Microstructure and Temperature Dependent Indentation Response of Additively Manufactured Precipitation-Strengthened Al 0.3 Ti 0.2 Co 0.7 CrFeNi 1.7 High Entropy Alloy
The temperature-dependent [from room temperature (RT) to 500°C] nanoindentation behavior of a precipitation-strengthened Al 0.3 Ti 0.2 Co 0.7 CrFeNi 1.7 high-entropy alloy (HEA) processed via two different additive manufacturing (AM) techniques was investigated in the as-deposited and annealed conditions. The hierarchically heterogeneous microstructures were achieved via simple one-step annealing treatments, exploiting the residual stresses in the AM-processed HEA to partially recrystallize the microstructure, performed remarkably better than the nearly homogeneous microstructures in the as-deposited state. Further, the one-step annealed conditions revealed < 6.6% reduction in hardness values at 500°C compared to RT, while the as-deposited conditions showed a > 18% reduction in the hardness. The one-step annealed conditions also exhibited significantly higher hardness than the as-deposited conditions owing to their L1 2 -strengthened FCC microstructures. Furthermore, serrated yielding or the Portevin-Le Chatlier effect indicative of microstructural instability was observed during nanoindentation deformation (at 500°C) for the as-deposited conditions but not for the one-step annealed conditions. This, therefore, signifies the robustness of the hierarchically heterogeneous microstructures at elevated temperatures presenting a strong avenue for tuning the HEAs for future nuclear reactor applications.