In Situ Neutron Diffraction Study of the Influence of Microstructure on the Mechanical Response of Additively Manufactured 304L Stainless Steel

In situ neutron diffraction measurements were completed for this study during tensile and compressive deformation of stainless steel 304L additively manufactured (AM) using a high power directed energy deposition process. Traditionally produced wrought 304L material was also studied for comparison. The AM material exhibited roughly 200 MPa higher flow stress relative to the wrought material. Crystallite size, crystallographic texture, dislocation density, and lattice strains were all characterized to understand the differences in the macroscopic mechanical behavior. The AM material’s initial dislocation density was about 10 times that of the wrought material, and the flow strength of both materials obeyed the Taylor equation, indicating that the AM material’s increased yield strength was primarily due to greater dislocation density. Finally, a ~50 MPa flow strength tension/compression asymmetry was observed in the AM material, and several potential causes were examined.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Structure/property (constitutive and spallation response) of additively manufactured 316L stainless steel

For additive manufacturing (AM) of metallic materials, the certification and qualification paradigm needs to evolve as there is currently no broadly accepted “ASTM- or DIN-type” additive manufacturing certification process or AM-produced material specifications. Accordingly, design, manufacture, and subsequent implementation and insertion of AM materials to meet engineering applications requires detailed quantification of the constitutive (strength and damage) properties of these evolving materials, across the spectrum of metallic AM methods, in comparison/contrast to conventionally-manufactured metals and alloys. For this paper, cylindrical samples of 316L SS were produced using a LENS MR-7 laser additive manufacturing system from Optomec (Albuquerque, NM) equipped with a 1 kW Yb-fiber laser. The microstructure of the AM-316L SS was characterized in both the “as-built” AM state and following a heat-treatment designed to obtain full recrystallization to facilitate comparison with annealed wrought 316L SS. The constitutive behavior as a function of strain rate and temperature was characterized and is compared to that of annealed wrought 316L SS plate material. The dynamic shock-loading-induced damage evolution and failure response of all three 316L SS materials was quantified using flyer-plate impact driven spallation experiments at peak stresses of 4.7 and 6.5 GPa. The spall strength of AM-produced 316L SS and the recrystallized-AM-316L SS were found to decrease with increasing peak shock stress while the annealed wrought 316L SS spall strength remained essentially constant. Finally, the damage evolution, characterized using optical metallography and electron-backscatter diffraction (EBSD), was found to vary significantly across the three 316L SS microstructures while the three samples loaded to a peak shock stress of 6.5 GPa displayed only ~12% differences in spall strength.

316L SS↗
DOE OSTI2017

Deformation behavior of additively manufactured GP1 stainless steel

In-situ neutron diffraction measurements were performed in this paper during heat-treating and uniaxial loading of additively manufactured (AM) GP1 material. Although the measured chemical composition of the GP1 powder falls within the composition specifications of 17-4 PH steel, a fully martensitic alloy in the wrought condition, the crystal structure of the as-built GP1 material is fully austenitic. Chemical analysis of the as-built material shows high oxygen and nitrogen content, which then significantly decreased after heat-treating in a vacuum furnace at 650 °C for one hour. Significant austenite-to-martensite phase transformation is observed during compressive and tensile loading of the as-built and heat-treated material with accompanied strengthening as martensite volume fraction increases. During loading, the initial average phase stress state in the martensite is hydrostatic compression independent of the loading direction. Finally, preferred orientation transformation in austenite and applied load accommodation by variant selection in martensite are observed via measurements of the texture development.

36 MATERIALS SCIENCE↗
DOE OSTI2016

Characterization of an aluminum alloy hemispherical shell fabricated via direct metal laser melting

The ability of additive manufacturing to directly fabricate complex shapes provides characterization challenges for part qualification. The orientation of the microstructures produced by these processes will change relative to the surface normal of a complex part. In this work, the microscopy and x-ray tomography of an AlSi10Mg alloy hemispherical shell fabricated using powder bed metal additive manufacturing are used to illustrate some of these challenges. The shell was manufactured using an EOS M280 system in combination with EOS-specified powder and process parameters. The layer-by-layer process of building the shell with the powder bed additive manufacturing approach results in a position-dependent microstructure that continuously changes its orientation relative to the shell surface normal. X-ray tomography was utilized to examine the position-dependent size and distribution of porosity and surface roughness in the 98.6% dense part. Optical and electron microscopy were used to identify global and local position-dependent structures, grain morphologies, chemistry, and precipitate sizes and distributions. The rapid solidification processes within the fusion zone (FZ) after the laser transit results in a small dendrite size. Cell spacings taken from the structure in the middle of the FZ were used with published relationships to estimate a cooling rate of ~9 × 10 5 K/s. Uniformly-distributed, nanoscale Si precipitates were found within the primary α-Al grains. A thin, distinct boundary layer containing larger α-Al grains and extended regions of the nanocrystalline divorced eutectic material surrounds the FZ. Moreover, subtle differences in the composition between the latter layer and the interior of the FZ were noted with scanning transmission electron microscopy (STEM) spectral imaging.

36 MATERIALS SCIENCE↗
DOE OSTI2014

Extracting grain-orientation-dependent data from in situ time-of-flight neutron diffraction. I. Inverse pole figures

The problem of calculating the inverse pole figure (IPF) is analyzed from the perspective of the application of time-of flight neutron diffraction to in situ monitoring of the thermomechanical behavior of engineering materials. On the basis of a quasi-Monte Carlo (QMC) method, a consistent set of grain orientations is generated and used to compute the weighting factors for IPF normalization. The weighting factors are instrument dependent and were calculated for the engineering materials diffractometer VULCAN (Spallation Neutron Source, Oak Ridge National Laboratory). The QMC method is applied to face-centered cubic structures and can be easily extended to other crystallographic symmetries. Examples include 316LN stainless steel in situ loaded in tension at room temperature and an Al–2%Mg alloy, substantially deformed by cold rolling and in situ annealed up to 653 K.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