DOE OSTI2024

Cost-Effective Thermomechanical Processing of Nanostructured Ferritic Alloys: Microstructure and Mechanical Properties Investigation

Nanostructured ferritic alloys (NFAs), such as oxide-dispersion strengthened (ODS) alloys, play a vital role in advanced fission and fusion reactors, offering superior properties when incorporating nanoparticles under irradiation. Despite their importance, the high cost of mass-producing NFAs through mechanical milling presents a challenge. This study delves into the microstructure-mechanical property correlations of three NFAs produced using a novel, cost-effective approach combining severe plastic deformation (SPD) with the continuous thermomechanical processing (CTMP) method. Analysis using scanning electron microscopy (SEM)-electron backscatter diffraction (EBSD) revealed nano-grain structures and phases, while scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectroscopy (EDS) quantified the size and density of Ti-N, Y-O, and Cr-O fine particles. Atom probe tomography (APT) further confirmed the absence of finer Y-O particles and characterized the chemical composition of the particles, suggesting possible nitride dispersion strengthening. Correlation of microstructure and mechanical testing results revealed that CTMP alloys, despite having lower nanoparticle densities, exhibit strength and ductility comparable to mechanically milled ODS alloys, likely due to their fine grain structure. However, higher nanoparticle densities may be necessary to prevent cavity swelling under high-temperature irradiation and helium gas production. Further enhancements in uniform nanoparticle distribution and increased sink strength are recommended to mitigate cavity swelling, advancing their suitability for nuclear applications.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Mechanical Performance of Additively Manufactured ODS 316L and 316H Stainless Steels

This work package within the Advanced Materials and Manufacturing Technologies (AMMT) program focused on the mechanical and microstructural characterization of oxide dispersion strengthened (ODS) stainless steels produced using advanced manufacturing techniques. The research aimed to identify an accelerated development path for ODS alloys by integrating additive manufacturing (AM) technologies with recent advancements in ODS materials and traditional manufacturing methods. For FY 24, the research specifically targeted exploring an accelerated development path for ODS alloys by combining AM technologies with these advancements. Novel AM and post-build processing routes were developed for ODS austenitic alloys, including Fe-Cr-Ni alloys such as 316L and 316H. Electron microscopy and mechanical characterizations were conducted to evaluate the impact of process variables on microstructure and properties, with the goal of optimizing these properties economically. Traditionally, producing ODS alloys involves multi-day, high-energy mechanical milling of alloy powder with yttria powder, followed by milled-powder consolidation through extrusion or other methods, and additional thermomechanical processing (TMP) for property control. To overcome the challenges associated with this complex and costly approach, we propose exploring alternative, cost-effective processing routes that emphasize AM and traditional TMP methods. The new processing routes for ODS alloys have achieved significantly higher strengths—several times greater than those of wrought stainless steels—while maintaining substantial ductility and fracture toughness. This report outlines the novel and economical AM-based processing routes for ODS austenitic alloys, combined with post-build TMPs, and discusses the mechanical and microstructural characteristics of the developed materials.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Thermomechanical Processing for Improved Mechanical Properties of HT9 Steels

Thermomechanical processing (TMP) of ferritic–martensitic (FM) steels, such as HT9 (Fe–12Cr–1MoWV) steels, involves normalizing, quenching, and tempering to create a microstructure of fine ferritic/martensitic laths with carbide precipitates. HT9 steels are used in fast reactor core components due to their high-temperature strength and resistance to irradiation damage. However, traditional TMP methods for these steels often result in performance limitations under irradiation, including embrittlement at low temperatures (<~430 °C), insufficient strength and toughness at higher temperatures (>500 °C), and void swelling after high-dose irradiation (>200 dpa). This research aimed to enhance both fracture toughness and strength at high temperatures by creating a quenched and tempered martensitic structure with ultrafine laths and precipitates through rapid quenching and unconventional tempering. Mechanical testing revealed significant variations in strength and fracture toughness depending on the processing route, particularly the tempering conditions. Tailored TMP approaches, combining rapid quenching with limited tempering, elevated strength to levels comparable to nano-oxide strengthened ferritic alloys while preserving fracture toughness. For optimal properties in high-Cr steels for future reactor applications, this study recommends a modified tempering treatment, i.e., post-quench annealing at 500 °C or 600 °C for 1 h, possibly followed by a brief tempering at a slightly higher temperature.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Characteristics of oxide-dispersion strengthened alloys produced by high-temperature severe deformation

