Chen, Youxing

Publications and source records attributed to Chen, Youxing.

8 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Heavy ion irradiation effects on CrFeMnNi and AlCrFeMnNi high entropy alloys

Co-free but Al-included medium/high entropy alloys (M/HEAs) have gained increasing interests due to their lower cost and the potential to tune the multi-phase microstructure. The irradiation response of two Co-free HEAs, face-centered cubic (FCC) CrFeMnNi with limited Cr enriched α' phase and body-centered cubic (BCC) AlCrFeMnNi with B2s phase and nanoprecipitates were explored. Ion irradiations using 5 MeV Fe 2+ ions were performed at 500°C to a peak fluence of 50 and/or 100 displacements per atom (dpa). In dual-phase AlCrFeMnNi, there was no significant radiation induced segregation or chemical intermixing at the coherent matrix (FeCrMn-rich)/second phase (AlNi-rich) boundaries. In CrFeMnNi, limited voids were only detected at the peak damage location of ~ 50 dpa. On the other hand, voids were widely distributed in AlCrFeMnNi: under 50 and 100 dpa irradiation conditions, voids were found with larger dimension and denser distribution in the FeCrMn-rich matrix, smaller and slightly lower density in an AlNi-rich second phase. In addition, the diameter of the FeCMn-rich nanoprecipitates didn't reveal any tendency of dissolution or growth. This is correlated with their superior structural stability against irradiation. Significant radiation-induced hardening (increases from 3.8 ± 0.2 GPa to 4.7 ± 0.6 GPa) was measured in CrFeMnNi, but only ~ 4% hardness increase (from 7.4 ± 0.8 GPa to 7.7 ± 0.4 GPa) was noted in AlCrFeMnNi. Finally, in addition to the radiation-induced defects, such as voids, dislocation loops and point defects, other factors, such as chemical short-range ordering may play an important role.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Deformation mechanisms in single crystal Ni-based concentrated solid solution alloys by nanoindentation

Nanoindentation is a critical technique to probe mechanical properties at the micrometer and sub-micrometer scales, accompanied by challenges from indentation size effect, pile-up/sink-in effect, and strain rate sensitivity. In this work, different nanoindentation techniques have been employed to explore Ni-based concentrated solid solution alloys (CSAs) with the addition of 3d transition metal elements including Co, Cr, Mn, and Fe, including unique single-crystal Ni, NiCo, NiFe, Ni 80 Cr 20 , and NiCoFeCr samples with (100) surfaces. A procedure of nanoindentation tests and data analysis/correction have been developed, and a data set of hardness, elastic modulus, strain rate sensitivity, and activation volume for Ni-based CSAs are provided, including the less explored binary alloys such as Ni 80 Cr 20 and Ni 80 Mn 20 . The results show that the type of alloying elements is more critical than the number of elements in strengthening: Co does not provide strengthening in NiCo, while Cr, Mn, and Fe are effective strengthening elements. Cr is the most effective among all the 3d transition metal elements. Furthermore, atomic-level lattice distortion is responsible for the strengthening and the role of stacking fault energy is insignificant in Ni-based CSAs at room temperature. In summary, nanoindentation shows increasing promise as a reliable and fast tool to provide comprehensive mechanical information for new alloy design and development.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-Throughput Nanoindentation Mapping of Additively Manufactured T91 Steel

Here, this work aims to adapt nanoindentation mapping combined with a k-means algorithm as a high-throughput technique to study the nano-scale spatial changes in mechanical properties for a heterogeneous material. This technique can also classify the individual data points based on their properties. Hundreds to thousands of indents were performed on additively manufactured T91 at room temperature, 300°C, 400°C, and 500°C across a square area with a side length of 120 μm to 400 μm. From this data, the hardness and reduced modulus at each point could be calculated and mapped. Using k-means clustering, we were able to arrange the data into three or four clusters corresponding roughly to the ferritic and martensitic phases as well as one or two intermediate clusters sampling both the phases. The hardness of these two phases appears to be quite stable as a function of temperature. Nanoindentation mapping and the k-means algorithm can therefore be used to rapidly assess the feasibility of heterogeneous materials under extreme conditions, such as nuclear reactor steels.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Epitaxial nanotwinned metals and alloys: synthesis-twin structure–property relations

Extensive studies have been performed to understand the structure–property relationship in nanotwinned (NT) metals, where the average twin thickness or twin spacing is less than 100 nm. NT metals may have high strength, ductility, good electrical conductivity and corrosion resistance and have promising applications in microelectronics, structural materials and coatings for gas and oil industry. Most prior studies focus on the computational and experimental investigations of NT metals with low stacking fault energy (SFE) and often in polycrystalline forms. In this highlight, we review recent findings on epitaxial growth of NT metals and alloys with low and high SFEs deposited on single crystal substrates, and focus primarily on advancing our comprehension towards tailoring the microstructures and properties of NT metals via extrinsic factors, including the synthesis technique, parametric control and growth template, and intrinsic factors, such as SFE and thermodynamic, kinetic alloying effects. The review intends to illuminate how to synthesize and design epitaxial NT structures to achieve desirable properties.

36 MATERIALS SCIENCE↗