Effect of impurities on hydrogen defect stability and migration barrier in yttrium dihydride crystal

The impurity or alloying atoms in YH 2 can alter the local electronic structure and so the hydrogen defect stability, as well as the H migration barrier energy. Thus, DFT calculations were employed to determine the effect of foreign elements from alkali and alkaline earth metals to transition metals and one critical impurity element, O, on H vacancy stability and retention characteristics in YH2. Results revealed that alloying elements act as hydrogen vacancy sinks by reducing the vacancy formation energy at neighboring sites. The implantation of non-magnetic foreign elements (s1, s2, and d10 valence electrons) in hydrogen energy landscape was calculated to be minor; while the hydrogen vacancy formation energy was reduced from 1.37 eV to 1.00 eV, the migration energy barrier of hydrogen was increased from 0.87 eV to 1.15 eV for non-magnetic foreign elements. The migration energy barrier monotonically decreased with increasing d-shell occupancy, reaching as low as 0.4 eV for Cr, Mo(d4), and Fe (d4). Alloying with late transition metals (d8 and d9) moderately impacted the hydrogen vacancy formation. Finally, it was found to be O addition into the YH 2- lattice did not alter the energy landscape of hydrogen vacancies. Since alloyed YH 2 has not been studied extensively, this study provides an atomistic understanding how alloying elements and impurities trap vacancies and affects hydrogen mobility YH 2 . Meanwhile, the main findings of this study may serve as guidelines for introducing alloying elements in ZrH 2 as well.

08 HYDROGEN↗

DOE OSTI2024

Hydrogen permeation in iron-chromium-aluminum (FeCrAl) alloys and the effects of microstructure and surface oxide

Iron–chromium–aluminum (FeCrAl) class alloys are candidates for use as cladding for accident-tolerant fuels and moderators. In this context, hydrogen isotope permeation in FeCrAl alloys is an important material property. Here, in the present work, the apparent permeability, effective diffusivity, and apparent solubility of hydrogen in the FeCrAl alloys C26M and Kanthal D (KD) were measured with gas-driven hydrogen permeation. Permeation measurements were conducted at temperatures of 400 to 700 °C and at gas-driven pressures from 1 to 100 kPa. In particular, the effect of grain size on hydrogen transport was studied with KD samples with three different microstructures: nanocrystalline (NC), ultra-fine grained (UFG), and coarse-grained (CG). The UFG and NC specimens had higher apparent activation energies (73.4 kJ mol -1 and 65.2 kJ mol -1 , respectively) for hydrogen permeability than the CG sample (46.9 kJ mol -1 ). An aluminum oxide layer formed on the primary- and secondary-side surfaces of all samples subjected to permeation experiments which demonstrated the propensity of FeCrAl alloys to form these innate oxide permeation barriers.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Community Data Contribution to M.E.T.A. with ATF-relevant Hydrided Zr cladding (Coated and Uncoated)

Since the aftermath of the Fukushima Daiichi loss-of-coolant accident, accident-tolerant fuel (ATF) claddings have been developed to improve the coping times in such events. However, the mechanical performance of ATF cladding is crucial in ensuring that it does not negatively impact the mechanical integrity during all other stages of the nuclear fuel cycle, and the validity of the existing safe operating margins must be verified. However, due to the cladding’s tube geometry and textured anisotropy, determination of apparent mechanical properties under certain deformation paths is challenging. In the uniaxial hoop direction, for instance, the measured mechanical stresses include frictional forces caused by loading mandrels or varying deformation paths in the sample during traditional ring tensile testing. This experimental difficulty is exacerbated by the specimen size. However, addressing these challenges enables irradiation separate-effects investigations in which the materials can be inserted in reactors like the High Flux Isotope Reactor, and reducing the material consumption of commercially irradiated material allows for further post-irradiation examinations. Despite the advantages of reduced-scale mechanical testing, any drawbacks from new specimen geometries must be evaluated, and uncertainties from specimen preparation, setup, and analysis methodologies must be understood.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Report on RIA Relevant Modified Burst Testing of ATF Cladding Materials