This study is to explore an economically attractive and technically feasible processing method for oxide-nanoparticle strengthened alloys for fusion reactor application. Despite many scientific merits of the advanced oxide-dispersion strengthened (ODS) alloys, such as the nanostructured ferritic alloy (NFA) 14YWT, the only viable production path for a high-quality NFA is the high-power mechanical alloying process. This process is often a multi-day high-speed ball milling of alloy powder with a small quantity of yttria (Y 2 O 3 ) powder, followed by the milled-powder consolidation using extrusion or other methods and additional thermomechanical processing (TMP) for property control. This complex production path, including the low-temperature mechanical alloying in particular, has limited technical advancement toward the cost-effective and scale-up production of ODS alloy components. To overcome such a practical limitation, we proposed to explore alternative low-cost processing routes using traditional thermomechanical processing (TMP) method only. Further, a series of continuous TMP cycles, which were designed to impose high-temperature severe plastic deformation (HT-SPD) conditions to the consolidated powder mixtures, were applied to achieve the effective distribution of oxide particles in nanograin structure and thus desirable mechanical properties. Since the reduced-activation ferritic-martensitic (RAFM) alloy powders (Fe-10Cr and Fe-14Cr alloys with various Y contents) are available in our inventory, we focused to utilize the new solid-state synthesis approach for controlling oxide (oxygen source) dissolution and nanoscale clustering in nanograin structure in those alloys. A combination of powder consolidation at 900 °C and continuous thermomechanical activation at 600 °C yielded two essential ODS alloy microstructure contents–nanograin structure and nanoparticle distribution–and thus demonstrated a good combination of strength and ductility.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Deformation and Fracture Behavior of Additively Manufactured 316L Stainless Steel

Tensile deformation and fracture behavior of an additively manufactured (AM) 316L stainless steel (SS) in the as-built, stress-relieved, and solution-annealed conditions was investigated using in situ tensile testing in a scanning electron microscope with an electron back scattering diffraction (SEM–EBSD) detector. Analyses were performed to discuss the characteristic deformation and fracture process of the fine-grained AM 316L SS with and without relaxation heat treatment. The as-built 316L showed the highest strength, and both post-build heat treatments lowered the strength of the alloy. Regardless of the post-build processing, the AM 316L SS showed overall higher strength but slightly lower ductility when compared to the wrought (WT) 316L SS. Analysis of EBSD data indicated that the characteristic microstructural features from AM, such as the complex and fine grain morphology, dislocation network, pores, and silicon-rich oxides, evolved and exerted various roles during the tensile deformation and fracture processes. Further, it was obvious that the interaction of dislocation slips with oxide particles and cavities (or pores) resulted in an accelerated cracking in AM 316L SS. Overall, however, their influence on mechanical behavior was limited, as the genuinely high ductility of 316L SS could help avoid any premature or brittle fracture.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Detecting Thermally-Induced Spinodal Decomposition with Picosecond Ultrasonics in Cast Austenitic Stainless Steels

