Surface studies on Surveyor 3 tubing sections
Sections C and E of the unpainted, polished aluminum tubing from the strut of the radar altimeter and Doppler velocity sensor were examined in a transmission electron microscope for micrometeorite damage and ion bombardment. Both sections were contaminated and eroded on one side; it is suggested that these conditions were caused by sandblasting by lunar dust and retrorocket plume contamination during Surveyor 3 landing. Microcraters of different configurations were found on the bright sides of the tubes. Several degrees of violence were involved in the formation of the craters, and the particle size could be responsible for some differences. All micropits found were on the bright areas and data indicate 0.2 hypervelocity impact/sq cm and 2/sq cm for other types of craters. The greatest degree of damage resulted from particle impact and was limited to a maximum depth of 2 microns.