NASA NTRS1995

Failure Mechanisms During Isothermal Fatigue of SiC/Ti-24Al-11Nb Composites

Failure mechanisms during isothermal fatigue of unidirectional SiC/Ti-24Al-11Nb (at.%) composites have been determined by microstructural analysis of samples from tests interrupted prior to the end of life and from tests conducted to failure. Specimens from three regions of life were examined based on the maximum strain from a fatigue life diagram: Region 1 (high strain), Region 2 (mid-strain) and Region 3 (low strain). Crack lengths were also measured from interrupted samples and compared based on temperature (23-815 C), region of life and numbers of cycles. Region 1 was controlled by fiber-dominated failure. A transition zone was observed between Regions 1 and 2 due to competition between failure mechanisms. Failure in Region 2 was generally described as surface-initiated cracking with varying amounts of fiber bridging. However, the specific descriptions of crack propagation through the fibers and matrix varied with strain and temperature over this broad region. Region 3 exhibited endurance behaviour at 23 C with no cracking after lO(exp 6) cycles. However at 425 C, surface-initiated cracking was observed after 10(exp 6) cycles with fractured fibers in the crack wake. If endurance behaviour exists for conditions of isothermal fatigue in air at temperatures of greater than or equal to 425 C, it may only be found at very low strains and at greater than 10(exp 6) cycles.

Brindley, P. K.↗

NASA NTRS1992

The effect of temperature on the deformation and fracture of SiC/Ti-24Al-11Nb

The effect of temperature on the stress-strain behavior in air and the failure mechanisms of Ti-24Al-11Nb alloy and of a SiC/Ti-24Al-11Nb composite with continuous SiC fibers oriented parallel to the loading direction was investigated over temperature range 23-815 C. It was found that the tensile failure process of SiC/Ti-24Al-11Nb was controlled at all temperatures by fiber fracture. Composite failure occurred at 0.8 percent strain at all temperatures. Debond and frictional stresses at the fiber-matrix interface decreased with increased temperature.

Brindley, P. K.↗

NASA NTRS1991

Continuous fiber-reinforced titanium aluminide composites

An account is given of the fabrication techniques, microstructural characteristics, and mechanical behavior of a lightweight, high service temperature SiC-reinforced alpha-2 Ti-14Al-21Nb intermetallic-matrix composite. Fabrication techniques under investigation to improve the low-temperature ductility and environmental resistance of this material system, while reducing manufacturing costs to competitive levels, encompass powder-cloth processing, foil-fiber-foil processing, and thermal-spray processing. Attention is given to composite microstructure problems associated with fiber distribution and fiber-matrix interfaces, as well as with mismatches of thermal-expansion coefficient; major improvements are noted to be required in tensile properties, thermal cycling effects, mechanical damage, creep, and environmental effects.

Mackay, R. A.↗

NASA NTRS1991

Effect of Fiber Strength on the Room Temperature Tensile Properties of Sic/Ti-24Al-11Nb

SCA-6 SiC fibers of known strength were incorporated into SiC/Ti-24Al-11Nb (at. percent) composites and the effect of fiber strength variability on room temperature composite strength was investigated. Fiber was etched out of a composite fabricated by the powder cloth technique and the effect of the fabrication process on fiber strength was assessed. The strength of the composite was directly correlated with the strength of the as-received fiber. The strength of composite plates containing mixed fiber strengths was dominated by the lower strength fiber. Fabrication by the powder cloth technique resulted in only a slight degradation of fiber strength. The strength of the composite was found to be overestimated by the rule of mixtures strength calculation. Examination of failed tensile specimens revealed periodic fiber cracks and the failure mode was concluded to be cumulative. With the variation in fiber strength eliminated, the composite UTS was found to have a positive correlation with volume fraction of fiber.

Draper, S. L.↗

NASA NTRS1990

Reaction zone microstructure in a Ti3Al + Nb/SiC composite

A composite of Ti-25Al-13Nb (atomic percent) matrix with a continuous SiC fiber (SCS-6) reinforcement was fabricated by hot pressing powder cloths and mats of fiber. The fiber/matrix reaction zone was studied using scanning electron microscopy (SEM) and transmission electron microscopy/analytical electron microscopy (TEM/AEM) techniques. The extent of reaction was determined, phases were identified, and solute partitioning among the phases was determined. It was found that the matrix had reacted only with a portion of the carbon-rich outer layer of the SCS-6 fiber. The reaction zone contained two concentric zones which are distinguished by the presence of different carbide phases. Both zones contained a hexagonal Si-bearing phase, and one of the zones also contained some fine scattered porosity. The results are discussed with reference to available phase equilibria data.

