DOE OSTI2024

Characterization of Precipitation-Strengthening Heat-Resistant Austenitic Stainless Steels for Life-Prediction Modeling

In this study, the role of minor alloying additions in 347H stainless steels (UNS34709, ASTM A240/240M) on creep-rupture properties at 650-750°C and microstructure evolution during isothermal exposure at 750°C has been investigated, aiming to provide the experimental dataset as boundary conditions of physics-based modeling for material/component life prediction. Four different 347H heats containing various amounts of boron and nitrogen additions were prepared and evaluated. The combined additions of B and N are found to stabilize the strengthening secondary M23C6 carbides and retarding the transition from M23C6 to sigma phase precipitates during thermal exposure. The observed kinetics of microstructure evolution reasonably explains the improvement of creep-rupture properties of 347H stainless steels with the B and N additions.

Yamamoto, Yukinori↗

DOE OSTI2022

Electrochemical Corrosion Analysis of Stainless Steels in LALM Pyrolysis Bio-Oil with Organic Corrodents

Pyrolysis bio-oils are corrosive to low alloy steels, e.g., 2.25Cr-1Mo, 5Cr-1Mo, and 9Cr-1Mo grades. To identify the alloys with sufficient bio-oil compatibility, several commercial stainless steels were examined in bio-oil using electrochemical impedance spectroscopy to semi quantitatively assess their corrosion resistance. Low-Ash Low-Moisture (LALM) bio-oil, produced from a forest residue feedstock by the National Renewable Energy Laboratory in Golden, CO, was used as a test liquid for electrochemical impedance spectroscopy measurements. Three organic corrodents, formic acid, catechol, and lactobionic acid, were added into LALM bio-oil to produce test liquids with intentionally increased corrosivity. Corrosion reaction resistance, determined from the impedance data, was used to evaluate the corrosion compatibility of each stainless steel in LALM bio-oil and LALM bio-oil + organic corrodent(s). The results from corrosion reaction resistance indicated that the critical Cr content of stainless steels for corrosion resistance would be greater than 14 wt % if Ni and Mo contents are low but can be as low as 12–13 wt % with appreciable amounts of Ni and Mo.

Jun, Jiheon↗

DOE OSTI2021

Compatibility of Alumina-Forming Austenitic Steels in Static and Flowing Pb

Alumina-forming austenitic (AFA) steels were evaluated for the lead fast reactor application in static and flowing high-purity Pb. Two AFA composition ranges with different Ni, Mn, Al, Cr and Nb contents were targeted, and Zr foil was used in an attempt to getter O in some capsules. Based on two rounds of capsule testing at 500–800°C, two AFA compositions were selected for evaluation in flowing Pb with a peak temperature of 650°C in a thermal convection loop made of pre-oxidized FeCrAlMo tubing. After exposure for 1000 h, the mass losses for both AFA alloys were generally low, suggesting good compatibility under these conditions without preoxidation.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Minimizing Cr-Evaporation from Balance of Plant Components by Utilizing Cost-Effective Alumina-Forming Austenitic Steels

