High-temperature, high-pressure hydrothermal synthesis, characterization, and structural relationships of mixed-alkali metals uranyl silicates
Three mixed-alkali metals uranyl silicates, Na{sub 3}K{sub 3}[(UO{sub 2}){sub 3}(Si{sub 2}O{sub 7}){sub 2}]·2H{sub 2}O (1), Na{sub 3}Rb{sub 3}[(UO{sub 2}){sub 3}(Si{sub 2}O{sub 7}){sub 2}] (2), and Na{sub 6}Rb{sub 4}[(UO{sub 2}){sub 4}Si{sub 12}O{sub 33}] (3), have been synthesized by high-temperature, high-pressure hydrothermal reactions at 550 °C and 1440 bar, and characterized by single-crystal X-ray diffraction, photoluminescence, and thermogravimetric analysis. Compound 1 and 2 are isostructural and contain layers of uranyl disilicate. The smaller cation, Na{sup +}, is located in the intralayer channels, whereas the larger cations, K{sup +} and Rb{sup +}, and water molecule are located in the interlayer region. The absence of lattice water in 2 can be understood according to the valence-matching principle. The structure is related to that of a previously reported mixed-valence uranium(V,VI) silicate. Compound 3 adopts a 3D framework structure and contains a unique unbranched dreier fourfold silicate chain with the structural formula {uB,4"1_∞}[{sup 3}Si{sub 12}O{sub 33}] formed of Q{sup 2}, Q{sup 3}, and Q{sup 4} Si. The connectivity of the Si atoms in the Si{sub 12}O{sub 33}{sup 18−} anion can be interpreted on the basis of Zintl–Klemm concept. Crystal data for compound 1: triclinic, P-1, a=5.7981(2) Å, b=7.5875(3) Å, c=12.8068(5) Å, α=103.593(2)°, β=102.879(2)°, γ=90.064(2)°, V=533.00(3) Å{sup 3}, Z=1, R1=0.0278; compound 2: triclinic, P-1, a=5.7993(3) Å, b=7.5745(3) Å, c=12.9369(6) Å, α=78.265(2)°, β=79.137(2)°, γ=89.936(2)°, V=546.02(4) Å{sup 3}, Z=1, R1=0.0287; compound 3: monoclinic, C2/m, a=23.748(1) Å, b=7.3301(3) Å, c=15.2556(7) Å, β=129.116(2)°, V=2060.4(2) Å{sup 3}, Z=2, R1=0.0304. - Graphical abstract: Three mixed-alkali metals uranyl silicates were synthesized under hydrothermal conditions at 550 °C and 1400 bar and structurally characterized by single-crystal X-ray diffraction. Two of them have a layer structure with the alkali metal cations within and between the layers. The third one adopts a 3D framework structure and contains a unique unbranched dreier fourfold silicate chain formed of Q{sup 2}, Q{sup 3}, and Q{sup 4} Si. - Highlights: • Three new mixed-alkali metals uranyl silicates were synthesized by high-T, high-P hydrothermal method and structurally. • Two compounds adopt a layer structure and the third one has a 3D framework structure. • The 3D framework structure contains a unique unbranched dreier fourfold silicate chain formed of Q{sup 2}, Q{sup 3}, and Q{sup 4} Si.