DOE OSTI2021

Low-temperature sprayed SnO x nanocomposite films with enhanced hole blocking for efficient large area perovskite solar cells

Scalable fabrication of charge transport layers with high uniformity and compactness is essential for the commercialization of perovskite solar cells (PSCs). Cost-effective deposition of high-quality electron transport layers (ETLs) is a particularly important step to achieve low-cost, efficient and large-area PSCs. Here, an open-air (relative humidity of 40–50%) and low-temperature (≤100 °C) ultrasonic spray coating of tin oxide (SnO 2 ) nanocomposite films incorporating nanocrystalline SnO 2 nanoparticles in an amorphous SnO x matrix is demonstrated to fabricate large-area ETLs for planar PSCs. The optimized SnO 2 /SnO x nanocomposite exhibits significantly enhanced hole-blocking and high-power conversion efficiencies of 18% and 16% for planar PSCs with an active area of 0.2 cm 2 and 1 cm 2 , respectively. More importantly, the devices show little current–voltage hysteresis as well as good shelf-life stability by maintaining ~90% of the initial performance without encapsulation after 2500 hours storage under inert conditions. Additionally, high voltages of >6.0 V have been obtained for solar modules of 2.1 cm 2 aperture area comprising six sub-cells in series, suggesting that the low-temperature, open-air and fast spray coating is suitable and transferable to deposit large-area charge transport layers for scalable PSCs or other optoelectronic devices.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

DOE OSTI2021

Rapid Open-Air Processing of Low-Cost Perovskite Solar Modules

We report an industrially relevant approach to both scalable and fast open-air perovskite photovoltaic (PV) module production. This work resolves some of the most formidable barriers to module-level scaling that the perovskite community has been facing. Key advances include scalable large-area spray deposition, new monolithic integration scribing techniques, advanced photoluminescence characterization, and reproducible high-throughput manufacturability. Our rapid spray processing techniques enabled the highest perovskite PV efficiency produced in open-air. Innovations in scribing techniques enabled the first single-source laser process to achieve perovskite module monolithic integration and technoeconomic analysis led to a comprehensive cost model for perovskite module manufacturing. We report significant progress in reducing perovskite manufacturing costs necessary to potentially compete with incumbent Si-based PV for utility-scale power generation.

cost modeling↗

DOE OSTI2021

Perspectives of Open-Air Processing to Enable Perovskite Solar Cell Manufacturing

We report high throughput open-air processing techniques for the scalable production of all device and barrier layers for perovskite photovoltaics (PV). This work discusses and resolves some of the most formidable barriers to module-level scaling that the perovskite community has been facing. Our advanced technoeconomic manufacturing analysis indicates that vacuum-based processes with high capital expenditures (CapEx) and low throughputs dominate the cost of production. Open-air fabrication methods offer low CapEx routes to manufacturing, but achieving reproducibility in ambient conditions with varying relative humidity has been a persistent challenge. The use of rapid processing methods with plasma curing to convert films from the solution-state enables reproducibility, moisture immunity, and the highest perovskite PV efficiency produced in open-air. These methods are readily translatable to in-line processing where layers are sequentially deposited without the need for lengthy post-annealing steps that reduce throughput and involve additional equipment. Significant progress is demonstrated in reduced manufacturing costs as perovskites contend as a commercially viable next-generation thin film PV technology.

14 SOLAR ENERGY↗

DOE OSTI2020

Rapid Open-Air Fabrication of Perovskite Solar Modules

We report on the open-air fabrication of perovskite solar modules with key advances including scalable large-area spray deposition, new monolithic integration scribing techniques, advanced photoluminescence characterization, and reproducible high-throughput manufacturability. Perovskite deposition with linear speeds of 12 m/min without a post-anneal are demonstrated with improved device performance, luminescent yield and >10X carrier lifetimes. Manufacturability using monolithic integration of series-connected modules is accomplished with a new indirect fiber laser ablation scribing method. A stable cell and module power output of 18.0% and 15.5%, respectively, was achieved with a subcell V oc > 1.06V. A comprehensive supporting technoeconomic analysis details the entire in-line manufacturing process from the glass substrate to the junction box of the encapsulated module. Here, the module manufacturing cost, balance of system costs and levelized cost of energy for a range of module efficiencies and lifetimes provides insights for the necessary tool speeds, efficiencies, and lifetimes for utility-scale energy generation.

14 SOLAR ENERGY↗

DOE OSTI2020

Scalable open-air deposition of compact ETL TiO x on perovskite for fullerene-free solar cells

We report a scalable, low-temperature TiO x electron transport layer (ETL) produced directly on top of perovskite in an inverted architecture device by an open-air chemical vapor deposition (OA-CVD) process. The OA-CVD pyrolysis of a titanium ethoxide precursor forms a fully inorganic, conformal, and compact TiO x film. The resultant film is mechanically robust and exhibits a fracture toughness 30-fold higher than commonly used fullerene-based ETL films. The TiO x is an effective barrier layer against environmental degradation—unencapsulated devices with the TiO x ETL retain 60% of their initial efficiency after 1000 hours in ambient aging conditions—compared to devices with a fullerene ETL which were inoperable after 144 hours. Inverted architecture devices with an optimized TiO x ETL thickness of 70 nm exhibited high open-circuit voltages of 1.08 V. We comment on the photocatalytic properties of TiO x and the influence of an amorphous film on maximum power point stability.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