Evaluation of an Al-Cu-Zn-Mg Alloy for Wire-Fed Additive Manufacturing

A collaborative research study was conducted to evaluate an experimental Al-Cu-Zn-Mg alloy, designated Al C380H, developed by Arconic Corporation for wire-fed additive manufacturing (AM) techniques such as NASA’s electron beam freeform fabrication (EBF 3 ) process and the wire arc additive manufacturing (WAAM) process. The goal of the study was to determine, based upon metallurgical properties, whether additively manufactured Al C380H represented a viable alternative for applications currently using wrought 7xxx series aluminum. Al 2319 and Al 7075 were also deposited as AM-compatible and non-AM-compatible baselines, respectively. Evaluation was based on tensile, fracture, and corrosion properties. The strength and ductility of Al C380H-T6 materials produced by EBF3 and WAAM were sufficiently lower than typical values for Al 7050-T7 to indicate that additively manufactured Al C380H is not a viable replacement for current parts fabricated with Al 7050, due largely to the significant losses in Zn and Mg and development of porosity during deposition. EBF 3 parameters that reduced porosity, such as increasing electron beam current, higher raster frequency, sharper beam focus, and slower travel speed, augmented de-alloying of fugitive solute. Further enhancement of Zn and Mg content in Al C380H feedstock wire combined with adjustments to deposition conditions to minimize porosity may enable production of Al C380H parts by EBF 3 or WAAM that are viable replacements for current Al 7050 wrought products.

electron beam freeform fabrication (EBF3)↗
NASA NTRS2023

Hot Cracking Behavior and Beam-Induced Grain Refinement in Electron Beam Freeform Fabricated Al 7075

Electron beam freeform fabrication (EBF 3 ) is a high deposition rate, wire-based directed energy deposition (DED) additive manufacturing (AM) process used to print metallic parts in a vacuum environment. While high specific strength 7xxx-series Al alloys are of interest in the aerospace and automotive industries, these alloys suffer from hot cracking issues during fusion welding and AM. In this work, linear deposits of Al 7075 were fabricated with EBF 3 to study the effects of baseplate thickness, preheat temperature, and beam focus on hot cracking behavior. Solidification cracks were observed in the first deposition layer, and by the third layer coalesced into large “macrocracks” running vertically through the build height. Fine, intergranular liquation “microcracks” appeared between macrocracks below the root of the final deposit layer fusion zone. Increasing the substrate preheat temperature from 165°C to 320°C deepened the partially melted zone and resulted in a more than twofold increase in the liquation microcrack density. Analysis of Scheil solidification diagrams revealed that fugitive losses of Zn and Mg during deposition increased the susceptibility to solidification cracking and promoted substrate liquation cracking. Focused electron beam (EB) conditions combined with a high aspect ratio elliptical raster pattern resulted in bands of refined, equiaxed grains. The refined microstructure suppressed solidification macrocracking and caused a nearly fivefold reduction in liquation crack density, demonstrating that beam-induced grain refinement may be a promising low-cost method for reducing hot cracking during AM.

