Engineering topics

Bui, Vinh

Publications and source records attributed to Bui, Vinh.

4 records

DOE OSTI2023

Ultrathin polyorganosilica membranes synthesized by oxygen-plasma treatment of polysiloxanes for H 2 /CO 2 separation

Oxygen plasma treatment of polydimethylsiloxane (PDMS) induces an ultrathin polyorganosilica (POSi) layer (<10 nm) on top of a PDMS membrane, leading to excellent H 2 /gas separation properties and providing a rapid and scalable way to fabricate robust silica membranes compared with conventional high-temperature and time-consuming sol-gel methods. Here, we thoroughly investigate POSi membranes derived from poly (dimethylsiloxane-co-methylhydroxidesiloxane) (poly (DMS-co-MHOS)) containing -SiOH groups that can be more easily converted to silica networks than the -SiCH 3 in PDMS. Further, the effect of the polysiloxane structure and plasma treatment conditions (including plasma generating powers, oxygen flowrate, chamber pressure, and treatment time) on the silica chemistry, structure, and H 2 /CO 2 separation properties are systematically determined to derive structure/property relationships. An optimized membrane exhibits H 2 permeance of 880 GPU and H 2 /CO 2 selectivity of 67 at 150 °C, superior to state-of-the-art polymeric membranes. The membrane retains H 2 /CO 2 selectivity as high as 46 when challenged with simulated syngas containing 2.8 mol% water vapor at 150 °C, demonstrating the potential of these POSi membranes for practical applications.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Membrane Adsorbents Comprising Self-Assembled Inorganic Nanocages (SINCs) for Super-fast Direct Air Capture Enabled by Passive Cooling

The objectives of the proposed project were to develop highly porous membrane adsorbents comprising CO 2 -philic polymers and self-assembled inorganic nanocages (SINCs) for rapid temperature swing adsorption using electricity-free solar heating and radiative cooling, enabling an economically viable approach for direct air capture (DAC). Our core technical activities combine three key innovations. (1) Highly porous flat-sheet membrane adsorbents contain CO 2 -philic amines that can be easily produced using a phase inversion method. (2) CO 2 -philic SINCs can be easily dispersed in the polymers with great stability (compared with the metal-organic frameworks or MOFs). (3) The adsorption and desorption are integrated with solar heating and radiative cooling for rapid continuous operation, in contrast to traditional long-cycle separate operation. The membrane adsorbents containing amines, polymers, and SINCs were produced using a one-step industrial process. The porous membranes coupled with porous SINCs offer low resistance for gas flow and fast CO 2 sorption/desorption cycles, while the incorporation of the additional amine groups provides high CO 2 sorption capacity. The key achievements are summarized below. (1) Membrane adsorbents with high PEI loading (>40%), high porosity of >80%, and low gasflow resistance were prepared in one step using commercially available, low-cost materials. (2) Membrane adsorbents based on Solupor and PEI show CO 2 sorption capacity of >1.5 mmol/g using air containing 400 ppm at a relative humidity of 15%. (3) Effect of the adsorbent compositions (such as PEI type, PEI content, SINC content, porosity) on the CO 2 sorption was systematically investigated. (4) Effect of the processing conditions (such as CO 2 content, temperature, and relative humidity) on the CO 2 sorption was systematically investigated; (5) The stability of the membrane adsorption against many cycles of sorption and desorption was studied. The higher molecular weight of PEI (PEI25k) shows better stability than PEI800. (6) Advanced materials with radiative cooling were developed, which can decrease the temperature by 5-7 °C compared to the ambient temperature. (7) Preliminary techno-economic analysis shows that our process may achieve a capture cost of $1,343/tonne CO 2 with a total OPEX cost of $1,112/tonne CO 2 . The adsorbent replacement cost accounted for 52% of the total OPEX cost. Membrane adsorbents with lower costs and longer operation life can significantly decrease the cost. The proposed project directly addresses the requirement of DE-FOA-0002188, i.e., novel materials with CO 2 adsorption capacity for direct air capture with integrated solar heating and radiative cooling to reduce the cost of the DAC. Our future work will focus on the development of low-cost adsorbents that can be stable at the sorption and desorption conditions for long term.

14 SOLAR ENERGY↗

DOE OSTI2022

Development of Carbon Molecular Sieves Hollow Fiber Membranes based on Polybenzimidazole Doped with Polyprotic Acids with Superior H 2 /CO 2 Separation Properties (Final Report)