Destructive techniques to monitor nuclear reactor component health may not always be available during service, as they are time-consuming and often require pre-installed inspection coupons. Non-destructive evaluation (NDE) techniques can bridge this gap by rapidly identifying the state of mission-critical reactor components, via inference between NDE-measurable material properties and those of ultimate interest, such as ductility and toughness. Here, we demonstrate one such inference about the health of thermally aged cast austenitic stainless steels. Observations of surface acoustic wave peak (SAW) splitting correlate with spinodal decomposition-induced embrittlement as destructively measured by Charpy impact energy. Elastodynamic calculations and molecular dynamics simulations of the effects of spinodal decomposition on elastic moduli support that the new acoustic modes present are due to stiffening in the δ-ferrite domains. Finally, this discovery enables one to probe structure-property relationships in materials in a greatly accelerated manner, suggesting that similar inference methods can be used to determine material fitness-for-service, or to quickly uncover new structure-property relationships.

304-type stainless steel↗
DOE OSTI2022

Two-step deformation-induced martensitic transformation in additively manufactured High-Si stainless steel

Deformation-induced phase transformation in the additively manufactured (AM) Fe–18Cr–8Ni-5.5Si (in wt.%) alloy was analyzed using the in-situ electron backscattered diffraction (EBSD) record during uniaxial tensile testing in a scanning electron microscope (SEM). Analysis of EBSD data was focused to investigate phase transformation behavior during deformation with consideration of mechanical interactions among phases and grains in the ultrafine AM microstructure. The initial EBSD phase map illustrated that the as-built microstructure was a duplex structure consisting of major austenite (γ) and minor ferrite phases, some of which showed non-traditional orientation relationship since the rapid solidification in the AM process has produced non-equilibrium state in phase formation. In the deformed as-built AM alloy, the two-step martensitic transformation (γ→ε→α´) was identified as the main deformation-induced transformation mechanism. Martensitic transformation steps were found to be associated with glides of Shockley partial dislocations on closed packed (111) planes under the influence of atomic disturbance in the γ and ε phases, respectively. Using the closed-packed plane pole figures and unit cell orientations, their evolutions and mechanisms accompanying with the transformation were analyzed. Finally, the results indicate that one variant of ε-martensite forms from their parent γ phase, while two variants of α´ form from their parent ε phase.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Deformation Mechanism Transition in Additively Manufactured Compositionally Graded Fe-Base Alloys

Microstructure-dependent deformation and fracture behavior was investigated for an additively manufactured compositionally graded alloy (CGA) printed using the laser-directed energy deposition (L-DED) method to explore an alternative approach for dissimilar metal joints in nuclear energy systems. The electron backscatter diffraction (EBSD) maps from scanning electron microscopy (SEM) display a clear microstructural transition with decreasing austenite-forming elements (Ni and Mn), from an austenite (γ) dominant structure, to a complex composite structure containing ferrite (α), martensite (α') and retained austenite, and then to a fully ferritic structure. EBSD data were recorded in situ during tensile testing in SEM, and the evolution of the deformation mechanism and microstructure was characterized using Kikuchi diffraction pattern analysis. Complementary analysis for high-resolution features was also performed using scanning transmission electron microscopy (STEM). The Ni/Mn-rich austenite-dominant microstructures showed a complex deformation mechanism of two-step martensitic transformation (γ→ε→α'), whereas the minor austenite phase retained in the ferrite and/or martensite matrix showed a single transformation route (γ→α'). Ordinary dislocation glide and twinning via partial dislocation glide were observed in the austenite deformation. Meanwhile, the ferrite and martensite grains deformed mainly by ordinary dislocation slips and grain rotation. Furthermore, static tensile fracture was also highly dependent on local composition and phase constituents.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Irradiation hardening and ductility loss of Eurofer97 steel variants after neutron irradiation to ITER-TBM relevant conditions

