Precision Structure Engineering of High-Entropy Oxides under Ambient Conditions
High-entropy oxides (HEOs) have unveiled a unique frontier in the realm of heterogeneous catalysis, taking advantage of the entropic effect and increased complexities to deliver ultrahigh stability and large tuning capability. However, current HEO synthesis mainly relies on high-temperature annealing approaches affording HEOs possessing no or low surface area, inferior active site exposure efficiency, and low controllability over the structure tuning. The grand challenge lies in producing high-quality HEO catalysts with high active site utilization efficiency, which relies on precision structure engineering, preferably under mild conditions. In this work, an in situ lattice engineering approach was developed to afford a supported HEO catalyst under ambient conditions. The HEO compositions (CuCoFeNiMnO x ) were uniformly integrated into the lattice of CeO 2 driven by cavitation-induced nucleation being generated via ultrasonication. The as-afforded catalysts were featured by high surface area, atomically dispersed HEO compositions, active redox properties, abundant oxygen vacancies (O V ), antiagglomeration, and high phase stability under harsh conditions. Compared with the ex situ introduction of HEO on the surface, the in situ method provides dual benefits to maintain the dispersity of HEO via entropic and lattice confinement effects. Engineering the complex HEO within the lattice of fluorite-structured CeO 2 also yields abundant defects (e.g., O V ) and active metal sites with strong reducing properties (e.g., Ce 3+ and Cu + ), which greatly improves the activity of the lattice oxygen and tunability of the adsorption behavior of the guest molecules, especially in the presence of impurities (e.g., water and propane). The catalytic performance of the supported HEO catalyst in oxidative procedures surpasses the pure dense phase HEO as well as the ex situ-generated catalysts. Further, the synthesis approach being developed in this work, together with the fundamental understanding in structure evolution and reaction mechanism, showcases a facile pathway under ambient conditions to generate stable catalysts capable of maintaining structural robustness in high-temperature conditions while delivering enhanced catalytic performance.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Fine-Tuning of Pt Dispersion on Al 2 O 3 and Understanding the Nature of Active Pt Sites for Efficient CO and NH 3 Oxidation Reactions
Fine-tuning the dispersion of active metal species on widely used supports is a research hotspot in the catalysis community, which is vital for achieving a balance between the atomic utilization efficiency and the intrinsic activity of active sites. In this work, using bayerite Al(OH) 3 as support directly or after precalcination at 200 or 550 °C, Pt/Al 2 O 3 catalysts with distinct Pt dispersions from single atoms to clusters (ca. 2 nm) were prepared and evaluated for CO and NH 3 removal. Richer surface hydroxyl groups on AlO x (OH) y support were proved to better facilitate the dispersion of Pt. However, Pt/Al 2 O 3 with relatively lower Pt dispersion could exhibit better activity in CO/NH 3 oxidation reactions. Further reaction mechanism study revealed that the Pt sites on Pt/Al 2 O 3 with lower Pt dispersion could be activated to Pt 0 species much easier under the CO oxidation condition, on which a higher CO adsorption capacity and more efficient O 2 activation were achieved simultaneously. Compared to Pt single atoms, PtO x clusters could also better activate NH 3 into –NH 2 and –HNO species. The higher CO adsorption capacity and the more efficient NH 3 /O 2 activation ability on Pt/Al 2 O 3 with relatively lower Pt dispersion well explained its higher CO/NH 3 oxidation activity. This study emphasizes the importance of avoiding a singular pursuit of single-atom catalyst synthesis and instead focusing on achieving the most effective Pt species on Al 2 O 3 support for targeted reactions. Finally, this approach avoids unnecessary limitations and enables a more practical and efficient strategy for Pt catalyst fabrication in emission control applications.
37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
Tuning the Interaction between Platinum Single Atoms and Ceria by Zirconia Doping for Efficient Catalytic Ammonia Oxidation
Aiming at the development of an efficient NH 3 oxidation catalyst to eliminate the harmful NH 3 slip from the stationary flue gas denitrification system and diesel exhaust aftertreatment system, a facile ZrO 2 doping strategy was proposed to construct Pt 1 /Ce x Zr 1–x O 2 catalysts with a tunable Pt-CeO 2 interaction strength and Pt–O–Ce coordination environment. According to the results of systematic characterizations, Pt species supported on Ce x Zr 1–x O 2 were mainly in the form of single atoms when x ≥ 0.7, and the strength of the Pt-CeO 2 interaction and the coordination number of Pt–O–Ce bond (CN Pt–O–Ce ) on Pt 1 /Ce x Zr 1–x O 2 showed a volcanic change as a function of the ZrO 2 doping amount. Here, it was proposed that the balance between the reasonable concentration of oxygen defects and limited surface Zr–O x species well accounted for the strongest Pt-CeO 2 interaction and the highest CN Pt–O–Ce on Pt/Ce 0.9 Zr 0.1 O 2 . It was observed that the Pt/Ce 0.9 Zr 0.1 O 2 catalyst exhibited much higher NH 3 oxidation activity than other Pt/Ce x Zr 1–x O 2 catalysts. The mechanism study revealed that the Pt 1 species with the stronger Pt-CeO 2 interaction and higher CN Pt–O–Ce within Pt/Ce 0.9 Zr 0.1 O 2 could better activate NH 3 adsorbed on Lewis acid sites to react with O 2 thus resulting in superior NH 3 oxidation activity. This work provides a new approach for designing highly efficient Pt/CeO 2 based catalysts for low-temperature NH 3 oxidation.
