High temperature solid lubrication by catalytically generated carbon

The wear process in bearings generates a clean active surface. Carbon is known to form readily on catalytic surfaces through the reduction of carbon oxides or hydrocarbon. Carbon, through the adsorption of hydrocarbons, water vapor, or oxygen, becomes an effective lubricant. If these three phenomena can be made to work together, a new concept of high temperature lubrication would be available. This paper presents laboratory investigations towards the development of this concept. Carbon has been successfully produced through catalytic reduction of ethylene on a variety of metallic and ceramic surfaces containing nickel. This carbon has been shown to reduce friction at a sliding interface at elevated temperatures.

Lauer, James L.↗

NASA NTRS1988

Investigation of PTFE transfer films by infrared emission spectroscopy and phase-locked ellipsometry

When a PTFE sheet was rubbed unidirectionally over a smooth surface of stainless steel an essentially monomolecular transfer film was formed. by ellipsometric and emission infrared spectroscopic techniques it was shown that the film was 10 to 15 A thick and birefringent. From the intensity differences of infrared bands obtained with a polarizer passing radiation polarized in mutually perpendicular planes, it was possible to deduce transfer film orientation with the direction of rubbing. After standing in air for several weeks the transfer films apparently increased in thickness by as much as threefold. At the same time both the index of refraction and the absorption index decreased. Examination of the surfaces by optical and electron microscopies showed that the films had become porous and flaky. These observations were consistent with previous tribological measurements. The coefficients of friction decreased with the formation of the transfer film but increased again as the film developed breaks. The applicability of the ellipsometric and polarized infrared emission techniques to the identification of monomolecular tribological transfer films of polymers such as PTFE has been demonstrated.

Lauer, James L.↗

NASA NTRS1987

Investigation of PTFE transfer films by infrared emission spectroscopy and phase-locked ellipsometry

When a PTFE sheet was rubbed unidirectionally over a smooth surface of stainless steel an essentially monomolecular transfer film was formed. By ellipsometric and emission infrared spectroscopic techniques it was shown that the film was 10 to 15 A thick and birefringent. From the intensity differences of infrared bands obtained with a polarizer passing radiation polarized in mutually perpendicular planes, it was possible to deduce transfer film orientation with the direction of rubbing. After standing in air for several weeks the transfer films apparently increased in thickness by as much as threefold. At the same time both the index of refraction and the absorption index decreased. Examination of the surfaces by optical and electron microscopies showed that the films had become porous and flaky. These observations were consistent with previous tribological measurements. The coefficients of friction decreased with the formation of the transfer film but increased again as the film developed breaks. The applicability of the ellipsometric and polarized infrared emission techniques to the identification of monomolecular tribological transfer films of polymers such as PTFE has been demonstrated.

Lauer, James L.↗