Superconducting Nb3Ge tape conductors 5 to 10 m long were fabricated by chemical vapor deposition. Such tapes could be used in high-field magnet applications. Average tape properties set the upper performance limit of a magnet at 17 teslas (4.2 K). Highest critical-current densities obtained in thin and layered films set the upper performance limit at 20 teslas (4.2 K).
The critical temperature, upper critical field and structure of Nb3Ge materials produced by sputtering onto sapphire or by chemical vapor deposition on sapphire or Hastelloy were determined. In the case of the samples formed by deposition, several dopants, including Nb5Ge3, NbN and NbC were used. A variety of deposition temperatures were studied. Highest upper critical field values were obtained in samples deposited in the 750 to 850 C range. The degree of flux pinning exhibited a correlation with grain size. The presence of an impurity dopant had a depressant effect on the critical temperature and upper critical field.
A process of fabricating superconducting Nb3Ge tapes by chemical vapor deposition (CVD) has been developed and tapes up to 10 meters long fabricated. The typical properties achieved were: critical temperature T sub c = 20 K, upper critical field H sub c2 = 29 tesla at 4.2 K, and J sub c = 3 to 4 x 10 to the 8th power A m(-2) at 4.2 K, 18 tesla. The relative depression of T sub c and H sub c2 compared with the best thin film samples sputtered on sapphire was due to the presence of Nb5Ge3 second-phase particles used as flux pinning centers and to strains induced by thermal mixmatch with Hastelloy B tape substrates. A peculiar field dependence of flux pinning force that was observed in both CVD and sputtered Nb3Ge indicated a premature pin-breaking mechanism or a phase inhomogeneity. Directions of further optimization work were defined.