Mechanical Milling – Induced Microstructure Changes in Argyrodite LPSCl Solid-State Electrolyte Critically Affect Electrochemical Stability

Microstructure of argyrodite solid-state electrolyte (SSE) critically affects lithium metal electrodeposition/dissolution. While the stability of unmodified SSE is mediocre, once optimized state-of-the-art electrochemical performance is achieved (symmetric cells, full cells with NMC811) without secondary interlayers or functionalized current collectors. Planetary mechanical milling in wet media (m-xylene) is employed to alter commercial Li 6 PS 5 Cl (LPSCl) powder. Quantitative stereology demonstrates how milling progressively refines grain and pore size/distribution in the SSE compact, increases its density, and geometrically smoothens the SSE-Li interface. Mechanical indentation demonstrates that these changes lead to reduced site-to-site variation in the compact's hardness. Milled microstructures promote uniform early-stage electrodeposition on foil collectors and stabilize solid electrolyte interphase (SEI) reactivity. Analysis of half-cells with bilayer electrolytes demonstrates the importance of microstructure directly contacting current collector, with interface roughness due to pore and grain size distribution being key. For the first time, short-circuiting Li metal dendrite is directly identified, employing 1.5 mm diameter “mini” symmetrical cell and cryogenic focused ion beam (cryo-FIB) electron microscopy. The branching sheet-like dendrite traverses intergranularly, filling the interparticle voids and forming an SEI around it. Importantly, mesoscale modeling reveals the relationship between Li-SSE interface morphology and the onset of electrochemical instability, based on underlying reaction current distribution.

25 ENERGY STORAGE↗
DOE OSTI2023

Roles of Mn and Co in the Air Synthesizability of Layered Oxide Cathodes for Lithium-Based Batteries

High-nickel layered oxides (LiNi 1-x-y Mn x Co y O 2 ) are the prevailing cathode materials for high-energy-density lithium-based batteries, but they are plagued with deleterious surface air instabilities stemming from residual lithium formation. These issues severely hinder mass production as cathode calcination is limited to a flowing oxygen atmosphere, which entails high manufacturing costs as opposed to simpler and more economical air calcination. Here, while higher Ni contents are known to worsen air instabilities, the influence of Mn and Co contents on impacting these phenomena are less elucidated. We herein present the synthesis in ambient air and flowing oxygen atmospheres of three cathode variants with the same Ni contents, but varying Mn and Co contents: LiNi 0.7 Mn 0.3 O 2 , LiNi 0.7 Mn 0.15 Co 0.15 O 2 , and LiNi 0.7 Co 0.3 O 2 . It is found that the critical parameter influencing the air stability of the cathodes is the average Ni oxidation state, which is greatly dependent on the Mn and Co contents. Substitution of Mn for Ni drives down the Ni oxidation state as Mn exists as Mn4 + and reduces surface residual lithium formation, which vastly improves the overall air stability and, therefore, the synthesizability in air, but with a penalty of lowered capacity. In contrast, substitution of Co for Ni maintains Ni 3+ as Co exists as Co 3+ , offering increased initial capacity, but worsens the air stability and cyclability as the driving force for residual lithium formation and surface reactivity is increased.

25 ENERGY STORAGE↗
DOE OSTI2023

Tuned Reactivity at the Lithium Metal–Argyrodite Solid State Electrolyte Interphase

Thin intermetallic Li 2 Te–LiTe 3 bilayer (0.75 µm) derived from 2D tellurene stabilizes the solid electrolyte interphase (SEI) of lithium metal and argyrodite (LPSCl, Li 6 PS 5 Cl) solid-state electrolyte (SSE). Tellurene is loaded onto a standard battery separator and reacted with lithium through single-pass mechanical rolling or transferred directly to SSE surface by pressing. State-of-the-art electrochemical performance is achieved, e.g., symmetric cell stable for 300 cycles (1800 h) at 1 mA cm -2 and 3 mAh cm -2 (25% DOD, 60 µm foil). Cryo-stage focused ion beam (Cryo-FIB) sectioning and Raman mapping demonstrate that the Li 2 Te–LiTe 3 bilayer impedes SSE decomposition. The unmodified Li–LPSCl interphase is electrochemically unstable with a geometrically heterogeneous reduction decomposition reaction front that extends deep into the SSE. Decomposition drives voiding in Li metal due to its high flux to the reaction front, as well as voiding in the SSE due to the associated volume changes. Analysis of cycled SSE found no evidence for pristine (unreacted) lithium metal filaments/dendrites, implying failure driven by decomposition phases with sufficient electrical conductivity that span electrolyte thickness. In conclusion, DFT calculations clarify thermodynamic stability, interfacial adhesion, and electronic transport properties of interphases, while mesoscale modeling examines interrelations between reaction front heterogeneity (SEI heterogeneity), current distribution, and localized chemo-mechanical stresses.

25 ENERGY STORAGE↗