DOE OSTI2024

Ageing Studies of Mega Battery Packs for Grid Storage Applications Using Physics Based Modeling

The lower Levelized Cost of Electricity (LCOE) from wind and solar photovoltaics has enabled for greater integration of variable energy resources with energy storage tech-nologies such as larger centralized lithium-ion battery megapacks (with 1MWh total energy and 500V rating) to provide utility-scale services to grid operators. The daily cycling of standalone lithium-ion grid storage will reduce the battery cells' capacity due to several degradation mechanisms. A comprehensive physics-based Python tm framework called Liionpack was developed to estimate these megapacks' remaining life and ageing. The study includes various degradation mechanisms coupled to the electrochemical-thermal model at the pack level. The effect of the inhomogeneities from cell-to-cell thermodynamic and kinetic properties for different working conditions including temperature and charge/discharge protocols on the ageing of a megapack are presented here.

Karra, Vikrant↗

DOE OSTI2021

Prevention of lithium-ion battery thermal runaway using polymer-substrate current collectors

Isolating electronically conducting material from internal short circuits is a promising way to prevent the onset of thermal runaway within lithium-ion cells. Here, a metal-coated polymer current collector, which is designed to disconnect internal short circuits by withdrawing from the heating region, is tested in 18650 cells. In addition to having lower mass and manufacturing costs, cells with metal-coated polymer current collectors demonstrate a reduced risk of thermal runaway during nail penetration. High-speed synchrotron X-ray radiography of 18650 cells during nail-penetration testing, in tandem with pre- and post-mortem X-ray computed tomography, provides insights into the function of the current collectors. The results are compared with those of 18650 cells with standard commercial aluminum and copper current collectors. Cells with aluminum-coated polymer current collectors demonstrated 100% success in thermal runaway prevention during nail penetration, retaining a cell voltage >4.00 V, while standard cells consistently experienced thermal runaway.

25 ENERGY STORAGE↗

DOE OSTI2021

Internal insulation and corrosion control of molten chloride thermal energy storage tanks

A chloride-based molten-salt system that uses a ternary blend of MgCl 2 /KCl/NaCl is investigated to provide higher-temperature thermal energy storage capability than conventional nitrate salt-based systems. Despite their high thermal stability and operating temperature, molten chlorides present several challenges, including the design of internal liners to prevent the corrosion and thermal stress of alloy tank shells. This work discusses issues and potential solutions related to containment of molten chloride salt, specifically the optimization of the hot face refractory materials for use as internal liners. Furthermore, three down-selected refractory materials were analyzed with respect to permeation of salt through the material as well as chemical stability during high temperature operation. Through the application of X-ray imaging and electron spectroscopy techniques, highly stable secondary surface phases in equilibrium with the molten salt were identified, as well as time-dependent changes in the salt composition itself.

25 ENERGY STORAGE↗