36 MATERIALS SCIENCE↗
Surface Lattice-Embedded Pt Single-Atom Catalyst on Ceria-Zirconia with Superior Catalytic Performance for Propane Oxidation
Tuning the metal–support interaction and coordination environment of single-atom catalysts can help achieve satisfactory catalytic performance for targeted reactions. Herein, via the facile control of calcination temperatures for Pt catalysts on pre-stabilized Ce 0.9 Zr 0.1 O 2 (CZO) support, Pt single atoms (Pt 1 ) with different strengths of Pt–CeO 2 interaction and coordination environment were successfully constructed. With the increase in calcination temperature from 350 to 750 °C, a stronger Pt–CeO 2 interaction and higher Pt-O-Ce coordination number were achieved due to the reaction between PtO x and surface Ce 3+ species as well as the migration of Pt 1 into the surface lattice of CZO. The Pt/CZO catalyst calcined at 750 °C (Pt/CZO-750) exhibited a surprisingly higher C 3 H 8 oxidation activity than that calcined at 550 °C (Pt/CZO-550). Here, through systematic characterizations and reaction mechanism study, it was revealed that the higher concentration of surface Ce 3+ species/oxygen vacancies and the stronger Pt–CeO 2 interaction on Pt/CZO-750 could better facilitate the activation of oxygen to oxidize C 3 H 8 into reactive carbonate/carboxyl species and further promote the transformation of these intermediates into gaseous CO 2 . The Pt/CZO-750 catalyst can be a potential candidate for the catalytic removal of hydrocarbons from vehicle exhaust.
36 MATERIALS SCIENCE↗
Regulating the Pt 1 –CeO 2 interaction via alkali modification for boosting the catalytic performance of single-atom catalysts
K + modification helps in boosting the CO oxidation activity on Pt 1 /CeO 2 through tuning the coordination environment and oxidation states of Pt sites.
Chemistry↗
Constructing efficient CuO x -CeO 2 catalyst for NO reduction by CO: New insights into the structure–activity relationship
CuO-CeO 2 based materials have been recognized as promising substitutes for precious metal catalysts in emission control field due to their superior redox property and low cost. In this work, by optimizing the deposition process of CeO 2 and CuO onto γ-Al 2 O 3 , highly dispersed CuO clusters on unique CeO 2 -Al 2 O 3 support with small CeO 2 particles (7Cu-Ce/CeAl) were successfully constructed for efficient NO reduction by CO, which exhibited much higher NO removal efficiency and N 2 selectivity than CuO catalysts supported on γ-Al 2 O 3 (7Cu/Al) and conventional CeO 2 -Al 2 O 3 support (7Cu/CeAl). Moreover, H 2 O showed limited inhibition effect on the catalytic performance of 7Cu-Ce/CeAl catalyst. With the help of Raman spectra, X-ray absorption spectroscopy, in situ diffuse reflectance infrared Fourier transform spectroscopy, etc., it was clearly revealed that the abundant Cu + /Ce 3+ paired sites with surface synergetic oxygen vacancies (SSOV) on 7Cu-Ce/CeAl catalyst could effectively facilitate the adsorption and activation of CO and NO, thus significantly enhancing the NO removal efficiency.
36 MATERIALS SCIENCE↗
Transformation of Highly Stable Pt Single Sites on Defect Engineered Ceria into Robust Pt Clusters for Vehicle Emission Control
Engineering surface defects on metal oxide supports could help promote the dispersion of active sites and catalytic performance of supported catalysts. Herein, a strategy of ZrO 2 doping was proposed to create rich surface defects on CeO 2 (CZO) and, with these defects, to improve Pt dispersion and enhance its affinity as single sites to the CZO support (Pt/CZO). The strongly anchored Pt single sites on CZO support were initially not efficient for catalytic oxidation of CO/C 3 H 6 . However, after a simple activation by H 2 reduction, the catalytic oxidation performance over Pt/CZO catalyst was significantly boosted and better than Pt/CeO 2 . Pt/CZO catalyst also exhibited much higher thermal stability. The structural evolution of Pt active sites by H 2 treatment was systematically investigated on aged Pt/CZO and Pt/CeO 2 catalysts. With H 2 reduction, ionic Pt single sites were transformed into active Pt clusters. Much smaller Pt clusters were created on CZO (ca. 1.2 nm) than on CeO 2 (ca. 1.8 nm) due to stronger Pt-CeO 2 interaction on aged Pt/CZO. Consequently, more exposed active Pt sites were obtained on the smaller clusters surrounded by more oxygen defects and Ce 3+ species, which directly translated to the higher catalytic oxidation performance of activated Pt/CZO catalyst in vehicle emission control applications.
36 MATERIALS SCIENCE↗