Engineering topics
Publications and source records attributed to Bryce, Keith.
Elemental release: amorphous Y 2 Si 2 O 7 is leached in pH 3 nitric acid. Post-leaching characterization of the leachate and pellet surface indicates a preferential release of Y, and the formation of an SiO 2 alteration layer on the surface of the pellet.
Multicomponent zirconate solid solutions A 2 Zr 2 O 7 (A= (Sm,Yb), (Sm,Yb,Gd), (Sm,Yb,Gd,Er), and (Sm,Yb,Gd,Er,Dy)) were synthesized through spark plasma sintering and their chemical durability was investigated via semi-dynamic leaching tests in pH = 1 nitric acid at 90°C. Incongruent dissolution occurred for all samples with the preferential elemental release of zirconium in all A 2 Zr 2 O 7 except for high entropy (Sm,Yb,Gd,Er,Dy)Zr 2 O 7 which displays a congruent release of the A-site elements and Zr. A strong positive correlation was found between the lanthanide elemental release rates and the A-site cation size disorder, whereas a negative correlation was observed between the elemental release rates and mixing entropy.
Chemical durability of compositionally-complex rare-earth titanate pyrochlore solid solutions with or without uranium incorporation was investigated by semi-dynamic leaching testing. A Ti-enriched amorphous passivation film formed on the surface due to the surface alteration-reorganization mechanism with preferential release of the weakly oxygen-bonded rare earth elements. Elemental release was found to be strongly correlated with chemical disorder, with a negligible correlation with entropy. The release rate of the uranium gradually decreased with increasing numbers of components, implying a possibility of designing and optimizing waste form performance with enhanced chemical durability by controlling composition complexity and chemical disorder for effective nuclear waste management.
Elemental release: a CsPbI 3 perovskite pellet is leached in distilled water; post-leaching analysis indicates the formation of PbI 2 and PbI(OH) alteration layers on the pellet surface, and the incongruent release of elements into the leachate.
Multicomponent pyrochlore solid solutions with and without uranium incorporation were fabricated and their thermal-mechanical properties were characterized. Multicomponent pyrochlore solid solutions without uranium exhibit comparable thermal conductivity and higher mechanical strength compared to baseline single component rare-earth titanate pyrochlore (A 2 Ti 2 O 7 ). Uranium incorporation reduces hardness as compared with single component compositions. High entropy pyrochlore with uranium displays the highest thermal conductivity within multicomponent pyrochlore solid solutions with significantly better mechanical properties than UO 2 . The measured thermal conductivity correlates well with A-site cation mixing entropy and a modified size disorder parameter, and thus the size disorder and mixing entropy could be good indicators for predicting thermal conductivity of multicomponent pyrochlore solid solutions. This work opens up the possibility of designing multicomponent oxide solid solutions by controlling their chemical disorder/mixing entropy to achieve acceptable thermal-mechanical properties, desired radiation and corrosion performance for potential nuclear waste form and inert matrix fuel applications.