Engineering topics

Buzek, B.

Publications and source records attributed to Buzek, B..

7 records

NASA NTRS1986

Si3N4-Based Ceramic With Greater Hot Strength

Zyttrite-doped material outperforms MgO-doped material above 1,200 degrees C. New ceramic material produced by addition of 10 weight percent zyttrite (yttria-stabilized zirconia) to (silicon nitride) offers significantly-improved high-temperature properties (those of MgO-doped Si3N4 ceramic). Work also showed that controlled Si3N4 powder with 10 weight percent zyttrite, significant improvement in room-temperature strength achieved. Variety of high-temperature structural applications are silicon nitride and silicon carbide. Potential for use in aircraft and automobile engines and in electric-power generating systems. Improved properties strongly suggest that the 10-weight percent zyttrite/Si3N4 material has strong potential for high-temperature applications.

Dutta, S.↗

NASA NTRS1984

Microstructure, strength, and oxidation of a 10 wt pct zyttrite-Si3N4 ceramic

Hot pressed Si3N4 doped with 10 wt pct zyttrite as a sintering aid was studied. An equiaxed, fine grained microstructure was predominant, with no apparent porosity. Bend strengths were determined at room temperature and high temperatures (up to 1370 C). Oxidation was measured by weight gain at 1370 C in air. The resulting material exhibited very good room temperature strength (755 MPa). The work showed that room temperature strength can be improved significantly by using controlled Si3N4 powder with 10 wt pct zyttrite. High temperature strength (514 MPa) at 1370 C was nearly double that of hot-pressed Si3N4 (NC-132). The oxidation resistance at 1370 C was also higher than that of NC-132.

Dutta, S.↗

NASA NTRS1981

Frictional and morphological characteristics of ion plated soft, metallic films

Ion plated metallic films in contrast to films applied by other deposition techniques offer a lower friction coefficient, longer endurance lives and exhibit a gradual increase in friction coefficient after the film has been worn off. The friction coefficients of metallic films are affected by the degree of adherence, thickness and nucleation and growth characteristics. The effective film thickness for the minimum friction coefficient was established for Au and Pb films. The nucleation and growth characteristics during ion plating lead to a fine, continuous crystalline structure, which contributes to a lower friction coefficient.

Spalvins, T.↗

NASA NTRS1981

Frictional and morphological characteristics of ion plated soft, metallic films

Ion plated metallic films in contrast to films applied by other deposition techniques offer a lower friction coefficient, longer endurance lives and exhibit a gradual increase in friction coefficient after the film has been worn off. The friction coefficients of metallic films are affected by the degree of adherence, thickness and nucleation and growth characteristics during ion plating lead to a fine, continuous crystalline structure, which contributes to a lower friction coefficient.

Spalvins, T.↗

NASA NTRS1976

Fundamental studies of black chrome for solar collector use

The thicknesses of black chrome plated for various times have been measured from electron photomicrographs and correlated with the solar spectrum absorptance and infrared emittance as calculated from spectral reflectance measurements. The maximum absorptance is reached at an average thickness of 0.5 micrometer. The emittance increases only slightly up to 1.0 micrometer but increases rapidly at thickness above 1.0 micrometer.

Mcdonald, G.↗

NASA NTRS1976

Fundamental studies of black chrome for solar collector use

Mcdonald, G.↗

NASA NTRS1973

An Exploratory Study of the Microstructure of Mullite Fibers

The microstructures of mullite composition fibers were examined by transmission electron microscopic techniques and by X-ray diffraction analyses. Both spun and monofilament fiber structures contained little porosity, nor did the degree of porosity change after heating the monofilament to 1205 C for one half hour. Thermal exposure produced crystallite growth and nucleation from the amorphous phase in all three of the spun fibers. After 116 hours at 1426 C, the crystallites of the standard spun fibers became contiguous. In addition, the surface crystallites of these fibers were found to be more than twice as large as the interior crystallites.

Santoro, G.↗