The goal of this project was to develop a highly efficient membrane-based process to capture CO 2 from coal-derived syngas with 95% CO 2 purity, achieving the cost of electricity (COE) 30% below the baseline capture approaches (i.e., Selexol process) when coupled with the advancement in other areas of the power generation facility. Our core approach is based on high-permeance hollow fiber membranes (HFMs) with superior H 2 /CO 2 separation properties at the syngas process conditions, which can then be further utilized to design membrane reactors for process intensification of H 2 production and purification and CO 2 capture. Three organizations with complementary skills collaborated to achieve the goal, including the University at Buffalo (UB), Los Alamos National Laboratory (LANL), and Trimeric Corporation (Trimeric). We formulated logical steps to bring the membrane technology from Technology Readiness Level (TRL) 3 (Experimental proof of concept) to TRL 4 (Laboratory scale validation in relevant environment). During the budget period (BP) 1, we screened various polymeric materials and identified polybenzimidazole doped with inorganic polyprotic acids as the desirable platform. The acid doping increases the H 2 /CO 2 selectivity, and the sequential carbonization increases H 2 permeability while retaining the high selectivity. By manipulating the acid type and doping level and the carbonization temperature, we demonstrated advanced carbon molecular sieving (CMS) materials with H 2 permeability of above 200 Barrer (1 Barrer = 10 -10 cm 3 (STP) cm cm -2 s -2 cmHg -1 ) and H 2 /CO 2 selectivity of above 40 at 200-300°C with simulated syngas containing CO and water vapor. For example, the PBI-(H 3 PO 4 ) 0.11 carbonized at 700 °C exhibits H 2 permeability of 200 Barrer and H 2 /CO 2 selectivity of 60 at 200 °C, and H 2 permeability of 240 Barrer and H 2 /CO 2 selectivity of 54 at 225 °C, which meets the targeted properties and surpasses Robeson’s upper bound. During the BP2, we focused on the conversion of the advanced CMS materials to stable HFMs. Membranes with H 2 permeance of 1,090 GPU (1 GPU = 10 -6 cm 3 (STP) cm -2 s -2 cmHg -1 ) and H 2 /CO 2 selectivity of 57 at 300 °C were successfully fabricated. The effects of temperature, gas compositions, pressure, and time on the separation properties were systematically investigated. Pencil modules were continuously evaluated for 219 h (dry pure gas) and 669 h (dry simulated syngas) and showed initial decline in permeance and increased H 2 /CO 2 selectivity over time, ultimately achieving a steady state stable value, indicating that the ageing phenomena in the nanoporous structures of the membranes during the test. Membrane reactors were fabricated based on the CMS membranes and evaluated for water-gas shift (WGS) reaction. The use of membranes slightly improves the conversion of the CO. However, parametric tests of the membrane reactors at various temperatures and flow rates need to be conducted, as well as the membranes with improved separation performance. We performed a sensitivity analysis on the impact of H 2 /CO 2 selectivity on the COE based on a hybrid process of a membrane unit and cryogenic unit developed by Membrane Technology and Research, Inc. (MTR). Three H 2 /CO 2 selectivity (40, 60, and 15) cases were developed and compared with the baseline capture process (Case B5B) provided by the DOE report. Increasing the membrane H 2 /CO 2 selectivity reduces COE, but the rate of the decrease of COE also diminishes. The COE values for H 2 /CO 2 selectivities of 40 and 60 were nearly the same. As the H 2 /CO 2 selectivity increases, the inert recycling decreases, leading to smaller equipment, less auxiliary power requirements, and less heating, cooling, and refrigeration duty. The refrigeration system used to liquefy the CO 2 is the most expensive piece of equipment and consumes the most electricity within the CO 2 capture process. Increasing the CO 2 concentration in the recycle stream would improve the economics of the process by reducing the refrigeration duty requirement of the unit and also allow for higher liquefaction temperatures. The high H 2 -selective membrane developed by our team may be applicable in other separation processes where lower pressure H 2 retains value. Typically, hydrogen retains its pressure when it is separated from syngas components. Residual components may be used as low-quality fuel and then vented to the atmosphere. Applications might include control of H 2 /CO ratios or mitigation of the water gas shift reaction by CO 2 recycling to the feed of a gasifier or steam methane reformer. To summarize, we have developed industrial HFMs with the best H 2 /CO 2 separation performance reported in the literature. The membranes demonstrate stability with simulated syngas and show great potential for membrane reactors for WGS reactions, lowering the cost of blue H 2 production.

20 FOSSIL-FUELED POWER PLANTS↗

DOE OSTI2020

Molecularly engineering polymeric membranes for H 2 / CO 2 separation at 100–300 °C

Over the last two decades, polymers with superior H 2 /CO 2 separation properties at 100–300 °C have gathered significant interest for H 2 purification and CO 2 capture. This timely review presents various strategies adopted to molecularly engineer polymers for this application. We first elucidate the Robeson's upper bound at elevated temperatures for H 2 /CO 2 separation and the advantages of high-temperature operation (such as improved solubility selectivity and absence of CO 2 plasticization), compared with conventional membrane gas separations at ~35 °C. Second, we describe commercially relevant membranes for the separation and highlight materials with free volumes tuned to discriminate H 2 and CO 2 , including functional polymers (such as polybenzimidazole) and engineered polymers by cross-linking, blending, thermal treatment, thermal rearrangement, and carbonization. Third, we succinctly discuss mixed matrix materials containing size-sieving or H 2 -sorptive nanofillers with attractive H 2 /CO 2 separation properties.

42 ENGINEERING↗