NASA NTRS1973

Buckling behavior of composite cylinders subjected to compressive loading

Room temperature compressive buckling strengths of eight cylinders, four boron-epoxy and four boron-epoxy reinforced-titanium, with diameter to thickness ratios ranging between 40 and 67 are determined experimentally and compared with analytical predictions. Numerical buckling strengths are presented for Donnell's, Flugge's and Sanders' shell theories for anisotropic and orthotropic material cases. Comparison of analytical predictions with experimental results indicates good agreement and the recommended correlation factor suggested in the literature is applicable for design. For the cylinders tested, the correlation between experiment and theory ranged from 0.73 to 0.97.

Carri, R. L.↗

NASA NTRS1972

Compressive strength of titanium alloy skin-stringer panels selectively reinforced with boron-aluminum composite.

Description of a method of selectively reinforcing conventional titanium airframe structure with unidirectional boron-aluminum composite attached by brazing which has been successfully demonstrated based on compression tests of short skin-stringer panels. Improvements in structural performance exceeded 25% on an equivalent weight basis over the range from room temperature to 800 F, both in terms of initial buckling and maximum strengths. Room-temperature performance was not affected by prior exposure at 600 F for 1000 hours in air, or by 400 cycles between -65 and 600 F. The experimental results were generally predictable on the basis of existing analytical procedures. No evidence of failure was observed in the braze bond between the boron-aluminum composite and the titanium alloy.

Herring, H. W.↗

NASA NTRS1971

Compressive behavior of titanium alloy skin-stiffener specimens selectively reinforced with boron-aluminum composite

A method of selectively reinforcing a conventional titanium airframe structure with unidirectional boron-aluminum composite attached by brazing was successfully demonstrated in compression tests of short skin-stiffener specimens. In a comparison with all-titanium specimens, improvements in structural performance recorded for the composite-reinforced specimens exceeded 25 percent on an equivalent-weight basis over the range from room temperature to 700 K (800 F) in terms of both initial buckling and maximum strengths. Performance at room temperature was not affected by prior exposure at 588 K (600 F) for 1000 hours in air or by 400 thermal cycles between 219 K and 588 K (-65 F and 600 F). The experimental results were generally predictable from existing analytical procedures. No evidence of failure was observed in the braze between the boron-aluminum composite and the titanium alloy.

Herring, H. W.↗