DOE OSTI2022

Dynamic substrate reactions during room temperature heavy ion irradiation of CoCrCuFeNi high entropy alloy thin films

Abstract High entropy alloys (HEAs) are promising materials for various applications including nuclear reactor environments. Thus, understanding their behavior under irradiation and exposure to different environments is important. Here, two sets of near-equiatomic CoCrCuFeNi thin films grown on either SiO 2 /Si or Si substrates were irradiated at room temperature with 11.5 MeV Au ions, providing similar behavior to exposure to inert versus corrosion environments. The film grown on SiO 2 had relatively minimal change up to peak damage levels above 500 dpa, while the film grown on Si began intermixing at the substrate–film interface at peak doses of 0.1 dpa before transforming into a multi-silicide film at higher doses, all at room temperature with minimal thermal diffusion. The primary mechanism is radiation-enhanced diffusion via the inverse Kirkendall and solute drag effects. The results highlight how composition and environmental exposure affect the stability of HEAs under radiation and give insights into controlling these behaviors.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Role of electronic energy loss on defect production and interface stability: Comparison between ceramic materials and high-entropy alloys

High-entropy alloys (HEAs) and some complex alloys exhibit desirable properties and significant structural stability in harsh environments, including possible applications in advanced reactors. Energetic ion irradiation is often used as a surrogate for neutron irradiation; however, the impact of ion electronic energy deposition and dissipation is often neglected. Moreover, differences in recoil energy spectrum and density of cascade events on damage evolution must also be considered. In many chemically complex alloys, the mean free path of electrons is reduced significantly, thus their decreased thermal conductivity and slow dissipation of localized radiation energy can have noticeable effects on displacement cascade evolution that is greatly different from metals with high thermal conductivity. In this work, nanocrystalline HEAs of Ni 20 Fe 20 Co 20 Cr 20 Cu 20 and nonequiatomic (NiFeCoCr) 97 Cu 3 , both having much lower room-temperature thermal conductivity than pure Ni or Fe, are chosen as model HEAs to reveal the role that electronic energy loss during ion irradiation has in complex alloys. The response of nanocrystalline HEAs is investigated under irradiation at room temperature using MeV Ni and Au ions that have different ratios of electronic energy to damage energy, which is the energy dissipated in displacing atoms. Different from previously reported amorphization of nanocrystalline SiC, experimental results on these HEAs show that, similar to the process in nanocrystalline oxide materials, both inelastic thermal spikes via electron–phonon coupling and elastic thermal spikes via collisions among atomic nuclei contribute to the overall grain growth. The growth follows a power law dependence with the total deposited ion energy, and the derived value of the power-exponent suggests that the irradiation-induced instability at and near grain boundaries leads to local rapid atomic rearrangements and consequently grain growth. The high power-exponent value can be attributed to the sluggish diffusion and delayed defect evolution arising from the chemical complexity intrinsic to HEAs. Here, this work calls attention to quantified fundamental understanding of radiation damage processes beyond that of simplified displacement events, especially in simulating neutron environments.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Magnetism in metastable and annealed compositionally complex alloys

Compositionally complex materials (CCMs) present a potential paradigm shift in the design of magnetic materials. These alloys exhibit long-range structural order coupled with limited or no chemical order. As a result, extreme local environments exist with a large variations in the magnetic energy terms, which can manifest large changes in the magnetic behavior. In the current work, the magnetic properties of (Cr, Mn, Fe, Ni) alloys are presented. These materials were prepared by room-temperature combinatorial sputtering, resulting in a range of compositions with a single bcc structural phase and no chemical ordering. The combinatorial growth technique allows CCMs to be prepared outside of their thermodynamically stable phase, enabling the exploration of otherwise inaccessible order. The mixed ferromagnetic and antiferromagnetic interactions in these alloys causes frustrated magnetic behavior, which results in an extremely low coercivity (<1mT), which increases rapidly at 50 K. At low temperatures, the coercivity achieves values of nearly 500 mT, which is comparable to some high-anisotropy magnetic materials. Further, commensurate with the divergent coercivity is an atypical drop in the temperature dependent magnetization. These effects are explained by a mixed magnetic phase model, consisting of ferro-, antiferro-, and frustrated magnetic regions, and are rationalized by simulations. A machine-learning algorithm is employed to visualize the parameter space and inform the development of subsequent compositions. Annealing the samples at 600 °C orders the sample, more-than doubling the Curie temperature and increasing the saturation magnetization by as much as 5×. Simultaneously, the large coercivities are suppressed, resulting in magnetic behavior that is largely temperature independent over a range of 350 K. The ability to transform from a hard magnet to a soft magnet over a narrow temperature range makes these materials promising for heat-assisted recording technologies.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Exploring the composition, phase separation and structure of AgFe alloys for magneto-optical applications

