Engineering topics
Chapman, Karena W.
Publications and source records attributed to Chapman, Karena W..
3D Lead-Organoselenide-Halide Perovskites and their Mixed-Chalcogenide and Mixed-Halide Alloys
Here, we incorporate Se into the 3D halide perovskite framework using the zwitterionic ligand: SeCYS ( + NH 3 (CH 2 ) 2 Se - ), which occupies both the X - and A + sites in the prototypical ABX 3 perovskite. The new organoselenide-halide perovskites: (SeCYS)PbX 2 (X=Cl, Br) expand upon the recently discovered organosulfide-halide perovskites. Single-crystal X-ray diffraction and pair distribution function analysis reveal the average structures of the organoselenide-halide perovskites, whereas the local lead coordination environments and their distributions were probed through solid-state 77 Se and 207 Pb NMR, complemented by theoretical simulations. Density functional theory calculations illustrate that the band structures of (SeCYS)PbX 2 largely resemble those of their S analogs, with similar band dispersion patterns, yet with a considerable band gap decrease. Optical absorbance measurements indeed show band gaps of 2.07 and 1.86 eV for (SeCYS)PbX 2 with X=Cl and Br, respectively. We further demonstrate routes to alloying the halides (Cl, Br) and chalcogenides (S, Se) continuously tuning the band gap from 1.86 to 2.31 eV–straddling the ideal range for tandem solar cells or visible-light photocatalysis. The comprehensive description of the average and local structures, and how they can fine-tune the band gap and potential trap states, respectively, establishes the foundation for understanding this new perovskite family, which combines solid-state and organo-main-group chemistry.
A Titanium-Based Metal–Organic Framework For Tandem Metallaphotocatalysis
Metal–organic frameworks (MOFs) have garnered substantial attention for their unique properties, such as high porosity and tunable structures, making them versatile for various applications. This paper constructs photoactive titanium–organic frameworks by combining Ti(IV) clusters and a bipyridine linker. The MOF is synthesized in situ through imine condensation, resulting in NU-2300. Subsequent ex situ nickel salt complexation results in NU-2300-Ni, which is then used for light-mediated carbon–heteroatom cross-couplings. The photophysical properties of the metallaphotocatalyst were investigated by UV-vis and EPR analysis, and both the Ti cluster and the bipyridine linker were found to contribute to successful catalysis, making it a tandem catalyst. The heterogeneous material retained its performance through five cycles of thioetherification. As a result, this work contributes not only to MOF synthetic strategies, but also to expanding MOF applications as recyclable, tandem metallaphotocatalysts.
Node Distortions in UiO-66 Inform Negative Thermal Expansion Mechanisms: Kinetic Effects, Frustration, and Lattice Hysteresis
In metal–organic frameworks (MOFs) the interplay between the dynamics of individual components and how these are constrained by the extended lattice can yield unusual emergent phenomena. For the archetypal Zr-MOF, UiO-66, we explore the cooperative dynamics of a Zr-node transformation that gives rise to negative thermal expansion (NTE). Here, using in situ synchrotron X-ray scattering, with powder diffraction and pair distribution function (PDF) analyses, we identify lattice hysteresis and a thermal ramp-rate-dependence of the thermal expansion. Specifically, kinetic trapping of distorted node states formed at high temperature, leads to broad variability in the apparent thermal expansion which ranges from large positive to large negative thermal expansion with coefficients of thermal expansion (CTE) from +45 to –80 × 10 –6 K –1 . Time-resolved relaxation studies at selected temperatures suggest that when equilibrated UiO-66 is intrinsically NTE, with a CTE of –35 × 10 –6 K –1 . Kinetic trapping of the node-distorted state following high temperature activation has broad implications for characterization and applications of these Zr-MOFs; the nonequilibrium node state depends on the thermal history of the sample with quench vs slow cooling likely to impact gas binding, pore volume, and accessible catalytic sites.