Analysis of PICA-NuSil at the Hypersonic Materials Environmental Test System (HyMETS)
Phenolic Impregnated Carbon Ablator (PICA) gained heritage during the stardust mission and is the baseline material for missions to Mars. The phenolic phase of PICA is friable, and therefore the surface is treated with a siloxane resin (NuSil) to mitigate the shedding of particulate matter. Historically, material response models have not accounted for the presence of this coating. Therefore, a test campaign was executed at the Hypersonic Materials Environmental Test System (HyMETS) to investigate the performance of NuSil under multiple heating rates and gas composition. Sphere-cone models were instrumented with thermocouples to measure the in-depth temperature response, and surface temperatures were monitored with a pyrometer. Furthermore, emission spectrometers were used to collect spectra from species emitting at the surface of the test article and the post-shock stagnation region. Post-test analysis suggests that the coating decomposes according to multiple stages. Inspection of silicon emission data reveals a rapid rise and decline in intensity within the first couple of seconds of testing, which is attributed to pyrolysis of NuSil. Pyrolysis is followed by a stagnation in silicon emission and surface temperature which are attributed to the formation of a thin layer of oxidation-resistant silicon oxycarbide. Moreover, the presence of the silicon oxycarbide layer significantly reduces the in-depth thermal response when compared to the baseline material. Eventually, the silicon oxycarbide layer decomposes via high-temperature reactions, which expose the underlying char layer to a highly reactive flow.