DOE OSTI2014
Sodium ions of TNWs were exchanged with hydrogen ions, and this protocol was very suitable for capturing high density of cobalt ions. Meanwhile, the fabricated Co{sub 3}O{sub 4}/TNWs nano-material presented a highly catalytic and stable activity for dye degradation. - Highlights: • Co{sub 3}O{sub 4} nanoparticles were deposited on the pretreated TNWs surface. • The TNWs treated by hydrogen ions captures higher density of cobalt ions. • The Co{sub 3}O{sub 4}/TNWs catalyst possesses highly efficiency for dyes degradation with oxone. - Abstract: In this paper, we reported a recyclable and highly active porous catalyst of titanate nanowires (TNWs) coated with well-distributed Co{sub 3}O{sub 4} nanoparticles (NPs) (Co{sub 3}O{sub 4}/TNWs). Sodium ions of TNWs were exchanged with hydrogen ions in the dilute nitric acid, and this protocol was very suitable for capturing cobalt ions. X-ray diffraction (XRD) demonstrated the existence of Co{sub 3}O{sub 4} phase with unique lattice planes, such as (2 2 0), (3 1 1) and (5 1 1). Electron microscopes (FE-SEM and TEM) indicated that the Co{sub 3}O{sub 4} NPs with an average diameter of 22 ± 3 nm were coated uniformly on TNWs surface (average diameter: 37 ± 5.5 nm), and the Co{sub 3}O{sub 4} NPs mainly exposed their (2 2 0) and (2 2 2) active planes. XPS analysis confirms the formation of Co{sub 3}O{sub 4} phase by the presence of Co 2p peaks at 780.1 eV (2p 3/2) and 795.5 eV (2p 1/2). Methylene blue (MB) and other organic dyes (rhodamine B (RhB) and methyl orange (MO)) were chosen as target compounds for catalytic degradation under indoor scattering light. Compared to the original Co{sub 3}O{sub 4}/TNWs catalyst, the catalytic efficiency of nanoscaled catalyst with oxone for MB was about 15 times higher, and the MB solution (10 mg L{sup −1}) was completely degraded within 8 min. The catalytic activity of recycled catalyst used in the sixth run still remained very active, and the degradation time for MB was only 16 min. The nanosized catalyst also had a high activity for dyes of RhB (10 mg L{sup −1}) and MO (10 mg L{sup −1}), as the degradation efficiencies of RhB and MO after 10 min of contact time were about 90.2% and 92.6%, respectively.