Boitnott, R. L.

Publications and source records attributed to Boitnott, R. L..

5 records

NASA NTRS1991

An experimental and analytical investigation on the response of GR/EP composite I-frames

Six-foot diameter, semicircular graphite/epoxy specimens representative of generic aircraft frames were loaded quasi-statically to determine their load response and failure mechanisms for large deflections that occur in an airplane crash. These frame-skin specimens consisted of a cylindrical skin section cocured with a semicircular I-frame. Various frame laminate stacking sequences and geometries were evaluated by statically loading the specimen until multiple failures occurred. Two analytical methods were compared for modeling the frame-skin specimens: a two-dimensional branched-shell finite element analysis and a one-dimensional, closed-form, curved beam solution derived using an energy method. Excellent correlation was obtained between experimental results and the finite element predictions of the linear response of the frames prior to the initial failure. The beam solution was used for rapid parameter and design studies, and was found to be stiff in comparison with the finite element analysis. The specimens were found to be useful for evaluating composite frame designs.

Moas, E., Jr.↗

NASA NTRS1986

Drop testing and analysis of six-foot diameter graphite-epoxy frames

Graphite-epoxy frames were drop tested onto a concrete floor to simulate crash loadings. The frames have Z-shaped cross-sections typical of designs often proposed for fuselage structure of advanced composite transports. The 6-foot diameter of the frames was chosen to reduce specimen fabrication costs and to facilitate testing. Response of the frames from accelerometer, strain gage, and photographic measurements are presented which characterize the behavior under 25-30 fps vertical impact velocity onto concrete. Failure of the graphite-epoxy frames involved a complete separation through the cross section near the impact point. All damage to the composite frame was confined to an area close to the impact point. Failure of aluminum frames tested for comparison were different from the composite specimens. The aluminum frames yielded (plastic hinges formed) at several locations around the lower portion of the frame without failing completely across the section.

Boitnott, R. L.↗

NASA NTRS1985

Nonlinear response and failure characteristics of internally pressurized composite cylindrical panels

Results of an experimental and analytical study of the nonlinear response and failure characteristics of internally pressurized 4- to 16-ply-thick graphite-epoxy cylindrical panels are presented. Specimens with clamped boundaries simulating the skin between two frames and two stringers of a typical transport fuselage were tested to failure. Failure results of aluminum specimens are compared with the graphite-epoxy test results. The specimens failed at their edges where the local bending gradients and interlaminar stresses are maximum. STAGS nonlinear two-dimensional shell analysis computer code results are used to identify regions of the panels where the response is independent of the axial coordinate. A geometrically nonlinear one-dimensional cylindrical panel analysis was derived and used to determine panel response and interlaminar stresses. Inclusion of the geometric nonlinearity was essential for accurate prediction of panel response. The maximum stress failure criterion applied to the predicted tensile stress in the fiber direction agreed best with the experimentally determined first damage pressures.

Boitnott, R. L.↗

NASA NTRS1985

A nonlinear analysis of infinitely long graphite-epoxy cylindrical panels loaded with internal pressure

The structural response of internally pressurized composite cylindrical panels, representative of a transport aircraft's fuselage skins, is predicted by means of a one-dimensional, geometrically nonlinear analysis. An analytical study is conducted for the response of 4-, 8-, and 16-ply graphite/epoxy skins. The results obtained indicate that the response is geometrically nonlinear, and that a boundary layer with a severe bending gradient exists at the panel edges. The importance of through-the-thickness shearing deformations in the bending boundary layer is illustrated through comparison of analyses based on Kirchhoff-Love and shear deformation theories. Numerical results for the bending boundary layer lengths of the different panels are presented, and two bending boundary layers are predicted with the shear deformation theory.

Boitnott, R. L.↗

NASA NTRS1984

Nonlinear response and failure characteristics of clamped internally pressurized graphite-epoxy cylindrical panels

The nonlinear response and failure characteristics of internally pressurized 4- to 16-ply cylindrical panels of graphite/epoxy are experimentally and analytically studied. Tests simulated the skin of a typical transport aircraft fuselage under loading to eventual failure. Aluminum test specimens were similarly tested and compared. All graphite/epoxy panels are found to withstand the internal pressures applied, which are well above the proof pressure loading expected for transport fuselage structures.

Boitnott, R. L.↗