Ten Eurofer97 steel variants, produced by non-standard fabrication-processing routes and modified alloying chemistries, were studied by neutron irradiations in the high flux isotope reactor. The irradiations were performed to ITER-TBM relevant conditions of ~255–350 °C, 2.94–3.24 dpa. We quantified the irradiation-induced degradation of the steels using mechanical property tests. All the steels suffered from irradiation hardening, where a significant increase in Vickers microhardness and yield stress (σ YS ) occurred, accompanied with severe loss of tensile elongation. The extent of hardening was material dependent. For T irr = 300±30 °C, most steels showed σ YS increase in the range of ~30% to as high as ~66%, except for a low temperature tempered steel with σYS increase below 15%. Despite large losses in elongation, most failures were ductile. Significant post-necking ductility was retained with reduction in area (RA) between 65–75%, but <50% for low temperature tempered steels. The ultimate tensile stress to yield stress (σ UTS /σ YS ) ratios decreased significantly after irradiation, highlighting irradiation-induced strain hardening capacity reduction. No major effect of irradiation on the plastic instability stress (σ PIS ) and true fracture stress of the steels was observed. By comparing the tensile stresses in true stress units and with literature, the results suggest that RAFM steel designing should target materials with a large separation between σ PIS and σ YS , to ensure the materials can maintain large work hardening and uniform deformation capability after irradiation. The tensile data of the steels additionally revealed a compelling evidence of an inverse trend between the change in RA and increase in σ YS of the neutron irradiated Eurofer97 type steels.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Evolution of the role of molybdenum in duplex stainless steels during thermal aging: From enhancing spinodal decomposition to forming heterogeneous precipitates

Thermal aging of ferrite in duplex stainless steels leads to a complex microstructural evolution that can give way to large deleterious changes in mechanical properties. The microstructural evolution mechanisms that happen concurrently are strongly linked to minor changes in composition. By characterizing duplex stainless steels with various compositions over a range of aging conditions, it was revealed that adding a modest amount of Mo to cast austenitic stainless steel (such as changing from grade CF3 to grade CF3M) not only increases the kinetics of spinodal decomposition and Ni-Si-Mn-rich G-phase precipitation, but it also forms a separate Mo-rich phase. At shorter equivalent aging times, Mo segregates from Fe and towards Cr accelerating spinodal decomposition. At longer aging times, Mo enriches in the Ni-Si-Mn clusters before phase separating into an adjoined Mo-rich cluster. We found that these phase changes and precipitation events result in a rather steep drop in fracture and impact toughness. These results will inform the design of similar alloys for use at high temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Correlative STEM-APT characterization of radiation-induced segregation and precipitation of in-service BWR 304 stainless steel

In this study, radiation induced segregation and precipitation phenomena in an in-service boiling water reactor 304 stainless steel component were investigated using directly correlated 3D-atom probe tomography and scanning transmission electron microscopy. Significant quantitative differences in measured segregation at grain boundaries were found between the atom probe and energy dispersive spectroscopy measurements of the exact same locations. In particular, a much stronger Si segregation (~10 atomic% via atom probe versus ~4 atomic% via electron microscopy) and different Cr profile shapes were detected that are critical to models of radiation induced segregation and stress corrosion cracking behavior. These quantitative differences highlight the need for comparative microscopy and critical evaluation of limitations in each analytical method. Elemental segregation to dislocations and conjoined-clusters were also highlighted by atom probe; confirming and expanding upon what has been observed in test reactor neutron and accelerator-based ion irradiations.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Degradation of impact toughness in cast stainless steels during long-term thermal aging

