DOE OSTI2022

Aluminization Coatings and Glass Seals for High Temperature Systems - CRADA 536 (Final Report)

The objective of this project was to demonstrate the suitability of PNNL’s Reactive Air Aluminization (RAA) coatings (US Patent Numbers 10,577,694, 10,378,094, and 9,481,923) for use in high-temperature systems. In particular, PNNL and Utility Global undertook a collaborative effort to explore the applicability of these coatings in Utility Global’s high-temperature hydrogen reactors where they would be used to prepare the sealing surfaces of the reactor technology. Utility Global instructed PNNL regarding their needs relating to further development of glass seal technologies suitable for use in their systems. This effort entailed alkaline earth-based silicate glass development and characterization; evaluation and characterization of reliability and compatibility of the coatings with glass seals, working environments, and substrates; performance demonstrations of representative cells and intermediate cells sealed using the glass seals and/or coatings of interest; and incorporation of the aluminization coatings and glass seals into Utility Global reactors for testing.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Lanthanum Strontium Cobaltite-Alumina Fiber Composite Contact Material for Solid Oxide Fuel Cells

Short alumina fibers were added to LSCo contact material to enhance the contact strength and improve thermal cycle stability. Alumina fiber from 2.5 v% to 20 v% were mixed with LSCo and sintered at elevated temperatures. Sintering study showed retardation in densification of LSCo matrix with increasing alumina content. Sintered bulk strength exhibited similar behavior where strength greatly reduced at high alumina v%. Coefficient of thermal expansion showed consistent results with prediction from rule of mixture. Contact strength using anode supported YSZ bilayer coupons improved greatly with the presence of small amount (2.5-5 v%) alumina fibers and no substantial reduction after 10 deep thermal cycles. Candidate LSCo-Al2O3 contact materials was validated in a generic stack test fixture for 1000h at 800oC followed by 10 thermal cycles. Results of impedance analysis showed substantial improvement in thermal cycle stability as compared to LSCo parent materials.

SOFC cathode, strength, LSCo, alumina↗

DOE OSTI2021

Electrically Conductive and Protective Coating Compatibility with LSCF Cathodes

Ferritic stainless-steel interconnect materials are used in intermediate or high-temperature SOFCs because of their oxidation resistance, high formability, and low cost. Their corrosion resistance is due to the formation of a protective chromium oxide scale during operation. However, the protective oxide layer produces Cr-containing volatile species at SOFC operating temperatures and conditions, which can cause cathode poisoning. Spinel coatings have been developed to prevent cathode poisoning while maintaining an electrically conductive pathway through SOFC stacks. Generally, Mn-Co-O spinel has been the material of choice, but PNNL has developed an Mn-Cu-O spinel protective coating to remove the costly Co and enhance the electrical conductivity. This paper will focus on the electrically conductive coating’s compatibility with LSCF in high-temperature operating environments.

Choi, Jung-Pyung↗