NiGa 2 O 4 interfacial layers in NiO/Ga 2 O 3 heterojunction diodes at high temperature
NiO/Ga 2 O 3 heterojunction diodes have attracted attention for high-power applications, but their high temperature performance and reliability remain underexplored. Here, we report the time evolution of the electrical properties in the widely studied p-NiO/n-Ga 2 O 3 heterojunction diodes and formation of NiGa 2 O 4 interfacial layers at high temperatures. Results of our thermal cycling experiment show an initial leakage current increase which stabilizes after sustained thermal load, due to reactions at the NiO–Ga 2 O 3 interface. High-resolution TEM microstructure analysis of the devices after thermal cycling indicates that the NiO–Ga 2 O 3 interface forms a ternary compound at high temperatures, and thermodynamic calculations suggest the formation of the spinel NiGa 2 O 4 layer between NiO and Ga 2 O 3 . First-principles defect calculations find that NiGa 2 O 4 shows low p-type intrinsic doping and hence can serve to limit electric field crowding at the interface. Vertical NiO/ Ga 2 O 3 diodes with intentionally grown 5 nm thin spinel-type NiGa 2 O 4 interfacial layers show an excellent device ON/OFF ratio of >10 10 (± 3 V), V ON of ~1.9 V, and increased breakdown voltage of ~1.2 kV for an initial unoptimized 300 lm diameter device. These p–n heterojunction diodes are promising for high-voltage, high temperature applications.