Using Additive Manufacturing to Repair Gas Turbine Hot Section Components

Ni-based superalloys are used in the hot sections of gas turbine engines due to their excellent high temperature performance. During service the material degrades due to exposure at high temperature and mechanical loads. Hence, utility provides often inspect, service, and repair components in gas turbine engines to ensure safe operation. A major challenge, however, is that the most heat-resistant alloys are generally considered ‘non-weldable’ rendering them difficult to repair via welding operations. In these cases components are often scrapped and then replaced by parts which must be re-manufactured. This burdens utilities with additional cost and supply chain issues can result in long term outages or reduced operating limtis. In this work EPRI and ORNL investigated a proposed repair strategy for gas turbine hot section components. Hot section superalloy GTD-111 was selected as a candidate repair material system and AM material ABD-900 the repair material. Sandwich structures were fabricated via electron beam melting additive manufacturing (EBM-AM) producing tensile bars with gage sections consisting of dissimilar ABD-900 / GTD-111 / ABD-900 material. Metallography revealed that the interface exhibited no deleterious phases or processing defeats. Creep rupture experiments on heat treated material demonstrates that the emulated repair coupons exhibit creep resistance between GTD-111 and ABD-900. This study demonstrates that the proposed EBM-AM repair strategy presents a viable opportunity towards enabling AM repair of gas turbine engine components.

99 GENERAL AND MISCELLANEOUS↗
DOE OSTI2024

Using Additive Manufacturing to Repair Gas Turbine Hot Section Components

Ni-based superalloys are used in the hot sections of gas turbine engines due to their excellent high temperature performance. During service the material degrades due to exposure at high temperature and mechanical loads. Hence, utility provides often inspect, service, and repair components in gas turbine engines to ensure safe operation. A major challenge, however, is that the most heat-resistant alloys are generally considered ‘non-weldable’ rendering them difficult to repair via welding operations. In these cases components are often scrapped and then replaced by parts which must be re-manufactured. This burdens utilities with additional cost and supply chain issues can result in long term outages or reduced operating limits. In this work EPRI and ORNL investigated a proposed repair strategy for gas turbine hot section components. Hot section superalloy GTD-111 was selected as a candidate repair material system and AM material ABD-900 the repair material. Sandwich structures were fabricated via electron beam melting additive manufacturing (EBM-AM) producing tensile bars with gage sections consisting of dissimilar ABD-900 / GTD-111 / ABD-900 material. Metallography revealed that the interface exhibited no deleterious phases or processing defeats. Creep rupture experiments on heat treated material demonstrates that the emulated repair coupons exhibit creep resistance between GTD-111 and ABD-900. This study demonstrates that the proposed EBM-AM repair strategy presents a viable opportunity towards enabling AM repair of gas turbine engine components.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Assessment of a Grade 91 Steel Forging and Seamless Pipe Section After 141,000-Hours of Operation in a Superheat Outlet Header

In this work, two unique heats of 9Cr creep strength enhanced ferritic (CSEF) steels extracted from a retired superheat outlet header after 141,000 hours of service were evaluated. These two CSEF steels were a forging manufactured to SA-182 F91 (F91) reducer and a seamless pipe produced to SA-335 P91 (P91) pipe. Their creep deformation and fracture behavior were assessed using a lever arm creep frame integrated with in-situ high-temperature digital image correlation (DIC) system. Critical metallurgical and microstructure factors, including composition, service damage, grain matrix degradation, precipitates, and inclusions were quantitatively characterized to link the performance of the two service aged F91 and P91 CSEF steels. The creep test results show the F91 and P91 steels exhibit a large variation in creep strength and creep ductility. The F91 steel fractured at 572 hours while P91 steel fractured at 1,901 hours when subjected to a test condition of 650 °C and 100 MPa. The nominal creep strains at fracture were 12.5% (F91) and 14.5% (P91), respectively. The high-resolution DIC strain measurements reveal the local creep strain in F91 was about 50% while the local creep strain in P91 was >80%. The characterization results show that the F91 steel possessed pre-existing creep damage from its time in service, a higher fraction of inclusions, and a faster matrix grain coarsening rate. These features contribute to the observed reduction in performance for the F91 steel. The context for these findings, and the importance of metallurgical risk in an integrated life management approach will be emphasized.

Wang, Yiyu↗
DOE OSTI2023

Relationship between Grain Size and Sample Thickness on the Creep-Rupture Performance of Thin Metallic Sheets of INCONEL Alloy 740H

A study was conducted on INCONEL® alloy 740H® to examine the role of grain size and sheet thickness on the alloy’s creep-rupture behavior. Three different starting sheet thicknesses were utilized and multiple heat-treatment conditions anticipated for compact heat exchanger (CHX) manufacturing were applied to produce a range of grain sizes. Creep-rupture testing was conducted at 750 °C for times up to about 6000 h and the results were compared to wrought databases. The data show that both creep strength and ductility were important factors in the overall creep performance of the sheets. Reductions in performance were observed due either to accelerated creep when grain size was fine or loss of rupture ductility when grain sizes approached the sheet thickness. Some combinations of heat-treatment and thickness were able to produce typical expected wrought creep properties. Historically a ‘rule-of-thumb’ requirement for creep testing suggests 3-5 grains per sample minimum dimension to ensure homogeneous behavior. This research shows that to ensure representative wrought creep performance (i.e. no effect of sample size), the sample minimum cross-section should be 10 times the average ASTM grain size. Statistical analysis of the microstructures suggests the population of larger grains as a controlling feature in creep failure.