aluminum↗
NASA NTRS2022

Advanced Lightweight Metallic Fuselage Project Manufacturing Trade Study

Recent advances in large-scale flow forming of integrally stiffened cylinders (ISCs) have motivated evaluation of available technologies for rapid manufacturing of metallic fuselages. The current state-of-the-art in flow forming of ISCs produces 10-ft. diameter, 5-ft. long barrels with integral longitudinal blade stiffeners, and these single-piece ISCs are produced in approximately 1.5 hours. While other manufacturing processes are required to incorporate additional structural elements (ASE) such as circumferential ring frames, reinforcements around window and door cut-outs, and floors to the ISCs to complete the fuselage structure, flow forming technology may assist the aerospace industry in meeting manufacturing rate demands. In order to evaluate this technology, a fuselage manufacturing demonstration article (MDA) fabricated from two ISCs is scheduled for fabrication and delivery to NASA Langley Research Center (LaRC) by the end of 2022. In this study, eight manufacturing technologies were assessed to downselect candidate manufacturing processes for adding ASE to complete the MDA. A literature review and evaluation of contractor-produced panels covering a spectrum of welding and additive manufacturing (AM) processes were conducted at NASA LaRC. The analytical hierarchy process (AHP) was used to evaluate figures of merit (FOMs) for selecting manufacturing process(es) to integrate ASE with the ISCs to form a fuselage MDA. The AHP results revealed that scalability, structural performance, and distortion control were the most valued criteria for downselecting the manufacturing process to construct the internal stiffening structures. Based on the FOMs, this study concluded that a welding process is best suited for integrating the majority of the ASE, namely the circumferential ring frames. All of the welding processes received higher scores than AM processes due to higher maturity, higher structural performance, fewer post-processing requirements in machining and heat treating, and faster deposition rates. Among the welding processes, cold metal transfer (CMT) welding was ranked the most favorable process for assembling the MDA, with the other welding processes (laser welding (LW), friction stir welding (FSW), and refill friction stir spot welding (RFSSW)) scoring slightly lower. This was a consequence of the perceived maturity of the CMT welding process and its relatively high structural performance and low distortion resulting from the low heat input. Among the AM processes, CMT AM showed the greatest promise due to benefits derived from its scalability, lower 1st order process complexity, and low distortion. The AM processes may have potential for select applications, such as adding structural reinforcements around window and door cut-outs, but are not considered optimal for integrating the entire MDA.

Manufacturing↗
NASA NTRSDate not supplied

Al-Cu-Zn-Mg Alloy for Additive Manufacturing by Electron Beam Deposition

The application of fusion-based additive manufacturing (AM) to aircraft structural components is limited by the lack of high-strength aluminum alloys optimized for AM processing. High strength aluminum alloys (such as 7050-T7451) are difficult to process by AM because of their solidification cracking susceptibility and loss of volatile alloying elements such as Zn and Mg. The performance of a proprietary Al-Cu-Zn-Mg alloy wire feedstock was evaluated for AM utilizing electron beam deposition. Deposit microstructure, composition, occurrence of porosity and cracking, and post-heat treatment tensile and fracture toughness were correlated with deposition parameters. Post-heat treatment strength, ductility, and fracture toughness were lower than typical values for wrought 7050-T7451, related to significant losses of Zn and Mg and to porosity. Recommendations are offered for modifications to wire feedstock composition and adjustments to deposition conditions and heat treatment to enable AM of electron beam deposited material that has strength comparable to 7050-T7451 wrought products.

Al-Cu-Zn-Mg alloy, electron beam deposition, mecha↗
NASA NTRSDate not supplied

Alloy Evaluation and Flow Forming Process Modeling for Net Shape Aerospace Structures

Over the past decade, NASA Langley Research Center (LaRC) has led several manufacturing demonstration projects exploiting flow forming technology. The work has resulted in the commercial-scale manufacture of 10-ft. diameter single-piece, integrally stiffened cylinders. Near-net-shape flow forming offers simplified manufacturing schedules and cost savings through reduced part count. Reduction or elimination of machining, welding, and/or riveting can also lead to significant performance gains. NASA LaRC recently established a flow forming research facility to investigate new alloys and stiffener geometries for fuselage and launch vehicle cryotank applications. Candidate aluminum alloys and heat treatment combinations have been characterized through advanced mechanical testing and microscopy to maximize workability during flow forming trials. Elasto-plastic deformation simulations of the forming process have been performed using the finite element software DEFORM and correlated with forming trial results. The overall objective is to optimize structural performance through a combination of innovative materials, processes, and designs.