A solid oxide fuel cell (SOFC) is a clean and efficient energy conversion device. The development of intermediate-temperature SOFCs has made it preferable to use metallic interconnects (MICs) to greatly reduce the cost and significantly increase the efficiency compared to ceramic interconnect materials. However, gaseous chromium species will evaporate from the chromium-containing layer formed on the surface of commonly used MICs and balance of plant (BoP) components. Volatile chromium species have been shown to form solid deposits which poison the cathodes of SOFCs, causing drastic cell performance degradation and thereby limiting commercialization. In order to alleviate the Cr poisoning and achieve long-term high performance of SOFC stacks, various Al2O3-forming austenitic (AFA) stainless steels applied at different temperatures are evaluated in this project. Based on our Phase I results (500 h operation), it is shown that on the AFAs, an alumina-based protective layer forms under high temperature that is invulnerable to water vapor effects and suppresses the diffusion of chromium and manganese which can prevent the generation of spinels on the alloy surface. Therefore, 310S, OC4 and OC5 at 800 °C and 625, OC11 and OC11LZ at 900 °C are selected to be tested in the Phase II long-term operation. From the results, we find that besides the lower Cr evaporation rates and better oxidation resistance of AFAs than benchmark alloys after short-term (500 h) operation, AFAs also possess the sturdy and compact alumina layer after a long-term operation (5000 h). A protective oxide layer is of great importance for the long-term high-temperature operation of structural materials. The high-temperature oxidation behavior of AFAs and commercial 310S and 625 alloys in Air + 10% H 2 O at 800 °C and 900 °C is systematically investigated. Severe breakaway oxidation and minor spallation are observed for the 310S and 625 after the long-term operation, while the AFAs show high oxidation resistance. It is found that the formation of a continuous alumina layer could greatly prevent the volatilization of chromium vapors. In addition, the corresponding evolving models are discussed. Chromium evaporation from BoP components in high-temperature environment could severely deteriorate the electrochemical performance of SOFC. Several methods were applied to evaluate the Cr evaporation rates of BoP after 500 h exposure at 800 °C to 900 °C in air with 10% H 2 O. An optimal method was designed to exclude the effect of silicon (Si) deposits from quartz tube and sodium (Na) deposits from the sodium carbonate on the oxidation process and the chemical interaction between Cr gaseous species and alumina tube which could provide further quantitative correlation of the evaporated Cr species quantities and degradation rates of SOFC. Based on the great performance of AFAs after long-term operation, AFAs are assembled with Anode-supported cells (ASC) to investigate the the Cr deposition of anode-supported cell under a constant current density of 0.5 A cm -2 at 800 °C with AFA alloys compared with commercial alloys. In addition, the anodic and cathodic processes are deconvoluted by distribution of relaxation times (DRT) method which are comprehensively discussed. It is found out that the voltage exhibited a slight decrease of 5.09 % and 1.54 % in the presence of OC11 and OC11LZA alloy, respectively. However, a considerable decrease of 22.14 % and 12.06 % was determined in the presence of 310S and 625 alloy, respectively. AFAs possessing the low-cost, low Cr evaporation rates and the high oxidation resistance will make it of great potential to replace the existing BoP components.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Corrosion Behavior of Alloy Structural Steels in Catechol and Biomass-Derived Pyrolysis Oils

Electrochemical impedance spectroscopy (EIS) was used to assess the corrosion behavior of three steels, 2.25Cr-1Mo, 5Cr-1Mo and 9Cr-1Mo (UNS K21590, S50200 and K90941) in bio-oils and catechol, an organic constituent commonly found in bio-oils. Two types of biomass pyrolysis oils produced from selected forest residue feedstocks, classified as high-ash and high-moisture (HAHM) and low-ash and low-moisture (LALM) types and 10 wt.% catechol, were used to test the alloys. According to previous results, 10 wt.% catechol in a water and methanol mixture was corrosive to 2.25Cr-1Mo but not to 9Cr-1Mo, highlighting that increasing Cr content in the steels resulted in improved corrosion resistance. 5Cr-1Mo, a steel with an intermediate Cr content, was tested in catechol solutions to better estimate the critical value of Cr for corrosion resistance under these conditions. Also, the three alloys were tested in both HAHM and LALM bio-oils to assess corrosion susceptibility. For EIS measurements, a customized electrochemical setup was employed to minimize the ohmic path through the bio-oils. The corrosion susceptibility was evaluated by determining the resistance at the alloy-corrosive medium interface.

Jun, Jiheon↗

DOE OSTI2021

Evaluation of Corrosion Susceptibility of Structural Steels in Biomass Derived Pyrolysis Oil

Biomass derived pyrolysis oil is a promising renewable energy source. Due to the variety of biomass feedstocks, the bio-oils could contain a wide range of organic constituents which would provide unique corrosive environments for structural materials. A preliminary work exposed different classes of steels and stainless steels to selected organic constituents of biomass pyrolysis oils and found that corrosion susceptibility, assessed using electrochemical impedance spectroscopy (EIS), was prominent in the steels with Cr lower than 11 wt.%. Although this result suggests stainless steels will resist corrosion by certain organic constituents, it may not be sufficient to predict the corrosion performance in real bio-oils. Therefore, this study attempted electrochemical measurements on Cr-alloyed steels and stainless steels directly exposed to a biomass derived pyrolysis oil. To overcome the low conductivity of bio-oils, a customized Luggin capillary was designed to minimize the ohmic path in bio-oils. The results of this work will be reported.

