NASA NTRS2024

Characterization of Low-Velocity Impact Damage in Toughened Non-Crimp Fabric Laminates

The damage response of resin-infused composites was investigated using quasi-static indentation (QSI) and instrumented drop-weight impact testing. The test specimens were composed of six layers of non-crimp fabrics where each layer contained +45°, 90°, −45°, and 0° plies. The goals of the testing were to identify damage responses that may differ from traditional thermoset materials and provide damage characterization data to evaluate current damage prediction analyses and aid improvements to current damage models. The damage was characterized using X-ray computed tomography (CT) and ultrasonic testing (UT). Incremental QSI loading was used on a single specimen to investigate damage growth in nine steps at progressively higher loads. Realtime acoustic emission data were used to determine the unloading points. Unlike typical thermoset composites, the force-displacement was smooth and showed no obvious indications of damage. The primary damage consisted of large lines of fiber fracture on the plies near the impact surface and delaminations through the thickness. Nine specimens were impacted at nominal impact energies of 25 ft-lbs, 30 ft-lbs, and 35 ft-lbs. The force histories at each energy followed nearly identical paths. Again, no obvious signs of damage were observed in any of the force histories. The general damage response in the dynamic tests was similar to the QSI-loaded specimens. However, repeat specimens impacted with a given impact energy showed variations in the damage. Some characteristics of the damage response were different than those typically observed in thermoset composites and will need to be evaluated using current analysis methods.

Composite Materials↗
NASA NTRS2023

Characterization of Low-Velocity Impact Damage in Thermoplastic Laminated Composites

The impact damage response of two thermoplastic material systems were compared over a range of impact energies. Eight-inch-square impact specimens with a 24-ply quasi-isotropic layup were manufactured from TC1225 LMPAEK T700G from Toray Industries and APC AS4D/PEKK-FC from Solvay. The effect of the degree of crystallinity (DOC) on the damage response was also investigated using a third set of specimens from the Toray material manufactured with reduced crystallinity. Using a combination of data obtained from X-ray computed tomography (CT) scans and ultrasonic testing (UT), detailed damage maps were created for every interface and ply for selected specimens. Using these damage maps, the delamination size, shape, and area were evaluated at each interface. The presence of fractured fibers was also identified on each ply. The LMPAEK material was found to have fewer and smaller delaminations than the PEKK specimens for impacts at the same energy. However, the LMPAEK specimens contained a larger number of fiber breaks. A similar trend was observed when comparing the baseline LMPAEK specimens with the low-crystallinity LMPAEK specimens. The low-crystallinity specimens had very little delamination but had a large number of plies with fiber breaks. In addition, the LMPAEK specimens often contained lines of fiber fractures in near-surface plies emanating from the contact region that were not present in the PEKK specimens.

Composite Materials↗
NASA NTRS2023

Characterization of Low-Velocity Impact Damage in Thermoplastic Laminated Composites

The impact damage response of two thermoplastic material systems were compared over a range of impact energies. Eight-inch-square impact specimens with a 24-ply quasi-isotropic layup were manufactured from TC1225 LMPAEK T700G from Toray Industries and APC AS4D/PEKK-FC from Solvay. The effect of the degree of crystallinity (DOC) on the damage response was also investigated using a third set of specimens from the Toray material manufactured with reduced crystallinity. Using a combination of data obtained from X-ray computed tomography (CT) scans and ultrasonic testing (UT), detailed damage maps were created for every interface and ply for selected specimens. Using these damage maps, the delamination size, shape, and area were evaluated at each interface. The presence of fractured fibers was also identified on each ply. The LMPAEK material was found to have fewer and smaller delaminations than the PEKK specimens for impacts at the same energy. However, the LMPAEK specimens contained a larger number of fiber breaks. A similar trend was observed when comparing the baseline LMPAEK specimens with the low-crystallinity LMPAEK specimens. The low-crystallinity specimens had very little delamination but had a large number of plies with fiber breaks. In addition, the LMPAEK specimens often contained lines of fiber fractures in near-surface plies emanating from the contact region that were not present in the PEKK specimens.

Composite Materials↗
NASA NTRSDate not supplied

Effect of Composite Stiffened Panel Design on Skin-Stringer Separation in Postbuckling

To design aeronautical composite multi-stringer panels that can safely operate in a postbuckled state, it is important to identify the parameters that can influence the different modes in which skin-stringer separation might occur. A methodology is under development to study the interaction between the skin-stringer separation and the postbuckling deformation. A simple criterion that can predict the initiation of skin-stringer separation is developed using the building block approach and single-stringer specimens. The criterion identifies whetherthe initiation is mainly due to bending or twisting deformations, so that these two possible modes can be studied separately. This procedure has the potential to reduce the overall development cost and allows the investigation of the design parameters that might precipitate or delay the skin-stringer separation.

Lucas J. Kootte↗
NASA NTRSDate not supplied

Critical Progressive Damage Analysis Model Features for Low-Velocity Impact on Thermoset and Thermoplastic Panels

A previous verification and validation framework evaluated the ability of various progressive damage analysis (PDA) tools to predict the mechanical response and damage state in post-buckled stiffened aerospace structures composed of fiber-reinforced thermoset composite materials. Herein, the ability of PDA tools to predict damage in thermoplastic composite materials subject to low-velocity impact (LVI) loading has been assessed. LVI tests and analyses have been conducted for similar panels, comprising thermoset or thermoplastic composite materials. Preliminary test/analysis correlations revealed that using the same combination of PDA model features and finite element model-building guidelines for the thermoset and thermoplastic LVI specimens resulted in underprediction of matrix crack lengths and delaminated area in the thermoplastic analyses despite yielding good correlations for the thermoset specimens. In this paper, the quality of the test/analysis correlations for analyses of thermoplastic LVI specimens performed with different combinations of PDA model features using the NASA CompDam material model are presented. Model features that were assessed in terms of effect on the quality of the test/analysis correlation include the representation of damageable interfaces, residual thermal stresses, and fiber damage.

