Goal of sensor-development program to measure concentrations as low as few parts per billion in continuous monitoring as well as peak concentrations up to hundreds of parts per million, such as encountered near leaks. Sensors based on Raman scattering from hydrazine or monomethyl hydrazine adsorbed on roughened metal or metal oxide substrates. Similar systems developed to detect nitrogen oxides and other gases.
This program was directed toward the production of Echelle diffraction gratings by a light-driven, electrochemical etching technique (photoelectrochemical etching). Etching is carried out in single crystal materials, and the differential rate of etching of the different crystallographic planes used to define the groove profiles. Etching of V-groove profiles was first discovered by us during the first phase of this project, which was initially conceived as a general exploration of photoelectrochemical etching techniques for grating fabrication. This highly controllable V-groove etching process was considered to be of high significance for producing low pitch Echelles, and provided the basis for a more extensive Phase 2 investigation.
A photoelectrochemical approach is employed to fabricate exceptionally smooth low-pitch grating structures consisting of polished single crystals of (100) oriented n-GaAs in a sawtooth profile. The depth of the edged features is controlled by monitoring the total coulombs passed, and the rate of etching is precisely controlled by the light intensity, minimizing diffusional gradients in the liquid which may impair the uniformity. Symmetrical grooves spaced 10 microns apart will have a depth of 7.14 microns, and typically, 10-20 percent less total charge is required.
Photoelectrochemical etching was demonstrated as a means of fabricating a variety of periodic structures in semiconductors. The semiconductor is used as an electrode in an electrochemical cell, and is in contact with a liquid electrolyte. When the crystal is held at a positive voltage and illuminated, etching occurs in only the illuminated regions to a depth proportional to the illumination intensity and exposure time. In Phase 1, it was determined that diffraction gratings could be produced in gallium arsenide crystals by this method, using either a scanned focused laser beam or by uniform illumination of a ruling mask defined in metal or photoresist on the crystal surface. The latter approach was determined to produce V-grooves if the mask is oriented along certain crystallographic directions. These V-grooves were produced with an exceedingly smooth crystal morphology due to the highly controllable nature of the process and the mild electrolytes involved. The results form the basis for photoelectrochemical fabrication of deep, low pitch Eschelle gratings for use in high orders in NASA spectrographic instrumentation such as the Space Telescope Imaging Spectrograph.