Engineering topics

Burns, Zachary M.

Publications and source records attributed to Burns, Zachary M..

7 records

DOE OSTI2023

Comparison of unirradiated and irradiated AGR-2 TRISO fuel particle oxidation response

The silicon carbide (SiC) coating in a tristructural isotropic (TRISO) particle acts as a barrier to fission product release during reactor operation and accident scenarios. Oxidation and subsequent failure of the SiC layer during a rare air ingress event is a proposed mechanism for fission product release in a high-temperature gas-cooled reactor (HTGR). Although previous oxidation studies have analyzed unirradiated TRISO particle response, this study compared the oxidation behavior of irradiated and unirradiated TRISO particles from the second Advanced Gas Reactor Fuel Development and Qualification Program irradiation experiment (AGR-2). Particles with exposed SiC were subjected to six varying oxidizing tests in the Furnace for Irradiated TRISO Testing (FITT), examined for failure fraction with the Irradiated Microsphere Gamma Analyzer (IMGA) and characterized with focused ion beam and scanning/transmission electron microscopy techniques to analyze the oxide layer. Uncorrelated unirradiated particle failures throughout the series of exposures suggests that external factors inherent to the experiment increased particle failure sensitivity. However, irradiated particle observations indicated an increased failure response at 400 h 1400 °C in both 2% and 21% O 2 atmospheres above failure associated with external factors. Oxide thickness measurements after 400 h at 1400 °C revealed a greater oxidation rate than predicted by parabolic growth, which was attributed to the increased complexity of the oxide structure at longer exposure times. Altering the atmosphere from 21% to 2% O 2 reduced the average oxide thickness by approximately 12%–14% in both irradiated and unirradiated particles at 400 h 1400 °C. Altogether, the minor variations observed between irradiated and unirradiated particles in this study led to the conclusion that unirradiated TRISO particles can be used to approximate irradiated TRISO oxidation kinetics.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Oxidation Testing and Examination of AGR-2 Particles

Post-irradiation examination (PIE) oxidation testing is being performed at Oak Ridge National Laboratory (ORNL) on fuel particles from the second Advanced Gas Reactor (AGR) irradiation experiment (AGR-2). Tristructural isotropic (TRISO)-coated particles containing mixed uranium carbide and uranium oxide (UCO) fuel kernels were taken from AGR-2 Compact 5-4-2 and heated in the Furnace for Irradiated TRISO Testing (FITT) under varying oxidizing conditions. Details on Compact 5-4-2 PIE can be found in a previous report (Hunn et al. 2018).

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

High Temperature Steam Oxidation of Irradiated FeCrAl in the Severe Accident Test Station

FeCrAl-UO2 test capsules were fabricated at Oak Ridge National Laboratory (ORNL) and irradiated at the Advanced Test Reactor. Following irradiation, samples were sectioned from the irradiated rod and oxidation kinetics were evaluated to access the candidate cladding high-temperature oxidation performance following irradiation. The irradiation was performed at approximately 400°C to a burnup of 10 GWd/MT. The high-temperature oxidation tests were conducted in the ORNL Severe Accident Test Station at 1200 and 1300°C. Weight measurements were taken before and after oxidation testing. Cross-sections of the cladding were metallographically mounted and optical microscopy was performed. Measurements of the oxidation layer before and after high-temperature testing were collected. The results indicate the irradiated FeCrAl C35M alloy provided good thermal stability up to 1200°C.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Sister Rod Destructive Examinations (FY20) Appendix B: Segmentation, Defueling, Metallograhic Data and Total Cladding Hydrogen

As a part of the US DOE-NE High Burnup Spent Fuel Data Project, ORNL is performing destructive examinations (DEs) of high burnup (>45 gigawatt days per metric ton uranium) spent nuclear fuel (SNF) rods from the North Anna Nuclear Power Station operated by Dominion Energy. The SNF rods, called the “sister rods,” are all HBU and include four different kinds of fuel rod cladding: standard Zircaloy-4, low-tin Zircaloy-4, ZIRLO®, and M5®. The DEs are being conducted to obtain a baseline of the HBU rod’s condition prior to dry storage and are focused on understanding overall SNF rod strength and durability. Both composite fuel and empty cladding are being tested. While the data generated can be used for multiple purposes, a primary goal for obtaining the post-irradiation examination data and the associated measured mechanical properties is to support SNF dry storage licensing and relicensing activities.This report documents the status of the ORNL Phase 1 DE activities related to: rough segmentation, defueling, optical microscopy, and cladding total hydrogen measurements for 7 Phase 1 sister rods and outlines the DE tasks performed and the data collected to date. The results of these detailed examinations and others are summarized in the Sister Rod DE Status Report.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

