Engineering topics
Chen, Xinyue
Publications and source records attributed to Chen, Xinyue.
Quadrupolar excitons and hybridized interlayer Mott insulator in a trilayer moiré superlattice
Transition metal dichalcogenide (TMDC) moiré superlattices, owing to the moiré flatbands and strong correlation, can host periodic electron crystals and fascinating correlated physics. The TMDC heterojunctions in the type-II alignment also enable long-lived interlayer excitons that are promising for correlated bosonic states, while the interaction is dictated by the asymmetry of the heterojunction. Here we demonstrate a new excitonic state, quadrupolar exciton, in a symmetric WSe 2 -WS 2 -WSe 2 trilayer moiré superlattice. The quadrupolar excitons exhibit a quadratic dependence on the electric field, distinctively different from the linear Stark shift of the dipolar excitons in heterobilayers. This quadrupolar exciton stems from the hybridization of WSe 2 valence moiré flatbands. The same mechanism also gives rise to an interlayer Mott insulator state, in which the two WSe 2 layers share one hole laterally confined in one moiré unit cell. In contrast, the hole occupation probability in each layer can be continuously tuned via an out-of-plane electric field, reaching 100% in the top or bottom WSe 2 under a large electric field, accompanying the transition from quadrupolar excitons to dipolar excitons. Our work demonstrates a trilayer moiré system as a new exciting playground for realizing novel correlated states and engineering quantum phase transitions.
Giant spontaneous polarization for enhanced ferroelectric properties of biaxially oriented poly(vinylidene fluoride) by mobile oriented amorphous fractions
Poly(vinylidene fluoride) (PVDF) and its random copolymers exhibit the most distinctive ferroelectric properties; however, their spontaneous polarization (60–105 mC m -2 ) is still inferior to those (>200 mC m -2 ) of the ceramic counterparts. In this work, we report an unprecedented spontaneous polarization ( P s = 140 mC m -2 ) for a highly poled biaxially oriented PVDF (BOPVDF) film, which contains a pure β crystalline phase. Given the crystallinity of ~0.52, the P s for the β phase ( P s,β ) is calculated to be 279 mC m -2 , if a simple two-phase model of semicrystalline polymers is assumed. This high P s,β is invalid, because the theoretical limit of P s,β is 185 mC m -2 , as calculated by density functional theory. To explain such a high P s for the poled BOPVDF, a third component in the amorphous phase must participate in the ferroelectric switching to contribute to the P s . Namely, an oriented amorphous fraction (OAF) links the lamellar crystal and the mobile amorphous fraction. From the hysteresis loop study, the OAF content was determined to be ~0.28, more than 50% of the amorphous phase. Because of the high polarizability of the OAFs, the dielectric constant of the poled BOPVDF reached nearly twice the value of conventional PVDF. Overall, the fundamental knowledge obtained from this study will provide a solid foundation for the future development of PVDF-based high performance electroactive polymers for wearable electronics and soft robotic applications.
Achieving Flat-on Primary Crystals by Nanoconfined Crystallization in High-Temperature Polycarbonate/Poly(vinylidene fluoride) Multilayer Films and Its Effect on Dielectric Insulation
To meet the stringent requirements of next-generation film capacitors for power electronics, multilayer films (MLFs) are fabricated with the advantage of achieving high temperature rating, high energy density, and reasonably low loss simultaneously. In this study, a high permittivity polar polymer, poly(vinylidene fluoride) (PVDF), is multilayered with a linear, low loss dielectric polymer such as high-temperature polycarbonate (HTPC). However, the dielectric loss of these MLFs was still high as compared with current state-of-the-art biaxially oriented polypropylene (BOPP) films. The goal of this work is to decrease the dielectric loss and enhance dielectric insulation by achieving flat-on primary PVDF crystals in MLFs via nanoconfined melt-recrystallization. Based on simultaneous small- and wide-angle X-ray scattering experiments, edge-on lamellar crystals were observed for all as-extruded MLFs, regardless of different PVDF layer thicknesses. However, after melting at 180 °C followed by recrystallization, flat-on primary crystals were successfully achieved when the PVDF layer thickness was below 39 nm. Above 78 nm for the PVDF layer, major edge-on primary crystals with minor flat-on secondary crystals were observed. Furthermore, from leakage current, breakdown, lifetime, and electric displacement-electric field loop studies, MLFs with the flat-on primary crystals exhibited reduced loss and enhanced dielectric insulation as compared to as-extruded MLFs and those with edge-on primary/flat-on secondary crystals. This was attributed to the effective blockage of charge carriers by the flat-on PVDF primary crystals and their reduced ferroelectric switching.
Reducing dielectric loss and enhancing electrical insulation for multilayer polymer films by nanoconfined ion transport under high poling electric fields
High temperature polar polymers have demonstrated potential for good thermal stability and high dielectric constant at the same time. However, polarization of contaminated impurity ions in polar polymers, even at the ppm level, can significantly increase the dielectric loss at high temperature and low frequencies. One effective strategy to mitigate this problem is to multilayer them with a high temperature nonpolar dielectric polymer to confine impurity ion transport at the nanometer scale. In this study, confined ion transport in high temperature polycarbonate (HTPC)/poly(vinylidene fluoride) (PVDF) multilayer films under high AC electric fields was studied using a direct analytical simulation method. Different from the ion transport under low fields, the ion diffusion model failed to describe the ion transport under high electric fields. An exponential ion distribution profile, which was observed for the DC poling situation, was employed to implement the direct analytical simulation. Confined impurity ion transport under high AC fields was quantitatively understood. As the AC field increased, the mobile ion concentration decreased whereas the diffusion coefficient increased. The decrease of mobile ion concentration was explained by the blockage of impurity ions by the HTPC layers. This knowledge helped in the determination of optimal conditions to polarize impurity ions from the PVDF layers into the HTPC layers. After cooling below the glass transition temperature of HTPC, polarized impurity ions were locked inside the HTPC layers. As a result, increased discharge efficiency and enhanced electrical insulation (i.e., increased dielectric breakdown strength) were achieved for the polarized multilayer films.