Jun, Jiheon↗

DOE OSTI2021

Corrosion and Chemical Characterization of Bio-Oils from Biomass with Varying Ash and Moisture Contents

As part of the Feedstock Conversion Interface Consortium four samples of pine chips (all combinations of low and high moisture and ash content) were collected and processed for fast pyrolysis. The prepared biomass samples were liquefied at the National Renewable Energy Laboratory (NREL) using the fast pyrolysis process. Following some characterization of the bio-oils at NREL, the bio-oils were shipped to Oak Ridge National Laboratory (ORNL) for corrosion testing and further characterization.The content and composition of ash in each bio-oil was determined. Corrosion testing consisted of exposing selected metallic and elastomer samples for 1000 hr at 50°C and for longer times at room temperature as well as electrochemical impedance spectroscopy measurements to assess relative corrosivity of the bio-oils. Chemical characterization was conducted to identify the corrosive component of the bio-oils as well as to define the chemical differences among the oils. It was hypothesized that there could be a catalytic effect from the higher ash content in two of the biomass sources. Results of these characterization and corrosion studies will be reported.

Keiser, Jim↗

DOE OSTI2020

Uncertainty Quantification of Machine Learning Predicted Creep Property of Alumina-Forming Austenitic Alloys

The development of machine learning (ML) approaches in materials science offers the opportunity to exploit existing engineering and developmental alloy datasets, such as Oak Ridge National Laboratory (ORNL)’s consistently measured creep-rupture dataset for alumina-forming austenitic (AFA) alloys, to accelerate their further development. As a first step toward achieving ML insights for improved alloy design, the potential sources of uncertainty and their impacts on ML output are examined. It is observed that the selection of algorithms and features as well as data sampling significantly affects the performance of ML models, either positively or negatively. Further, the performance of various ML models in predicting the creep properties of AFA alloys is compared, with further evaluation by assessment of a small set of new developmental AFA alloys that were not part of the training dataset. The present study demonstrates that uncertainty quantification (UQ) is essential in materials science for evaluating the performance of ML algorithms with specifically selected feature sets and obtaining a comprehensive understanding of their limitations and the resultant capability of effective prediction in complex materials systems.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Long-Term Corrosion Studies of Pine Derived Bio-Oil and Blends with Heavy Fuel Oil

Biomass derived liquid fuels offer a means to reduce greenhouse gas emissions compared to those produced by combustion of petroleum derived liquid fuels. However, the corrosivity of bio-oils toward the less expensive structural materials creates a material selection problem for designers of storage tanks and combustion systems. Samples of candidate structural materials are being exposed for thousands of hours in multiple fast pyrolysis bio-oils and conditions to evaluate the corrosion resistance of these materials. One method to mitigate the corrosivity of bio-oils and speed their adoption, while also decreasing the pollution issues associated with low quality petroleum derived fuels, is to utilize blends of bio-oil and heavy fuel oil in engines currently solely burning a petroleum-based fuel. In addition to the corrosion studies conducted in 100% bio-oil, studies were also conducted with blends of the fast pyrolysis bio-oil produced from pine tree components with a heavy fuel oil that is used in ocean-going ships. This bio-oil had a very high carboxylic acid content which made it very corrosive to carbon and 2¼ Cr-1 Mo steel and even 409 stainless steel. The heavy fuel oil was not corrosive to carbon steel, but its sulfur content makes it a significant pollution producer and particularly undesirable for use near coastlines. Corrosion tests were conducted with the individual components and with various blends of the two liquid fuels. Studies showed a significantly lower corrosivity of the blends than would be projected assuming linear mixing behavior. Adoption of such blends holds the potential to reduce production of sulfur-containing exhaust gases as well as carbon dioxide from non-renewable fuels.