AGR-2 Loose Particle Heating Tests in the Furnace for Irradiated TRISO Testing

A furnace system was developed to thermally expose individual tristructural-isotropic (TRISO) coated particles to expand upon established postirradiation examination (PIE) safety testing that is used to explore particle failures and fission product release from compacts. Two systems were installed in the Irradiated Fuels Examination Facility (IFEL) at Oak Ridge National Laboratory (ORNL). The targeted design was intended to be simple and flexible to allow a range in conditions to be explored. Initial inert atmosphere testing indicated the presence of particle failures, so modifications to the testing approach were implemented to improve the furnace operation. Ultimately, burnback particles were analyzed to provide a direct measurement of fission product release, thus avoiding the complications from integral release that were observed during whole compact testing. Particles were exposed to temperatures ranging 1,150–1,300°C for up to 1,500 h and 1,600°C up to 500 h. No indication of uniform release of fission products such as 106 Ru, 125 Sb, or 154 Eu was observed, however, indication of particle dependent 154 Eu release was suggested for select particles. Exploration of 110m Ag release was limited to 1,150°C and 1,300°C up to 500 h. The analysis indicated that there was nonuniform release of 110m Ag and supports a possible bimodal temperature dependence on silver release.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Integral LOCA fragmentation test on high-burnup fuel

Increasing the fuel burnup limit in light water reactors is sought to enhance fuel cycle economics and requires establishing a technical basis. Experimental observations of severe fuel fragmentation under loss-of-coolant-accident conditions at Halden and Studsvik had raised the need for additional considerations during the development of this technical basis. These test data suggested that the burnup threshold for high burnup fuel fragmentation may be influenced by pre-transient power. Additional loss-of-coolant-accident test data is therefore valuable to complement these tests and enhance the current state of understating. Oak Ridge National Lab has developed the Severe Accident Test Station capable of examining the oxidation kinetics and accident response of irradiated fuel and cladding materials for design basis accident and beyond design basis accident scenarios. Severe Accident Test Station provides various temperature profiles, steam, and the thermal shock conditions necessary for integral loss of coolant accident testing, defueled oxidation quench testing, and high-temperature beyond design basis accident testing. Severe Accident Test Station has been successfully installed and demonstrated in the Irradiated Fuels Examination Laboratory at Oak Ridge National Lab. Furthermore, descriptions of the in-cell re-fabrication capabilities and assembly of the loss-of-coolant-accident test train are provided. Installation of the Severe Accident Test Station system and in-cell re-fabrication restores United States capability to examine postulated and extended loss-of-coolant-accident conditions on spent fuel and cladding and provides a platform for evaluating advanced fuel and accident-tolerant fuel cladding concepts. Lastly, three in-cell integral loss-of-coolant-accident test were performed in the Severe Accident Test Station and compared to the Nuclear Regulatory Commission sponsored loss-of-coolant-accident test as well as the original loss-of-coolant-accident test performed at Argonne National Lab. Finally, the results of these tests as well as all publicly available integral loss-of-coolant-accident test were used to validate a threshold for high burnup fuel fragmentation.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Safety Testing and Destructive Examination of AGR-2 UO 2 Compact 3-1-1

Post-irradiation examination and elevated-temperature safety testing are being performed on compacts from the Advanced Gas Reactor (AGR) Fuel Development and Qualification Program’s second irradiation experiment (AGR-2). The compacts in the AGR-2 irradiation experiment held either tristructural isotropic (TRISO)-coated particles containing uranium oxide fuel kernels (UO 2 ) or TRISO-coated particles containing fuel kernels with both uranium carbide and uranium oxide phases (UCO). In UO 2 TRISO particles, oxygen released by uranium fission can react with the surrounding carbon in the buffer layer to form carbon monoxide (CO). Excess CO can lead to various irradiation performance issues under certain operating conditions, such as pressure-induced fracture, kernel migration, and silicon carbide (SiC) corrosion. In UCO TRISO particles, CO formation is reduced because the chemical potential for oxidation of uranium carbide is lower than for oxidation of carbon.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