Engineering topics
Publications and source records attributed to Christian, J. D..
Microwave discharge plasmas take place within heated zone. Changes in weight of specimens in plasma as well as temperature of sample and plasma can be obtained, facilitating determinations of reaction rates and recombination coefficients.
An apparatus is described which is used for the controlled production, characterization, and study of dissociated gases in a microwave discharge at elevated temperatures. A unique feature is the ability to produce and study a microwave discharge plasma in the heated zone. This allows elevated temperature reactions to be studied in high concentrations of dissociated gases. Further, the system permits weight change measurements of specimens in the plasma, thus facilitating reaction rate determinations. Included is a description of a cavity for use on a 50-mm diameter cylindrical reactor. The effects of flow rate, pressure, temperature, power, metal sample, and sampling position on dissociation percentage of oxygen in the apparatus are described as well as a technique for sample temperature measurements in the plasma which permits determination of high temperature recombination coefficients and reaction rates.
Explore the source record for details and available documents.
Silicone-rubber adhesive is applied externally to seal hair-line cracks in sections of high vacuum system while system is partially evacuated. No pretreatment of surface is required since adhesive will be drawn into crack while diffusion or ion pump is off.
The use of silicone rubber adhesive (particularly, G.E. RTV-108) for sealing large leaks in high vacuum systems subject to mechanical and thermal stresses is shown to be more effective than that of epoxy cements. The sealant is applied externally to the leak while the system is partially evacuated so that it is drawn into the hole.
The oxidation of nickel by atomic oxygen at pressure from 1 to 45 N/sq m between 1050 and 1250 K was investigated. In these ranges, the oxidation was found to follow the parobolic rate law, viz., K sub p = 0.0000114 exp(-13410/T) g squared/cm4/sec for films of greater than 1 micron thickness and was pressure independent. The activation enthalpy for the oxidation reaction was 112 + or - 11 kj/mole (27 + or - 3 kcal/mole). Of a number of possible mechanisms and defect structures considered, it was shown that the most likely was a saturated surface defect model for atomic oxidation, based on reaction activation enthalpies, impurity effects, pressure independence, and magnitudes of rates. A model judged somewhat less likely was one having doubly ionized cationic defects rate controlling in both atomic and molecular oxygen. From comparisons of the appropriate processes, the following enthalpy values were derived: enthalpy of activation (Ni diffusion in Ni0) = 110 + or - 30 kj/mole and standard enthalpy change for reaction formation (doubly ionized cation vacancies in Ni0 from atomic oxygen)= -9 + or - 25 kj/mole.
Derivation of equations relating the different variables involved in gas quantity measurements by liquid displacement from a Mariotte flask. The results are used to elucidate design criteria and operational procedures required for the realization of various degrees of desired accuracy down to 0.01%.
Mariotte bottle as liquid displacement device was used to measure gas volumes at flow rates that are far below threshold of wet test gas meters. Study of factors affecting amount of liquid displaced by gas flow was completed, and equations were derived which relate different variables.