NASA NTRS1973

Hot hardness characteristics of ausformed AISI M-50, Matrix 2, WD-65, modified AISI 440-C, and Super Nitralloy

Short-term hot hardness studies were performed with ausformed AISI M-50, Matrix 2, WD-65, modified AISI 440-C (14-4-1) and case hardened Super Nitralloy. Hardness levels of each material were measured at elevated temperatures in an electric furnace with a low oxygen environment. Test temperatures ranged from 294 to 877 K. The hot hardness characteristics of the ausformed AISI-M-50, Matrix 2 WD-65, and modified AISI 440-C were the same as those determined for high-speed tool steels. Hot hardness for these steels can be predicted within one point Rockwell C. The hot hardness characteristics of both the case and core of Super Nitralloy were superior to AISI 52100 but inferior to the high-speed tool steels. The short-term Rockwell C hardness at temperature for the Super Nitralloy material between 294 and 769 K can be predicted within one point Rockwell C hardness.

Chevalier, J. L.↗

NASA NTRS1973

Pitting fatigue characteristics of AISI M-50 and super nitralloy spur gears

Two groups of 3.50-in. pitch-diameter spur gears, without tip relief, made from consumable-electrode vacuum-melted (CVM) AISI M-50 steel and CVM super nitralloy (5Ni-2A1) were tested under conditions which produced fatigue pitting. The M-50 gears had fatigue lives approximately 50 percent longer than the super nitralloy gears. Both groups of gears failed by classical rolling-element fatigue at the pitch circle. When the gears were overrun past initial spall formation, the spalled M-50 gear teeth failed by fatigue fracture. The M-50 material had higher wear than the super nitralloy material. Differences in fatigue life and wear were not considered statistically significant.

Townsend, D. P.↗

NASA NTRS1973

Carbide factor predicts rolling-element bearing fatigue life

Analysis was made to determine correlation between number and size of carbide particles and rolling-element fatigue. Correlation was established, and carbide factor was derived that can be used to predict fatigue life more effectively than such variables as heat treatment, chemical composition, and hardening mechanism.

Chevalier, J. L.↗

NASA NTRS1972

A new criterion for predicting rolling-element fatigue lives of through-hardened steels.

A carbide factor was derived based upon a statistical analysis which related rolling-element fatigue life to the total number of residual carbide particles per unit area, median residual carbide size, and percent residual carbide area. An equation was empirically determined which predicts material hardness as a function of temperature. The limiting temperatures of all of the materials studied were dependent on initial room temperature hardness and tempering temperature. An equation was derived combining the effects of material hardness, carbide factor, and bearing temperature to predict rolling-element bearing life.

Chevalier, J. L.↗

NASA NTRS1972

Study of hot hardness characteristics of tool steels

Hardness measurements of tool steel materials in electric furnace at elevated temperatures and low oxygen environment are discussed. Development of equation to predict short term hardness as function of intial room temperature hardness of steel is reported. Types of steel involved in the process are identified.

Chevalier, J. L.↗

NASA NTRS1972

Effect of carbide size, area, density on rolling-element fatigue

A carbide parameter that can be used to predict rolling element fatigue life was developed.The parameter is based on a statistical life analysis and incorporates the total number of particles per unit area, particle size, and percent carbide area. These were determined from quantimet image analyzing computer examinations of random samples selected from eight lots of material previously tested in rolling fatigue. The carbide parameter is independent of chemical composition, heat treatment, and hardening mechanism of the materials investigated.

Chevalier, J. L.↗

NASA NTRS1972

Short-term hot hardness characteristics of rolling-element steels

Short-term hot hardness studies were performed with five vacuum-melted steels at temperatures from 294 to 887 K (70 to 1140 F). Based upon a minimum Rockwell C hardness of 58, the temperature limitation on all materials studied was dependent on the initial room temperature hardness and the tempering temperature of each material. For the same room temperature hardness, the short-term hot hardness characteristics were identical and independent of material composition. An equation was developed to predict the short-term hardness at temperature as a function of initial room temperature hardness for AISI 52100, as well as the high-speed tool steels.

Chevalier, J. L.↗

NASA NTRS1972

A new criterion for predicting rolling-element fatigue lives of through-hardened steels

A carbide factor was derived based upon a statistical analysis which related rolling-element fatigue life to the total number of residual carbide particles per unit area, median residual carbide size, and percent residual carbide area. An equation was experimentally determined which predicts material hardness as a function of temperature. The limiting temperatures of all of the materials studied were dependent on initial room temperature hardness and tempering temperature. An equation was derived combining the effects of material hardness, carbide factor, and bearing temperature to predict rolling-element bearing life.

Chevalier, J. L.↗