Engineering topics
Cheng, Zhe
Publications and source records attributed to Cheng, Zhe.
Ionic Peltier effect in Li-ion electrolytes
The coupled transport of charge and heat provide fundamental insights into the microscopic thermodynamics and kinetics of materials. We describe a sensitive ac differential resistance bridge that enables measurements of the temperature difference on two sides of a coin cell with a resolution of better than 10 μK. We use this temperature difference metrology to determine the ionic Peltier coefficients of symmetric Li-ion electrochemical cells as a function of Li salt concentration, solvent composition, electrode material, and temperature. The Peltier coefficients Π are negative, i.e., heat flows in the direction opposite to the drift of Li ions in the applied electric field, large, –Π > 30 kJ mol –1 , and increase with increasing temperature at T > 300 K. The Peltier coefficient is approximately constant on time scales that span the characteristic time for mass diffusion across the thickness of the electrolyte, suggesting that heat of transport plays a minor role in comparison to the changes in partial molar entropy of Li at the interface between the electrode and electrolyte. Here, our work demonstrates a new platform for studying the non-equilibrium thermodynamics of electrochemical cells and provides a window into the transport properties of electrochemical materials through measurements of temperature differences and heat currents that complement traditional measurements of voltages and charge currents.
Effects of processing conditions on flash sintering of commercial ZrN
Flash sintering (FS) is a potentially rapid and low-cost manufacturing technique for advanced ceramics. There are still many unknowns about ceramic FS, especially for highly conductive high-temperature ceramics (HTC), which often display decreased bulk conductivity with increasing temperature. This study qualitatively characterizes the flash behavior of highly conductive HTC materials using zirconium nitride (ZrN) as an example. The effects of processing parameters (e.g., DC voltage/electrical field strength, voltage ramp rate, post-flash holding time, mechanical pressure, sample milling, and choice of electrode materials) on ZrN flash behavior are also qualitatively studied and linked to samples microstructure and hardness. It is observed that best densification was achieved using 5 min Spex-milled ZrN powder under 25 MPa of applied pressure and constant 8 V DC. The potential mechanism for ZrN FS and the similarity and difference from FS of conventional oxides like YSZ have been proposed based on experimental observations, and the directions for future research are also pointed out.
Reactive flash sintering of TiZrN and TiAlN ternary metal nitrides
Here, this study demonstrated the reactive flash sintering (RFS) for two powder mixtures: TiN-ZrN (both conducting) and AlN-TiN (TiN conducting but AlN insulating), targeting ternary metal nitrides (TMN) of Ti 0.5 Zr 0.5 N and Ti 0.5 Al 0.5 N, respectively. A constant volage and pressure (e.g., 8 V DC, ∼15 MPa) at room temperature triggered the flash (current density up to 27 A/mm 2 ) without pre-heating, and the entire RFS process finished in a few minutes. For TiZrN, the flash was instantaneous whereas for TiAlN, there was a long incubation before the flash followed by a quick and dramatic flash. Both conventional ex situ XRD and in situ synchrotron study had been carried out. They showed a uniform Ti 0.57 Zr 0.43 N solution formed in RFS and persisted upon cooling, while (Ti, Al) N solid solution formed at high temperature was not stable and likely went through a very quick phase separation in the cooling process. The final products from RFS had been characterized using SEM/EDS for microstructure. Both TiZrN and TiAlN were dense. Distribution of Ti, Zr, and N was uniform for TiZrN; for TiAlN, Ti and N distribution was uniform, while association of Al with oxygen was observed. TGA-DSC revealed the onset oxidation temperature for TiZrN was comparable to TiN and ZrN, while it was higher by ∼200 °C for TiAlN, likely due to the formation of Al 2 O 3 . In terms of mechanical properties such as hardness or fracture toughness, forming a single-phase solid solution (like TiZrN) does not offer obvious benefits. while large grain size from RFS seemed to be unfavorable. Future optimization of RFS condition and in-depth study by both experiments and simulation are needed to fully understand the composition-processing-structure-property relationships for such TMN from the reactive flash sintering process.