Frank Leone↗
NASA NTRSDate not supplied

Interlaminar R-Curve Effects in Thermoplastic Composites: Experiments and Model Correlations

The interlaminar fracture behavior of thermoplastic composites under Mode-I and Mode-II static loading is investigated in this research. The material system under consideration is a carbon fiber reinforced low melt semi-crystalline resin TC1225 LMPAEK T700G (T700/LMPAEK)†. Characterization experiments were conducted to measure the load-displacement response, peak load, and propagation of delamination from a pre-implanted Kapton® insert. The Mode-I response was characterized using a double cantilever beam (DCB) test according to the ASTM D5528-22 standard. It was observed that the propagation exhibited significant resistance to delamination growth, i.e., an R-Curve effect. The test data indicated that the steady-state fracture toughness, G SS I , was approximately twice the mean initiation fracture toughness, G Ic . The Mode-II response of an end notch flexure (ENF) specimen tested according to the ASTM D7905-19 standard exhibited an unexpected stable behavior upon attaining peak load. Prior to attaining peak load, the Mode-II response exhibited some non-linearity, which may be attributed to nonlinear bulk material response, e.g., hyper-elasticity, viscoelasticity, plasticity, etc., and potentially friction at the load/support rollers and R-Curve effects. Finite element models based on the Cohesive Zone Method (CZM) and the Virtual Crack Closure Technique (VCCT) were used to predict the DCB and ENF specimen responses. DCB analysis results obtained using G SS I predicted propagation consistent with experimental data. However, results obtained with the as characterized G Ic were inaccurate in predicting delamination growth onset and peak load. ENF analysis results obtained with the as-characterized Mode-II fracture toughness, G IIc , were inaccurate in predicting the peak load and propagation. Hence, R-Curve effects were included in both DCB and ENF simulations, which enabled improved predictions. The experimentally determined Mode-I R-Curve was used for the DCB simulations, whereas an R-Curve was derived for Mode-II assuming that the change in compliance of the specimen was associated with crack growth only.

Prabhakar Rao↗
NASA NTRSDate not supplied

Critical Progressive Damage Analysis Model Features for Low-Velocity Impact on Thermoset and Thermoplastic Panels

A previous verification and validation framework evaluated the ability of various progressive damage analysis (PDA) tools to predict the mechanical response and damage state in post-buckled stiffened aerospace structures composed of fiber-reinforced thermoset composite materials. Herein, the ability of PDA tools to predict damage in thermoplastic composite materials subject to low-velocity impact (LVI) loading has been assessed. LVI tests and analyses have been conducted for similar panels, comprising thermoset or thermoplastic composite materials. Preliminary test/analysis correlations revealed that using the same combination of PDA model features and finite element model-building guidelines for the thermoset and thermoplastic LVI specimens resulted in underprediction of matrix crack lengths and delaminated area in the thermoplastic analyses despite yielding good correlations for the thermoset specimens. In this paper, the quality of the test/analysis correlations for analyses of thermoplastic LVI specimens performed with different combinations of PDA model features using the NASA CompDam material model are presented. Model features that were assessed in terms of effect on the quality of the test/analysis correlation include the representation of damageable interfaces, residual thermal stresses, and fiber damage.

Frank Leone↗
NASA NTRSDate not supplied

Low-Velocity Impact Analyses of Composite Panels Using Cohesive Zone Modeling and Continuum Damage Mechanics

A parametric study was conducted to gage the sensitivity of simulations of low-velocity impacts on laminated composite panels to various finite element model and material model features. The material model used in this parametric study was previously verified and validated for conducting progressive damage analyses of post-buckled composite structures subjected to quasi-static loading conditions. Based on the results of this parametric study, updates have been made to a progressive damage analysis material model and the best practices for its application. Experimental results are compared to computational results obtained with and without the updates to the models. Both thermoset and thermoplastic fiber-reinforced materials are considered. The resulting enhancements to the material model are presented in detail.

Frank Leone↗
NASA NTRSDate not supplied

Characterization of Low-Velocity Impact Damage in Toughened Non-Crimp Fabric Laminates

The damage response of resin-infused composites was investigated using quasi-static indentation (QSI) and instrumented drop-weight impact testing. The test specimens were composed of six layers of non-crimp fabrics where each layer contained +45°, 90°, −45°, and 0° plies. The goals of the testing were to identify damage responses that may differ from traditional thermoset materials and provide damage characterization data to evaluate current damage prediction analyses and aid improvements to current damage models. The damage was characterized using X-ray computed tomography (CT) and ultrasonic testing (UT). Incremental QSI loading was used on a single specimen to investigate damage growth in nine steps at progressively higher loads. Realtime acoustic emission data were used to determine the unloading points. Unlike typical thermoset composites, the force-displacement was smooth and showed no obvious indications of damage. The primary damage consisted of large lines of fiber fracture on the plies near the impact surface and delaminations through the thickness. Nine specimens were impacted at nominal impact energies of 25 ft-lbs, 30 ft-lbs, and 35 ft-lbs. The force histories at each energy followed nearly identical paths. Again, no obvious signs of damage were observed in any of the force histories. The general damage response in the dynamic tests was similar to the QSI-loaded specimens. However, repeat specimens impacted with a given impact energy showed variations in the damage. Some characteristics of the damage response were different than those typically observed in thermoset composites and will need to be evaluated using current analysis methods.

Composite Materials↗