The mechanical performance of accident-tolerant fuel (ATF) cladding candidates in light-water reactors (LWRs) must be similar to or better than that of current conventional nuclear fuel claddings to reduce dose to the public and ensure a that the core coolable geometry is maintained during a postulated reactivity-initiated accident (RIA) in light-water reactors (LWRs). During an RIA event, the rapid thermal expansion of nuclear fuel can deform the cladding once the fuel–cladding gap closes. In some cases, the pellet–cladding mechanical interaction (PCMI) can induce mechanical failure in ATF candidates. Thus, the mechanical response of ATF cladding must be investigated by mimicking the conditions of RIA and potentially performing Transient Reactor Test (TREAT) experiments to establish or verify the safety envelope. The work presented in this report investigated the failure behavior of as-received, hydrided, and chromium-coated (Cr-coated) Zircaloy-4 (Zry-4) cladding tube under strain-driven mechanical conditions, mimicking postulated RIA loading conditions. Mechanical testing was performed at 300°C via modified burst test (MBT) equipment with pulse width control previously developed under the Department of Energy’s (DOE’s) Advanced Fuel Campaign (AFC). The mechanical strains were determined using 2D digital image correlation (DIC) techniques. The base Zry-4 acquired by Cameco Inc. was in stress-relieved annealed (SRA) condition. Because of the observed large deformation of the cladding tubes, the failure strain definition was updated for the MBT, which can also be applied to other tube tests where significant bulging (out-of-plane deformation) is present. The failure strain was determined to be affected by the speed of the test or the RIA event. As the RIA-like event duration decreased from 75 to 15 ms, the failure strain decreased 5, 7 and 1% for as-received, hydrided, and Cr-coated specimens, respectively. Fractography on the Cr-coated specimens indicated the presence of two failure mechanisms: (i) crenulation at the outer surface of the coating due to the tensile tractional forces along with coatings grain microstructure and (ii) formation of critical defect at the coating/cladding interface that initiated coating rupture after severe plastic deformation of the Zry- 4 substrate. Based on the MBT results and fractography observations, performing mechanical property testing at high strain rates—in particular on Cr-coated tubes—and semi-integral TREAT experiments are required future efforts to ensure ATF cladding performance during transients. The testing recommended would also inform the development of long-term generalized cladding technologies.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2024

Hydrogen transport in yttrium hydride under asymmetric heat

Metal hydrides are a promising moderator material for high temperature fission reactors. Yttrium hydride can be loaded to a high hydrogen density with relatively high hydrogen stability at temperatures up to 800°C. This makes yttrium hydride a potential moderator material for microreactors as foreseen in the fission surface power program. However, during the operation of such advanced reactors temperature gradients are expected which can change the local hydrogen density in the moderator. Hydrogen diffusion in metals is driven by a concentration gradient (Fick’s law) and thermal diffusion (Soret diffusion). Thermal diffusion is the transport of hydrogen, or other species, due to a temperature gradient. For example, hydrogen might migrate from the hot side of a sample to the cold side of a sample. Measuring Fickian diffusion is achieved through various permeation or absorption experiments, however measuring thermal diffusion is challenging and has rarely been performed. The Hydrogen Experimental Apparatus for Thermal Diffusion (HEATD) experiment is designed to induce thermal diffusion in samples and quench those samples so that the hydrogen distribution can be analyzed using hot vacuum extraction (HVE). One side of the sample was heated to a high temperature e.g., 800°C, while the other side of the sample is at a lower temperature. The sample was held under the applied temperature gradient for a given time until the anticipated hydrogen diffusion has occurred. The actual time depends depend on the sample composition and hydrogen concentration. The results from HVE showed that thermal diffusion took place in the specimen and the Soret coefficient was calculated.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Micromechanical aspects of deformation and failure of advanced Iron-Chromium-Aluminum alloys

Here this work investigates the micromechanical deformation and failure mechanisms of advanced FeCrAl alloys developed for use in nuclear reactors as cladding material. Three different FeCrAl alloys (82-X)Fe-13Cr-5Al-X (X=Nb, TiC, 0 for base alloy) were investigated both in their as-received and welded states. In-situ neutron diffraction with simultaneous digital image correlation was used to determine micromechanical deformation mechanisms not only as a function of elemental composition but also as a condition of state (as-received vs. welded). Ex-situ X-ray computed tomography was used on as-deformed samples to help determine the failure mechanisms and void initiation strains.

36 MATERIALS SCIENCE↗