthening mechanisms for microstructures containing unimodal and bimodal γ' precipitates in ATI 718Plus
Here, the influence of γ' precipitate size distribution on the deformation mechanisms under tensile loading in ATI 718Plus was studied. A set of aging treatments within the temperature range of 720 °C–900 °C was performed on solution-treated samples to obtain various γ' precipitate size distributions. Unimodal and bimodal γ' precipitate size distributions were achieved through single-step and two-step aging sequences, respectively, and such microstructures were tensile tested to failure to assess their yield strength, ultimate tensile strength, and elongation-to-failure. Some of the tensile samples were interrupted after achieving 3–4 % plastic strain, and the deformed microstructures were examined using transmission electron microscopy to investigate the γ' precipitate-dislocation interactions. For the unimodal γ' precipitate size distribution samples with the smaller γ' precipitates (radius ~ 7 nm), dislocations sheared through the precipitates. Both dislocation loops and paired dislocations were observed for the microstructures containing larger γ' precipitates (radius ~ 24 nm). The microstructure containing a bimodal γ' precipitate size distribution, which included average γ' precipitate radii of ~6 nm and ~28 nm, exhibited shearing as the dominant deformation mechanism, and this microstructure exhibited the highest strength values. The experimental observations were rationalized based on the theoretically-calculated critical resolved shear stress values for shearing and looping and a modified model for predicting the yield strength for bimodal microstructures was introduced.
Lattice Parameter Evolution during the β-to-α and β-to-ω Transformations of Iron- and Aluminum-Modified Ti-11Cr(at.%)
β-titanium (β-Ti) alloys are useful in diverse industries because their mechanical properties can be tuned by transforming the metastable β phase into other metastable and stable phases. Relationships between lattice parameter and β-Ti alloy concentrations have been explored, but the lattice parameter evolution during β-phase transformations is not well understood. In this work, the β-Ti alloys, Ti-11Cr, Ti-11Cr-0.85Fe, Ti-11Cr-5.3Al, and Ti-11Cr-0.85Fe-5.3Al (all in at.%), underwent a 400 °C aging treatment for up to 12 h to induce the β-to-ω and β-to-α phase transformations. Phase identification and lattice parameters were measured in situ using high-temperature X-ray diffraction. Phase compositions were measured ex situ using atom probe tomography. During the phase transformations, Cr and Fe diffused from the ω and α phases into the β matrix, and the β-phase lattice parameter exhibited a corresponding decrease. The decrease in β-phase lattice parameter affected the α- and ω-phase lattice parameters. The α phase in the Fe-free alloys exhibited α-phase c/a ratios close to those of pure Ti. A larger β-phase composition change in Ti-11Cr resulted in larger ω-phase lattice parameter changes than that for Ti-11Cr-0.85Fe. This work illuminates the complex relationship between diffusion, composition, and structure for these diffusive/displacive transformations.
Influence of interrupted cooling on the development of bimodal γ' precipitate distributions in ATI 718Plus
The influence of aging treatments on the evolution of the γ' precipitates in ATI 718Plus was studied using scanning electron microscopy, energy dispersive spectroscopy, transmission electron microscopy, and atomic probe tomography. A set of aging treatments was performed on solution-treated samples to obtain various γ' size distributions. The aging temperatures ranged from 720 to 900°C with holding times of either two hours (for the 900°C aging temperature) or 10 h (for the 720°C and 750°C aging temperatures) followed by either air cooling, furnace cooling, or water quenching. The cooling method and aging temperature influenced the distribution of the solute elements. This work discussed the evolution of the γ' precipitation during single-step aging and two-step aging involving continuous cooling or interrupted cooling. Finally, a bimodal size distribution of the γ' precipitates was obtained through interrupted cooling two-step aging treatments, while single-step aging resulted in unimodal γ' precipitate distributions.
Microstructural evolution and intermetallic formation in Zn-3Mg (wt%) powder mixture processed by high-pressure torsion
Severe plastic deformation (SPD) techniques have been used extensively over the past 40 years for producing strong metals and alloys. High-pressure torsion (HPT) is one of the most promising SPD techniques for achieving high strength through nanoscale grain refinement and phase transformation. In this research, a mixture of pure zinc (Zn) and magnesium (Mg) powders, Zn-3Mg (wt%), was HPT-processed under a pressure of 6 GPa for 1, 5, 10, 20, and 30 turns at room temperature to achieve a high strength biodegradable material. In order to understand the effects of pre-consolidation on the resulting microstructure and hardness, HPT processing was performed on loose powders placed in the die and also on a pre-compacted powder mixture and the resulting HPT disks were characterized by X-ray diffraction, scanning electron microscopy, atom probe tomography, and Vickers microhardness. In both cases, the HPT disk microstructures contained nanoscale grains, and stable and metastable strain-induced intermetallics, but an unusual softening appeared at large shear strains. Grain size, grain morphology, and the formation of different intermetallics were analyzed to explain the unusual hardness distribution, and it was found that an inverse Hall-Petch relationship between hardness and grain size exists. It is suggested that thermally-activated phenomena such as grain boundary sliding contributed to the strain-induced softening of this nano-structured biomaterial due to its low melting point. Finally, the current results are compared with those for HPT-processed cast alloys and hybrids of the same composition.