14 SOLAR ENERGY↗
DOE OSTI2022

Development and performance of INCONEL® alloy 740H® seam-welded piping

INCONEL® alloy 740H® is an age-hardenable nickel-based alloy approved for pressure vessels and piping within ASME Section I, VIII, and B31.1. Currently, the code applies a weld strength reduction factor (WSRF) of 0.7 to the allowable stresses for longitudinal seam welds in the time dependent creep regime. In this work, a full-scale seam weld was successfully produced using typical industrial practices. The component was solution heat-treated and aged after fabrication to improve the performance of the weldment. Tensile, bend, impact, and low-cycle fatigue tests showed the component met all the specification requirements and elevated temperature properties were within base metal expectations with failures predominately in the weld metal. Long-term creep tests, including large samples more representative of the entire weldment, were fabricated and tested to times in excess of 10,000 h at multiple temperatures. Analysis of the creep data supports a WSRF of 0.9 for the solution annealed + aged weldments in contrast to the WSRF of 0.7 currently applied to welded + aged weldments. Metallurgical analysis shows that the solution annealing causes recrystallization of the weld metal and reduces the chemical compositional and microstructural gradients in the weldments resulting in acceptable short-term performance. In long-term creep, evidence for coarsened zones in the weldments due to discontinuous coarsening reactions were identified as the mechanism leading to accelerated creep damage formation in the weld metal and sample failure.

14 SOLAR ENERGY↗
DOE OSTI2022

Improving Economics of Generation 3 CSP System Components Through Fabrication and Application of High Temperature Nickel-Based Alloys

To improve the efficiency and lower the cost of Concentrating Solar Power (CSP) plants, new Generation 3 ‘Gen 3’ CSP concepts using novel salts, solids, or gas heattransfer media envisaged to integrated with a supercritical CO 2 (sCO 2 ) power block at temperatures >715ºC are being investigated. Regardless of the specific pathway, critical components including receivers, piping, and heat-exchangers (HXs) will require the use of heat-resistant nickel-based alloys. Furthermore, the use of age-hardenable alloys, such as INCONEL® alloy 740H® (alloy 740H) may be needed to reduce capital cost. The unique challenges presented by CSP plants to material manufacture, such as small diameter thin-walled tubing in receivers, large diameter thin wall piping, and thin sheet and tubes for HXs can add to the cost to produce such alloys when compared to traditional wrought and cast processing. The goal of this project was to facilitate a reduction of plant cost by developing alternate manufacturing routes and quantifying the performance and economic benefits for alloy 740H in comparison to other candidate nickel-based alloys through fabrication trials, high-temperature mechanical property studies, and interactions with technology developers and codes and standards.

14 SOLAR ENERGY↗
DOE OSTI2022

Characterization of Long-Term Service Coal Combustion Power Plant Extreme Environment Materials

The objective of this DOE-sponsored project was to develop a comprehensive database of mechanical properties, alloy microstructures, and to a lesser extent, the oxidation/corrosion behaviors of coal-fired power plant components, such as boiler tubing, steam headers, and steam piping, which had been in service for at least 100,000 operating hours (preferably more than 200,000 operating hours) under the operating conditions of high temperatures and high mechanical stresses where creep, fatigue, steam-side oxidation, and fireside corrosion were life-limiting factors. The components included in this database consisted of ferritic steels, creep strength enhanced ferritic (CSEF) steels, and 300-series H-grade stainless steels, as well as dissimilar metal welds (DMWs) among these types of materials. As a result of extensive metallurgical characterization and mechanical testing performed in this project, a comprehensive database on mechanical properties and detailed quantitative microstructural information was successfully developed for several long-term serviced EEM components. Such a database can be used by material research communities to develop, calibrate, refine, and validate mechanical behaviors, models, and other assessment tools for accurate prediction of remaining life of major components under similar EEM operating conditions.

20 FOSSIL-FUELED POWER PLANTS↗
DOE OSTI2022

Processing, Microstructure, and Properties of AM-Alloy ABD®900-AM

In this work the processability and properties of AM alloy ABD900 processed via laser and electron beam powder bed fusion are investigated. Both AM modalities are suitable for processing and the material exhibits good high temperature creep properties. This phase I CRADA demonstrates that ABD900 is a suitable allow for potential blade repair work using powder bed fusional AM technology.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Characterization of Long-term Service Coal Combustion Power Plant Extreme Environment Materials

The technical goal of this project is to develop a comprehensive database of mechanical properties, alloy microstructures, and to a lesser extent, the oxidation/corrosion behavior of coal-fired power plant components, such as boiler tubing, steam headers and steam piping, which have been in long-term service (at least 100,000 operating hours, and preferably more than 200,000 operating hours) under the operating conditions of high temperatures and high mechanical stresses where creep, fatigue, steam-side oxidation, and fireside corrosion are life-limiting factors. The components included in the database will include the following types of high temperature alloys: creep strength enhanced ferritic (CSEF) steels, 300-series H-grade stainless steels, and dissimilar metal welds (DMWs).

Characterization↗