DOE OSTI2023

Core-Level Spectroscopy with Hard and Soft X-rays on Phosphorus-Containing Compounds for Energy Conversion and Storage

The electronic properties of nine solid phosphorus (P)-containing compounds with varying oxidation states and chemical environments, including GaP (–III) , InP (–III) , red-P (0) , H 3 P (III) O 3 , Na 2 H 2 P 2 (IV) O 6 , H 3 P (V) O 4 , KH 2 P (V) O 4 , Na 2 HP (V) O 4 , and InP (V) O 4 , are investigated using X-ray absorption near-edge structure (XANES) spectroscopy in the hard (P K-edge) and soft X-ray regime (P L 2,3 - edge). We find shifts in the absorption-edge positions and correlate them with the ligands surrounding the P atom, likely causing a different core–hole interaction screening for different compounds. Complementing the experimental analysis, ab initio many-body calculations of XANES spectra provide insights into the excitonic nature of the observed spectral features and their impact on the electronic structure of the materials. Furthermore, we report on P K-edge XANES measurements on aqueous phosphorus-containing acids, including H 3 PO 3 , H 3 PO 4 , and their mixtures. At first sight, the spectra of the aqueous acids are similar to those of their solid counterparts. However, close inspection reveals a slight red shift of the absorption edge and the presence of fewer spectral features compared with spectra of the respective solids. Mixtures of aqueous acids display spectral features corresponding to the individual components, indicating the potential for speciation and quantification through fingerprinting.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2021

PBI nanofiber mat-reinforced anion exchange membranes with covalently linked interfaces for use in water electrolysers

Anion exchange membranes (AEM) are key components in anion exchange membrane water electrolysers. Recently developed materials are less susceptible to the alkaline degradation of the polymer backbone and quaternary ammonium groups. A remaining challenge is the mechanical stability in contact with hot water and dimensional stability when the temperature of the feed solution changes. One solution is to reinforce membranes with a porous support. Since support materials like PEEK or PTFE have a different swelling behavior than the matrix and no strong interactions with the matrix, voids can form, and gas crossover increases. In this work, we approach this issue by pore filling polybenzimidazole nanofiber mats with the bromomethylated precursor of mTPN, an ultra-stable AEM material. During drying, a covalent interaction between support (PBI amine groups) and matrix (-CH 2 Br) is established. After quaternization, the optimized PBI/mTPN-50.120 composite membrane still shows a high conductivity of 62 mS cm –1 , but 37% reduced length swelling in comparison to the non-reinforced membrane. Tensile strength and Young's modulus increase 17% and 56% to 49 MPa and 680 MPa, respectively. In an electrolyser, a stable voltage of 1.98V at 0.25 A cm –2 was achieved, and no change in membrane resistance was observed over the test time of 200 h (50°C, 1 M KOH, catalysts based on Ni/Fe and Mo).

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