29 ENERGY PLANNING, POLICY, AND ECONOMY↗

DOE OSTI2020

Long-Term Corrosion Studies Of Pine Derived Bio-Oil And Blends With Heavy Fuel Oil

Keiser, Jim↗

DOE OSTI2020

MECHANICAL AND CORROSION ASSESSMENT OF FRICTION SELF-PIERCING RIVET JOINT OF CARBON FIBER-REINFORCED POLYMER AND MAGNESIUM ALLOY AZ31B

In the present work, thermoset carbon fiber–reinforced polymer (CFRP) was spot joined to magnesium alloy AZ31B by a friction self-piercing riveting (F-SPR) process. Lap shear tensile and cross-tension testing were used to evaluate the mechanical joint performance. An average lap shear tensile load of 5.18 kN was achieved, while an average of 2.81 kN was found from cross-tension testing. All F-SPR samples showed pull-out of AZ31B after mechanical testing, indicating good mechanical interlocking between the steel rivet and AZ31B. Corrosion potential was measured for each material to establish the galvanic corrosion characteristics. As expected, AZ31B was found to be the most active, while thermoset CFRP was the most noble. The steel rivet fell between the AZ31B (active) and the thermoset CFRP (noble). Salt fog corrosion testing (ASTM B-117) was performed to evaluate the corrosion performance of the uncoated F-SPR joint. With up to 200 h of exposure, the post-corroded F-SPR joint integrity retained 81.2% of the pre-exposure F-SPR joint strength with AZ31B pull-out failure mode. From cross-sectional analysis of the F-SPR joint, extensive corrosion of AZ31B was observed at the joint and other exposure areas. However, steel rivet was not significantly corroded potentially due to sacrificial anode effect by which AZ31B corroded first in the galvanic couple.

Lim, Yong Chae↗

DOE OSTI2020

Dual Phase Soft Magnetic Laminates for Low-cost, Non/Reduced-Rare-Earth Containing Electrical Machines

To accelerate the mass market adoption of electric drive vehicles, the key technology barriers in electric motors are (1) magnet cost and rare-earth element price volatility; (2) non-rare-earth electric motor performance; and (3) materials property optimization. The goal of this project was to address these barriers by advancing a unique and innovative dual phase soft magnetic material technology and demonstrating the material in a 30-kW synchronous reluctance motor without using any permanent magnet for electric vehicles. Dual phase magnetic materials offer the electric motor designer the ability to locally control the magnetic saturation level in a motor laminate, while at the same time enhancing the mechanical strength of the laminate material, resulting in an enhancement in motor performance and efficiency. Scalable dual phase soft magnetic laminates manufacturing technologies were developed in collaboration with multiple US manufacturers. 1000 lbs of alloy sheet with a thickness of 0.25mm and width of 280 mm was manufactured within the specifications. Batch sizes of up to 240 laminates per run were produced from the alloy sheet. Two prototype motors with dual phase soft magnetic laminates were designed, built, and tested. The major goal of building the subscale prototype as a pathway to develop scalable manufacturing technologies for the dual phase soft magnetic laminates was met. The additional goal of building and testing the subscale prototype in order to validate the calculated performance with the tested motor performance was also met. For the full-scale 30kW continuous power synchronous reluctance motor prototype, the tested performance met the targets in terms of continuous power at the operating speeds up to 8000 rpm. Post-test studies were conducted and the root causes for the discrepancy between the predicted and tested peak power, continuous power at high speed range, and efficiency were identified. Further modeling study showed that the dual phase rotor machine has a 27% higher torque to active weight ratio than an equivalent performance silicon steel rotor machine. Application space and multiple discussions with traction motor and electric vehicle manufacturers for commercialization of the dual phase soft magnetic material technology were identified and conducted. An initial cost model was established based on the developed manufacturing technologies with the US manufacturers. Future paths for further cost reduction were identified, including increasing the market volume by broadening the applications of the dual phase soft magnetic laminate technology for electric machines in other energy sections such as oil & gas, heating, ventilation, and air conditioning (HVAC), and power generation.

33 ADVANCED PROPULSION SYSTEMS↗

NASA NTRS1987

Expert systems relations in space applications

The problem of expert systems relations as they pertain to space applications is discussed. First, these systems are categorized and the relationships between them are analyzed. Then, the expert systems cooperation paradigm is proposed. This paradigm addresses various types of communication and coordination issues in an attempt to create a general model applicable in a number of situations.

Brady, Michael↗