DOE OSTI2024

Platinum on High-Entropy Aluminate Spinels as Thermally Stable CO Oxidation Catalysts

Thermal degradation is a leading cause of automotive catalyst deactivation. Because high-entropy oxides are uniquely stabilized at high temperatures via an increase in configurational entropy, these materials may offer new mechanisms for preventing the thermal deactivation of precious metal catalysts. In this work, we evaluated platinum loaded on simple and high-entropy aluminate spinels (MAl 2 O 4 , where M = Co, Cu, Mg, Ni, or mixtures thereof) in carbon monoxide oxidation before and after aging at 800 °C. Pt supported on all simple spinels showed significant deactivation after thermal aging compared to the fresh samples, with T 90 increasing by at least 60 °C. However, Pt on high-entropy spinels had nearly the same or better activity after aging, with T 90 increasing by only 6 °C at most. During aging and reduction, copper exsolved from the spinel supports and alloyed with platinum. This interaction promoted low temperature oxidation activity, presumably through weakened CO binding, but did not prevent deactivation. On the other hand, Co, Mg, and Ni constituents promoted stronger CO bonding, as evidenced by apparent negative order kinetics and poor activity at low temperatures. High-entropy spinels, containing a variety of active metals, displayed synergetic reactant adsorption capacity and cooperative effects with supported platinum particles, which collectively prevented thermal deactivation.

CO oxidation↗

DOE OSTI2021

Engineering catalyst supports to stabilize PdO x two-dimensional rafts for water-tolerant methane oxidation

The treatment of emissions from natural gas engines is an important area of research since methane is a potent greenhouse gas. The benchmark catalysts, based on Pd, still face challenges such as water poisoning and long-term stability. In this work, we report an approach for catalyst synthesis that relies on the trapping of metal single atoms on the support surface, in thermally stable form, to modify the nature of further deposited metal/metal oxide. By anchoring Pt ions on a catalyst support we can tailor the morphology of the deposited phase. In particular, two-dimensional (2D) rafts of PdO x are formed, resulting in higher reaction rates and improved water tolerance during methane oxidation. The results show that modifying the support by trapping single atoms could provide an important addition to the toolkit of catalyst designers for controlling the nucleation and growth of metal and metal oxide clusters in heterogeneous catalysts.

2D raft↗

DOE OSTI2021

Achieving high ethylene yield in non-oxidative ethane dehydrogenation

Steam cracking of ethane, a non-catalytic thermochemical process, remains the dominant means of ethylene production. The severe reaction conditions and energy expenditure involved in this process incentivize the search for alternative reaction pathways and reactor designs which maximize ethylene yield while minimizing cost and energy input. Herein, we report a comparison of catalytic and non-catalytic non-oxidative dehydrogenation of ethane. We achieve ethylene yields as high as 67 % with an open tube quartz reactor without the use of a catalyst at residence times ~4 s. The open tube reactor design promotes simplicity, low cost, and negligible coke formation. Pristine quartz tubes were most effective, since coke formation was detected when defects were introduced by scratching the surface of the quartz. Surprisingly, the addition of solids to the quartz tube, such as quartz sand, alumina powder, or even Pt-based intermetallic catalysts, led to lower ethylene yield. Pt alloy catalysts are effective at lower temperatures, such as at 575 °C, but conversion is limited due to thermodynamic constraints. When operated at industrially relevant temperatures, such as 700 °C and above, these catalysts were not stable in our tests, causing ethylene yield to drop below that of the open tube. Furthermore, these results suggest that future research on non-oxidative dehydrogenation should be directed at optimizing reactor designs to improve the conversion of ethane to ethylene, since this approach shows promise for decentralized production of ethylene from natural gas deposits.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Towards defect engineering in hexagonal MoS 2 nanosheets for tuning hydrogen evolution and nitrogen reduction reactions

Combined computational and experimental approaches were used to evaluate defective 2H-MoS 2 nanosheets for their activity and selectivity for hydrogen evolution reaction (HER) and nitrogen reduction reaction (NRR). Density functional theory calculations were used to understand the relationship between HER and NRR activity on the ideal basal MoS 2 plane, seven grain-boundaries, ten single-/few-atom vacancies and anti-sites, and zigzag and armchair edge sites. The results confirm that 2H-MoS 2 should contain several defects with high activity for HER: armchair and zigzag edges, VS vacancy, MoS 2 anti-site, and S-S and Mo-Mo grain boundaries. Considering Gibbs free energy change for all the steps in the NRR mechanism and kinetic barriers for a key NRR step, we have found that activation of perspective NRR selective sites in 2H-MoS 2 , namely V MoS6 and clusters of S-vacancies, would require large overpotential, conditions at which HER dominates. The DFT conclusions are supported by the electrochemical studies of NRR activity and selectivity under aqueous conditions, which show an increase in NRR activity but a decrease in Faradaic efficiency as applied cell potential becomes more negative. The results of this work therefore highlight the challenges in activating natural 2H-MoS 2 for NRR, which would require additional material engineering or reaction condition optimization as a way to suppress HER, decrease the NRR overpotential or preferentially both.

2H-MoS2↗