Cast austenitic stainless steels (CASSs) have been extensively used for the large components of nuclear reactor primary coolant systems. Since the cast steels inevitably contain degradable metastable phases and replacement of the large coolant system components is impractical, the thermal embrittlement of CASS components has been a serious concern in the extended-term operation of nuclear power plants. This study aimed to systematically measure and analyze the effect of long-term thermal aging on the Charpy impact toughness to provide a comprehensive understanding of thermal degradation behavior and a practical aging model to predict the degree of thermal degradation in the cast stainless steels. Additionally, the materials tested in the research include eight CASS alloys (two CF3s, one CF3M, three CF8s, and two CF8Ms) and two reference wrought materials (304L and 316L), in which the nominal δ-ferrite content ranges from ~2% to 33%. These stainless steels have been thermally aged at two light water reactor (LWR) temperatures (290 and 330 °C) and at two accelerated-aging temperatures (360 and 400 °C) for up to 30,000 h; these include both under-aged and over-aged conditions relative to the extended service lifetime (80 years). Charpy impact testing was performed for aged and non-aged specimens, and the impact (absorbed) energy parameters were correlated with a new aging parameter (A). Both the reduction of impact fracture toughness and the shift of ductile-brittle transition temperature were strongly dependent on the δ-ferrite content and degree of thermal aging. A linear relationship was found between the increasing rate of the index transition temperature T 41J and aging parameter A; base on which an empirical model was proposed for prediction of the transition temperature as a simple function of the aging parameter (A) and δ-ferrite content (F). Finally, the critical aging parameter for embrittlement (AC) was evaluated and compared with the existing δ-ferrite content criteria.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Detecting Thermally Induced Spinodal Decomposition with Picosecond Ultrasonics in Cast Austenitic Stainless Steels

Given the existential climate crisis faced by mankind and the world, the lifetime and sustainability of nuclear reactors as a carbon-free source of renewable energy depend on the susceptibility of their structural components to environmental degradation. In particular, critical components for light water reactors (LWRs) evolve over decades in service, losing ductility and toughness due to thermal and irradiation aging. Techniques to monitor their health cannot be easily applied in the field due to their destructive, expensive, or immobile nature. Thus, non-destructive evaluation (NDE) methods are sought to monitor and evaluate the health of major LWR components such as core barrels, steam generator tubes, or primary coolant pipes and are often required by policy, such as NRC policy #10-CFR-50.65. In this work we demonstrate the use of gigahertz, non-contact ultrasonics to gauge the state of cast austenitic stainless steels (CASS), used in some of the largest components in LWR primary systems. We do so by linking changes in their surface acoustic wave (SAW) characteristics using transient grating spectroscopy (TGS) to transmission electron microscopy (TEM)-verified evidence of spinodal decomposition and G-phase precipitation. In this thesis, thermal aging is shown to induce SAW peak splitting in spinodally decomposed CASS alloys, correlated strongly with lowered toughness and decreased ductility. Furthermore, statistical testing on the number of SAW peak splits observed show that the second SAW peak significantly appears more frequently and is significantly different in frequency in comparison to counts and frequencies measured in unaged specimens. The ability of this technique to non-destructively detect microstructural degradation at a distance in a predictive manner in the case of CASS motivates extending gigahertz ultrasonics to detect other LWR material degradation modes as an in-vessel inspection technique, such as reactor pressure vessel (RPV) embrittlement. This allows for the greater use of NDE techniques for confident monitoring of LWR structural material health to 80 years and beyond, saving costs by minimizing structural replacements until needed and maximizing energy production by preventing early decommission until necessary.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Precipitation-site competition in duplex stainless steels: Cu clusters vs spinodal decomposition interfaces as nucleation sites during thermal aging

Competing microstructural evolution mechanisms can exist simultaneously when duplex stainless steels are operating for several decades in a high temperature service environment. Such competition between different microstructural evolution pathways can be difficult to ascertain using simple model alloy systems necessitating detailed structural and compositional analysis of phase transformation mechanisms in complex alloys Thus, in this study duplex stainless steels with complex but well understood chemistries were used to investigate the relative importance of different heterogeneous nucleation sites – specifically spinodal decomposition and Cu clustering – on precipitation of Ni-Si-Mn particles during long term thermal aging. Precipitation of Ni-Si-Mn particles in duplex stainless steels and ferritic steels during thermal aging and irradiation is known to have profound effect on mechanical properties. Using duplex stainless steels with custom modified compositions along with atom probe tomography characterization and first-passage kinetic Monte Carlo (FPKMC) simulations it is revealed that while the interface between Cr and Fe formed during spinodal decomposition can be a pathway for diffusion of Ni, Si, Mn, and Cu, it is not a site that encourages precipitation of Ni-Si-Mn rich particles. Instead, the presence of a higher concentration of Cu in these steels leads to formation of small Cu clusters with high energy interfaces that act as nucleation sites for Ni-Si-Mn particles because of its strong interaction particularly with Ni increasing the chemical driving force for precipitation. These results will help inform predictive models for the use of duplex stainless steels and other precipitation-hardened alloys for extended operation at high temperatures.

