3 records

NASA NTRS1993

Hot Deformation Of Si(3)N(4) Doped With Sc(2)O(3)

Report describes preparation, microstructural properties, and high-temperature deformation behavior of Si(3)N(4) doped with Sc(2)O(3). Powders of Si(3)N(4) with small additions of Sc(2)O(3) sintered under nitrogen overpressures to full density; expensive hot pressing or hot isostatic pressing not necessary to attain full density. Test of bars indicate high strengths at high temperatures and excellent time-dependent strength properties. Useful for fabrication of hot-section components of automotive gas-turbine engines.

Cheong, Deock-Soo↗

NASA NTRS1992

High-temperature deformation and microstructural analysis for silicon nitride-scandium(III) oxide

It was indicated that Si3N4 doped with Sc2O3 may exhibit high temperature mechanical properties superior to Si3N4 systems with various other oxide sintered additives. High temperature deformation of samples was studied by characterizing the microstructures before and after deformation. It was found that elements of the additive, such as Sc and O, exist in small amounts at very thin grain boundary layers and most of them stay in secondary phases at tripple and multiple grain boundary junctions. These secondary phases are devitrified as crystalline Sc2Si2O7. Deformation of the samples was dominated by cavitational processes rather than movements of dislocations. Thus the excellent deformation resistance of the samples at high temperature can be attributed to the very small thickness of the grain boundary layers and the crystalline secondary phase.

Cheong, Deock-Soo↗

NASA NTRS1990

High-temperature deformation and microstructural analysis for Si3N4-Sc2O3

It was indicated that Si3N4 doped with Sc2O3 may exhibit high temperature mechanical properties superior to Si3N4 systems with various other oxide sintered additives. High temperature deformation of samples was studied by characterizing the microstructures before and after deformation. It was found that elements of the additive, such as Sc and O, exist in small amounts at very thin grain boundary layers and most of them stay in secondary phases at triple and multiple grain boundary junctions. These secondary phases are devitrified as crystalline Sc2Si2O7. Deformation of the samples was dominated by cavitational processes rather than movements of dislocations. Thus the excellent deformation resistance of the samples at high temperature can be attributed to the very small thickness of the grain boundary layers and the crystalline secondary phase.

Cheong, Deock-Soo↗