DOE OSTI2026

Exploring the tempering behaviour of additively manufactured high-alloy tool steel using synchrotron X-ray and neutron techniques

Post-processing heat treatment provides a critical pathway toward the commercialisation of additively manufactured (AM) S390 high-speed steel, which is a representative high-alloy tool steel employed in precision manufacturing, offering up to 1.5 times longer tool life and over 20% higher cutting speeds compared to conventional grades. In this study, the phase evolution of AM S390 steel during heat treatment, with particular emphasis on carbide precipitation behaviour, was systematically investigated using a combination of synchrotron X-ray and neutron techniques. The metastable M2C carbides were found to dissolve during austenitisation, while the stable primary carbides MC and M6C experienced coarsening with an average size increase of about 60 nm after just 2 min of tempering. Moreover, the austenite lattice parameters reduced from 3.618 to 3.608 Å within the first 10 min of tempering, suggesting carbon depletion in the steel matrix was likely associated with the formation of secondary carbides. This interpretation was substantiated by small-angle scattering results, which revealed the presence of nanoscale precipitates with a volume fraction of 3.1% after 60 min of tempering. These microstructural evolutions collectively accounted for the observed peak hardness of 921 HV. Furthermore, a comparative analysis of synchrotron and neutron small-angle scattering data highlighted the complementary strengths of each technique, offering critical insight into their suitability for characterising nanoscale features in AM high-alloy steels.

Synchrotron X-ray diffraction↗

DOE OSTI2026

Solid-state transformations during laser directed energy deposition of Ti-6Al-4V powder hydride-dehydrided from scrap metals

During laser directed energy deposition (DED-LB), thermal cycling and powder chemical composition produce distinct thermal histories, which vary mechanical properties. Using real-time X-ray diffraction, this study investigates solid-state transformations during DED-LB to understand process-structure-property relationships for angular Ti-6Al-4V powder hydride–dehydrided from scrap metals. Results showed that regions near the molten pool experienced high cooling rates, leading to martensitic transformation from the β phase and increased hardness. Regions farther from the molten pool underwent tempering without solid-state transformation and decreased hardness. These findings support alternative feedstocks for metal additive manufacturing for a circular economy and resilient supply chains.

Additive manufacturing (AM)↗

DOE OSTI2023

Combining synchrotron X-ray diffraction, mechanistic modeling and machine learning for in situ subsurface temperature quantification during laser melting

Laser melting, such as that encountered during additive manufacturing, produces extreme gradients of temperature in both space and time, which in turn influence microstructural development in the material. Qualification and model validation of the process itself and the resulting material necessitate the ability to characterize these temperature fields. However, well established means to directly probe the material temperature below the surface of an alloy while it is being processed are limited. To address this gap in characterization capabilities, a novel means is presented to extract subsurface temperature-distribution metrics, with uncertainty, from in situ synchrotron X-ray diffraction measurements to provide quantitative temperature evolution data during laser melting. Temperature-distribution metrics are determined using Gaussian process regression supervised machine-learning surrogate models trained with a combination of mechanistic modeling (heat transfer and fluid flow) and X-ray diffraction simulation. The trained surrogate model uncertainties are found to range from 5 to 15% depending on the metric and current temperature. The surrogate models are then applied to experimental data to extract temperature metrics from an Inconel 625 nickel superalloy wall specimen during laser melting. The maximum temperatures of the solid phase in the diffraction volume through melting and cooling are found to reach the solidus temperature as expected, with the mean and minimum temperatures found to be several hundred degrees less. The extracted temperature metrics near melting are determined to be more accurate because of the lower relative levels of mechanical elastic strains. However, uncertainties for temperature metrics during cooling are increased due to the effects of thermomechanical stress.

36 MATERIALS SCIENCE↗