Baumann, S. F.↗

NASA NTRS1990

Development of a new generation of high-temperature composite materials

Intermetallic matrix composites proposed to meet advanced aeropropulsion requirements are discussed. The powder metallurgy fabrication process currently being used to produce these intermetallic matrix composites will be presented, as will properties of one such composite, SiC/Ti3Al+Nb. In addition, the direction of future research will be outlined, including plans for enhanced fabrication of intermetallic composites by the arc-spray technique and fiber development by the floating-zone process.

Brindley, P. K.↗

NASA NTRS1990

High temperature fatigue behavior of a SiC/Ti-24Al-11Nb composite

A series of tension-tension strain- and load-controlled tests were conducted on unidirectional SiC/Ti-24Al-11Nb (at percent) composites at 425 and 815 C. Several regimes of damage were identified using Talrega's concept of fatigue life diagrams. Issues of test technique, test control mode, and definition of failure were also addressed.

Bartolotta, P. A.↗

NASA NTRS1990

Factors which influence tensile strength of a SiC/Ti-24Al-11Nb (at. pct) composite

Tensile and fiber pullout tests were used in conjunction with SEM to investigate structural and processing effects on SiC fiber, a neat Ti-24Al-11Nb matrix alloy, and a composite fabricated from the two. The effects of oxygen content, fiber spacing, fiber volume fraction, fiber-matrix reaction thickness, Teflon content, and matrix powder size, appear to be smaller than the effects of variability in fiber strength. Fiber spacing did not influence radial crack formation, interfacial bond shear strength, or stress-strain behavior in the composite. The temperature dependence of composite properties was investigated over the 23-815 C range.

Brindley, P. K.↗

NASA NTRS1989

Investigation of interfacial shear strength in a SiC fibre/Ti-24Al-11Nb composite by a fibre push-out technique

A fiber push-out technique applied at several sample thicknesses was used to determine both the debond shear stress and the frictional shear stress at the fiber-matrix interface at room temperautre for a unidirectional SiC fiber-reinforced T-24Al-11Nb (in at. pct) composite prepared by a powder cloth technique. The push-out technique measures the separate contributions of bond strength and friction to the mechanical shear strength at the fiber-matrix interface. It was found that the fiber-matrix bond shear strength of this material is significantly higher than the fiber-matrix frictional shear stress (119.2 and 47.8 MPa, respectively).

Eldridge, J. I.↗

NASA NTRS1988

Investigation of a SiC/Ti-24Al-11Nb composite

A summary of ongoing research on the characterization of a continuous fiber reinforced SiC/Ti-24Al-11Nb (at percent) composite is presented. The powder metallurgy fabrication technique is described as are the nondestructive evaluation results of the as-fabricated composite plates. Tensile properties of the SiC fiber, the matrix material, and the 0-deg SiC/Ti-24Al-11Nb composite (fibers oriented unidirectionally, parallel to the loading axis) from room temperature to 1100 C are presented and discussed with regard to the resultant fractography. The as-fabricated fiber-matrix interface has been examined by scanning transmission electron microscopy and the compounds present in the reaction zone have been identified. Fiber-matrix interaction and stability of the matrix near the fiber is characterized at 815, 985, and 1200 C from 1 to 500 hr. Measurements of the fiber-matrix reaction, the loss of C-rich coating from the surface of the SiC fiber, and the growth of the Beta depleted zone in the matrix adjacent to the fiber are presented. These data and the difference in coefficient of thermal expansion between the fiber and the matrix are discussed in terms of their likely effects on mechanical properties.

Brindley, P. K.↗

NASA NTRS1986

Further observations of SCC in alpha-beta brass Considerations regarding the appearance of crack arrest markings during SCC

A series of constant displacement and constant extension rate stress corrosion cracking (SCC) tests was performed on an alpha-beta brass alloy in 1 N Na2SO4 solutions. The chosen mechanical and electrochemical conditions resulted in predominantly transgranular, cleavage-like failure at high (about 8 to 50 microns/s) average crack propagation rates. Crack arrest markings were observed on selected transgranular facets, which almost exclusively bordered regions of ductile overload failure. It is proposed that the observed crack velocities and the specific nature of the arrest mark appearance are most consistent with a cracking mechanism involving adsorption or some other interaction with a damaging environmental species.