Bimetallic alloys with large discrepancies in atomic radii and crystal structure typically yield systems that are highly immiscible, even at high temperatures. The Ag x Fe 1−x binary system has limited solid and liquid solubility and thus phase separated Ag + Fe alloys should result. Furthermore, Ag has interesting plasmonic properties and Fe is a strong ferromagnet, thus magneto-plasmonic nanoparticles/films should result due to their phase separation. We have leveraged a combinatorial sputter deposition to synthesize thin films with a large Ag x Fe 1−x (0.19 < x < 0.84) phase space to correlate the composition and structure to the optical and magnetic properties for both as-deposited and annealed compositions.

Bimetallic alloys↗
DOE OSTI2019

Programmable Electrofluidics for Ionic Liquid Based Neuromorphic Platform

Due to the limit in computing power arising from the Von Neumann bottleneck, computational devices are being developed that mimic neuro-biological processing in the brain by correlating the device characteristics with the synaptic weight of neurons. This platform combines ionic liquid gating and electrowetting for programmable placement/connectivity of the ionic liquid. In this platform, both short-term potentiation (STP) and long-term potentiation (LTP) are realized via electrostatic and electrochemical doping of the amorphous indium gallium zinc oxide (aIGZO), respectively, and pulsed bias measurements are demonstrated for lower power considerations. While compatible with resistive elements, we demonstrate a platform based on transitive amorphous indium gallium zinc oxide (aIGZO) pixel elements. Using a lithium based ionic liquid, we demonstrate both potentiation (decrease in device resistance) and depression (increase in device resistance), and propose a 2D platform array that would enable a much higher pixel count via Active Matrix electrowetting.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Thermal stability and irradiation response of nanocrystalline CoCrCuFeNi high-entropy alloy

Grain growth and phase stability of a nanocrystalline face-centered cubic (fcc) Ni 0.2 Fe 0.2 Co 0.2 Cr 0.2 Cu 0.2 high-entropy alloy (HEA), either thermally- or irradiation-induced, are investigated through in situ and post-irradiation transmission electron microscopy (TEM) characterization. Synchrotron and lab x-ray diffraction measurements are carried out to determine the microstructural evolution and phase stability with improved statistics. Under in situ TEM observation, the fcc structure is stable at 300 °C with a small amount of grain growth from 15.8 to ~20 nm being observed after 1800 s. At 500 °C, however, some abnormal growth activities are observed after 1400 s, and secondary phases are formed. Under 3 MeV Ni room temperature ion irradiation up to an extreme dose of nearly 600 displacements per atom, the fcc phase is stable and the average grain size increases from 15.6 to 25.2 nm. Lastly, grain growth mechanisms driven by grain rotation, grain boundary curvature, and disorder are discussed.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Low-Temperature Charging Dynamics of the Ionic Liquid and Its Gating Effect on FeSe 0.5 Te 0.5 Superconducting Films

Ionic liquids (ILs) have been investigated extensively because of their unique ability to form the electric double layer (EDL), which induces high electrical field. For certain materials, low-temperature IL charging is needed to limit the electrochemical etching. Here, we report our investigation of the low-temperature charging dynamics in two widely used ILs—DEME-TF 2 N and C4mim-TF 2 N. Results show that the formation of the EDL at ~220 K requires several hours relative to milliseconds at room temperature, and an equivalent voltage V e is introduced as a measure of the EDL formation during the biasing process. Here, the experimental observation is supported by molecular dynamics simulation, which shows that the dynamics are logically a function of gate voltage, time, and temperature. To demonstrate the importance of understanding the charging dynamics, a 140 nm thick FeSe 0.5 Te 0.5 film was biased using the DEME IL, showing a tunable T c between 18 and 35 K. Notably, this is the first observation of the tunability of the T c in thick film FeSe 0.5 Te 0.5 superconductors.

2D materials↗