Duplex stainless steel, Thermal aging, Precipitati↗
DOE OSTI2019

Fracture Toughness of High-Cr Steels after Various Thermomechanical Treatments

This research aimed to improve the mechanical properties of high-Cr steels by developing new thermomechanical processes for application to advanced fast reactors. A simultaneous improvement of fracture toughness and strength was specifically targeted in the design of thermomechanical processing for various 9Cr and 12Cr steels. For the structural materials of fusion and fast reactors, the high-chromium steels with fine ferritic/martensitic (FM) structures are favored because of their high creep strength and excellent resistance to high-temperature radiation damage such as void swelling. After the traditional thermomechanical treatment consisting of normalizing, water quenching, and tempering, however, the high-Cr steels show limited mechanical properties at high temperatures, e.g., significant decrease of strength above ~450°C. Since the high-Cr steels are tempered at high temperatures (typically around 750°C), significant coarsening of the lath structure and carbides and annihilation of dislocations occur in the final thermomechanical treatment. It is believed that the high-temperature tempering can maximize the ductility of the FM steels, but their high-temperature strength is reduced and often with high-temperature fracture toughness. It is also likely that such a fully-tempered structure will demonstrate a lowered radiation resistance when compared to the steels with finer structures. This research was planned to explore new processing routes that can produce ultrafine microstructures and thus can improve the high-temperature mechanical properties of the high-Cr steels. In this research, three 9Cr steels and two 12Cr steels were selected and a series of new thermomechanical process treatments (TMTs) were designed and applied to the five steels to find the TMT routes that will result in increase of both strength and fracture toughness. It was demonstrated for HT-9 steels that some tailored TMTs increased or maintained the fracture toughness of the high-Cr steels while the treatments could significantly increase their strength to the level comparable to those of nanostructured ferritic alloys. This report compares the fracture toughness data of both 9Cr and 12Cr steels after various thermomechanical treatments with the reference data of similar steels. A two-step tempering route is selected for application to the high-Cr steels for reactor core structures.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Effects of Thermal Aging on the Fracture Toughness of Cast Stainless Steel CF8

Cast stainless steels are widely used in the primary coolant systems of nuclear power plants because of their high strength, toughness, and corrosion resistance. Mechanical property degradation in the steels, primarily due to a thermally-embrittled ferrite, is of major concern in an extended-term operation. To investigate the aging-induced loss of fracture resistance in cast stainless steels, static fracture resistance (J-R) testing was performed for three different CF8 cast stainless steels with significantly different d-ferrite contents. The materials were thermally-aged at 290-400°C for up to 10kh and fracture-tested at 25-400°C. It was found that the fracture toughness in high-ferrite materials generally decreased with thermal aging while the relationship between aging and fracture toughness in low-ferrite materials was rather complicated, showing non-monotonic variation with the degree of aging. While significant degradation was observed for the highly-aged high-ferrite materials, no material was observed having a K0.2mm less than 100 MPavm.

Collins, David A.↗
DOE OSTI2018

SiC-ODS Alloy Gradient Nanocomposites as Novel Cladding Materials

Design and creation of novel SiC-ODS alloy cladding nanocomposites with gradient compositions through colloidal processing and layer deposition. Novel SiC-ODS gradient nanocomposites are designed and created. Procedures for producing such nanocomposites are made available.

36 MATERIALS SCIENCE↗