single-piece↗
NASA NTRSDate not supplied

Advances in Integrally Formed Metallic Structures

NASA Langley Research Center (LaRC) is applying flow forming technology to aerospace aluminum alloys for the manufacture of integrally stiffened cylinders that meet aircraft fuselage or launch vehicle specifications. High-strength 2xxx series alloys, in various temper/product form conditions, are being compared with medium-strength, very formable AA 6061 as the benchmark. Screening of candidate materials traditionally relies on empirical forming trials, but more recently on metrics derived from constant nominal strain rate tensile testing. In this work, the established hierarchy of formability metrics is adopted as the baseline; tensile area reduction, work hardening exponent, and modulus of resilience. The suite of metrics can be expanded based on phenomenological and mechanistic considerations of plastic flow instabilities to incorporate anisotropy ratio, rate of work hardening, and dynamic strain aging effects. Separate research thrusts at LaRC are aimed at formulating a protocol for scalable production of fully formed, defect-free components: 1) quantifying the extended set of formability metrics from constant and jump strain rate tensile tests with digital image correlation (DIC); 2) using statistically designed experiments on a vertical spin/flow forming facility (WF VUD-600®) to isolate the effect of convenient process variables, such as axial feed rate and thickness reduction; and 3) predicting the effect of feed ratio (roller translation relative to mandrel rotation speeds) on material response via process modeling using the DEFORM® simulation software. Current results will be discussed in terms of correlating intrinsic material properties with the bulk workability characteristics to successfully fabricate cylinders with complex cross-sections.

Aluminum↗
NASA NTRSDate not supplied

Influence of Feed Rate on Microstructure and Hardness of Conventionally Spun-formed Al 6061-O Plate

The effect of feed rate on the hardness and microstructure of a 7.35-mm-thick section from a spin-formed Al 6061 cylinder is investigated via microhardness mapping and electron backscatter diffraction (EBSD) analysis. The through-thickness hardness and microtexture profiles, corresponding to a true thickness strain of ≈ 0.3, are utilized to evaluate microstructural variations that could influence mechanical anisotropy and spin formability. The microhardness data reveal distinct gradients from the outer to the inner mold line that vary with feed rate and may be a function of the level of forming strain in the material. The microtextural mapping data expose a minor influence from feed rate, but contain trends through the material cross-section that suggest variations in the location-dependent stress states. The results demonstrate for the first time that the relationship between spin forming deformation and hardness or texture variations can be exploited to optimize processing parameters and mechanical response.

Spin forming↗
NASA NTRSDate not supplied

Utilizing Strain Rate Jump Testing to Predict Flow Formability of Al Alloys Sensitive to Portevin-Le Chatelier Instabilities

Predicting the flow formability of Al alloys is challenging due to the incremental deformation, complex loading path, and wide range of strain rates characteristic of the process. State-of-the-art research efforts have primarily focused on formability metrics derived from ambient temperature, constant strain rate uniaxial tensile testing. However, Al alloys in formable tempers tend to exhibit serrated Portevin-Le Chatelier (PLC) flow. The appearance of PLC instabilities implies a negative strain rate sensitivity, loss of tensile area reduction capacity, and decreased formability. Elevated temperature and interrupted strain rate tensile tests of relevant Al alloys were conducted to investigate the effects of rapid changes in strain rate (analogous to a forming increment by a passing roller) on common formability metrics. Emphasis was placed on the character/extent of PLC instabilities using digital image correlation strain measurements. The outcome of this work highlights the possibility of predicting flow formability using strain rate jump testing.

flow forming↗
NASA NTRSDate not supplied

Influence of Feed Rate on Microstructure and Hardness of Conventionally Spun-formed Al 6061-O Plate

The effect of feed rate on the mechanical properties and microstructure of a 7.35-mm-thick section from a spin-formed Al 6061 cylinder is investigated via microhardness mapping and electron backscatter diffraction (EBSD) analysis. The through-thickness hardness and microtexture profiles, corresponding to a true thickness strain of ≈ 0.3, are utilized to evaluate microstructural variations that could influence mechanical anisotropy and spin formability. The microhardness data reveal distinct gradients from the outer to the inner mold line that vary with feed rate and may be a function of the level of forming strain in the material. The microtextural mapping data expose a minor influence from feed rate, but contain trends through the material cross-section that suggest variations in the location-dependent stress states. The results demonstrate for the first time that the relationship between spin forming deformation and hardness or texture variations can be exploited to optimize processing parameters and mechanical response.

Spin forming↗