NASA NTRS1982

Optical conductivity of alpha-Mn

The optical constants were measured at room temperature in the photon-energy range 0.6-6.5 eV on evaporated thin films. Evaporation conditions were chosen that gave the alpha-Mn crystal structure with relatively large grains. The optical conductivity was separated into intraband and interband contributions by fitting to the Drude formula at low energies. The results are anomalous in comparison to other 3d transition metals: the free-electron lifetime is exceptionally short (in agreement with the large dc resistivity of Mn), and the interband transitions seem unusually weak at the lower energies. Possible explanations related to the complicated crystal structure of alpha-Mn with its loss of point symmetry at the atom sites are discussed.

Scoles, K. J.↗
NASA NTRS1982

Optical conductivity of alpha-Mn

The optical constants were measured at room temperature in the photon-energy range 0.6 to 6.5 eV on evaporated thin films. Evaporation conditions were chosen that gave the alpha-Mn crystal structure with reasonably large grains. The optical conductivity was separated into intraband and interband contributions by fitting to the Drude formula at low energies. The results are anomalous in comparison to other 3d transition metals. The free-electron lifetime is exceptionally sort (in agreement with the large dc resistivity of Mn), and the interband transitions seem unusually weak at the lower energies. Possible explanations related to the complicated crystal structure of alpha-Mn are discussed.

Scoles, K. J.↗
NASA NTRS1982

Optical conductivity of amorphous Ta and beta-Ta films

Tantalum films evaporated in high vacuum onto liquid-nitrogen-cooled substrates had an amorphous structure that persisted even after warming to room temperature. The optical conductivity (as well as the dc conductivity) of the amorphous films differed significantly from that of the bcc films.

Nestell, J. E., Jr.↗
NASA NTRS1981

Intraband optical conductivity sigma/omega,T/ of Cu, Ag, and Au - Contribution from electron-electron scattering

The frequency and temperature dependence of the intraband optical conductivity of the noble metals Cu, Ag and Au is measured and contributions of electron-electron scattering are assessed. Optical measurements were performed at temperatures of 77, 295 and 425 K to obtain values of the Drude electron scattering rate with a linear dependence on temperature which may be attributed to electron-phonon scattering, and a quadratic dependence on photon energy, which is suggestive of electron-electron scattering but is a factor of two to three times greater than would be expected. Comparison of the optical data with dc electrical and thermal resistivity data which also show behavior attributed to electron-electron scattering reveals discrepancies of up to an order of magnitude. Other possible mechanisms for the frequency dependence, including absorptance, electron-surface plasmon interactions, a two-carrier model, and a structure dependence are considered, and it is concluded that the frequency dependence in the Drude scattering rates of the noble metals is not yet quantitatively understood

Parkins, G. R.↗
NASA NTRS1980

Structure and optical properties of evaporated films of the Cr- and V-group metals

Thin films of Cr, Mo, and W rapidly evaporated in high vacuum (5 x 10 to the -7th torr) onto room-temperature substrates show anomalously low reflectance (compared to bulk samples). From electron and X-ray diffraction and electron microscopy, the normal bcc crystal structure is found, but with very fine grains. Columnar grains about 100 A in diameter were separated by a less dense grain-boundary network about 10-A wide. The measured optical conductivity agrees with an inhomogeneous-medium model that assumes the normal crystalline conductivity for the grain interiors, with model parameters that correlate to the observed columnar grain size. In contrast, V and Nb films rapidly evaporated onto room-temperature substrates have the reflectance of bulk crystalline material. On liquid-nitrogen temperature substrates, however, V and Nb have normal bcc crystal structure but with small flat-plate grains, and the same model, with appropriate parameters, accounts for the optical conductivity. The difference between these two groups apparently depends on residual gases segregated at the grain boundaries in the Cr-group films.

Nestell, J. E., Jr.↗
NASA NTRS1972

Electron-beam-deposited thin polymer films - Electrical properties vs bombarding current.

Polymer films about 150 A thick, deposited on glass substrates by electron bombardment of tetramethyltetraphenyltrisiloxane, were studied, after being sandwiched between evaporated aluminum electrodes, the top one semitransparent. The capacitance, conductance, and photoconductance of the sandwiches were measured at room temperature as a function of the electron bombarding current which formed the polymer. The polymer thickness was obtained independently from Christy's (1960) empirical formula for the rate of formation. The obtained results indicate that, with increasing bombarding current, the polymer undergoes an increase in both crosslinking bonds and dangling bonds. Exposure to air drastically reduces the density of dangling bonds, but does not affect the crosslinking.

Babcock, L. E.↗