Nanostructure refinement and phase formation of flash annealed FeNi-based soft magnetic alloys

In this work, the resulting nanocomposite microstructures of FeNi nanocrystallites under different heating and cooling rates (5 °C/min vs 400-500 °C/s) is investigated. Conventional furnace annealing under low heating rates and slow cooling resulted in both BCC α-FeNi and FCC γ-FeNi nanocrystallites with an average grain size on the order of 25-27 nm whereas high heating rates achieved via flash annealing techniques have enabled a dramatically refined microstructure consisting of 5-7 nm grains with FCC γ-FeNi phase and found to be the dominant phase following primary crystallization. Grain size refinement and phase identity optimization yielded low values of coercivities-17 A/m and high permeability similar to 11 x 10 3 measured at 400 Hz/1 kA/m in flash annealed samples at 450 °C for 5 s. The magnetic behavior and the underlying mechanism of optimal soft magnetic properties are discussed in terms of the critical role of the grain size in domain wall pinning and coercivity.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Surface oxidation and crystallization of FeNi-Based soft magnetic nanocrystalline and amorphous nanocomposite alloys

In this work, we present characterization of surface oxidation and crystallization behavior of Metal Amorphous Nanocomposite (MANC) (Fe 70 Ni 30 ) 80 Nb 4 Si 2 B 14 alloys via complementary x-ray diffraction, electron microscopy, and x-ray photoelectron spectroscopy techniques. An adherent amorphous oxide of roughly 15–20 nm in thickness is observed on the wheel side of the ribbon, enriched in Fe relative to Ni and with significant content of Si and Nb as would be expected based upon a comparison of the Gibbs free energy of formation of the stable oxide phases. The amorphous character of the oxide is likely to result from the significant Si-content coupled with the amorphous and nanocrystalline character of the underlying metallic layer. Higher density of FeNi-enriched nanocrystals is also observed within ~100 nm of the wheel-side surface, presumably due to reduction in local glass former concentration. A rough, crystalline copper oxide layer is also present and forms through contact between the copper wheel and the solidifying melt during the rapid solidification process. On the air side of the ribbon, a crystalline oxide layer of ~15–20 nm is formed as well as intergranular oxidation that penetrates along the grain boundaries between highly textured surface crystallites of ~50–100 nm in size. The crystalline nature of the oxide on these surfaces is asserted to result from the lack of significant Si-content and the pre-existing surface crystallites that form during the rapid solidification process which promote a crystalline oxide surface layer. Furthermore, these results shed new insights into the details of surface oxidation and can help to inform processing and alloy composition adjustments which seek to tailor surface properties.

36 MATERIALS SCIENCE↗

NASA NTRS2004

Microwave-Spectral Signatures Would Reveal Concealed Objects

A proposed technique for locating concealed objects (especially small antipersonnel land mines) involves the acquisition and processing of spectral signatures over broad microwave frequency bands. This technique was conceived to overcome the weaknesses of older narrow- band electromagnetic techniques like ground-probing radar and low-frequency electromagnetic induction. Ground-probing radar is susceptible to false detections and/or interference caused by rocks, roots, air pockets, soil inhomogeneities, ice, liquid water, and miscellaneous buried objects other than those sought. Moreover, if the radar frequency happens to be one for which the permittivity of a sought object matches the permittivity of the surrounding soil or there is an unfavorable complex-amplitude addition of the radar reflection at the receiver, then the object is not detected. Low-frequency electromagnetic induction works well for detecting metallic objects, but the amounts of metal in plastic mines are often too small to be detectable. The potential advantage of the proposed technique arises from the fact that wideband spectral signatures generally contain more relevant information than do narrow-band signals. Consequently, spectral signatures could be used to make better decisions regarding whether concealed objects are present and whether they are the ones sought. In some cases, spectral signatures could provide information on the depths, sizes, shapes, and compositions of objects. An apparatus to implement the proposed technique (see Figure 1) could be assembled from equipment already in common use. Typically, such an apparatus would include a radio-frequency (RF) transmitter/receiver, a broad-band microwave antenna, and a fast personal computer loaded with appropriate software. In operation, the counter would be turned on, the antenna would be aimed at the ground or other mass suspected to contain a mine or other sought object, and the operating frequency would be swept over the band of interest.

Arndt, G.↗