Interference fits and stress-corrosion failure

It is pointed out that any proper design of interference fit fastener, interference fit bushings, or stress coining processes should consider both the stress-corrosion susceptibility and fatigue-life improvement together. Investigations leading to such a methodology are discussed. A service failure analysis of actual aircraft parts is considered along with the stress-corrosion susceptibility of cold-working interference fit bushings. The optimum design of the amount of interference is considered, giving attention to stress formulas and aspects of design methodology.

Hanagud, S.↗

NASA NTRS1975

Stress corrosion susceptibility of stress-coined fastener holes in aircraft structures

The cold working process of stress coining is used to provide fatigue improvement of fastener holes in aircraft structures. The cold working produces a radial flow of the metal. The residual stresses resulting from stress coining provide protection against fatigue damage by opposing the applied tensile stresses in service at the edge of the fastener hole. However, it is shown in this paper that in addition to the compressive stresses surrounding the stress coined hole, there are tensile stresses that result from the coining operation and that these residual tensile stresses can have a deleterious effect on the stress corrosion susceptibility of the postcoined structure.

Carter, A. E.↗