NASA NTRS2004

Detached Growth of Germanium by Directional Solidification

Detached crystal growth technique (dewetting) offers improvement in the quality of the grown crystals by preventing sticking to the walls of the crucible and thus reducing the possibility of parasitic nucleation and formation of lattice defects upon cooling. One of the factors relevant for the phenomena is the pressure differential across the meniscus at the crystal-melt interface. We investigated this effect experimentally. The growth took place in closed ampoules under the pressure of an inert gas (forming gas: 96% Ar + 4% H2). The pressure above the melt was adjustable and allowed for a control of the pressure difference between the top and bottom menisci. The crystals were characterized, particularly by taking profilometer measurements along the grown crystals surface. The effects of the experimental conditions on the detachment were compared with those predicted based on the theory of Duffar et al.

Palosz, W.↗

NASA NTRS2004

Detached Growth of Germanium by Directional Solidification

The conditions of detached solidification under controlled pressure differential across the meniscus were investigated. Uncoated and graphite- or BN-coated silica and pBN crucibles were used. Detached and partly detached growth was achieved in pBN and BN-coated crucibles, respectively. The results of the experiments are discussed based on the theory of Duffar et al.

Palosz, W.↗

NASA NTRS2002

First Materials Science Research Facility Rack Capabilities and Design Features

The first Materials Science Research Rack (MSRR-1) is the primary facility for U.S. sponsored materials science research on the International Space Station. MSRR-1 is contained in an International Standard Payload Rack (ISPR) equipped with the Active Rack Isolation System (ARIS) for the best possible microgravity environment. MSRR-1 will accommodate dual Experiment Modules and provide simultaneous on-orbit processing operations capability. The first Experiment Module for the MSRR-1, the Materials Science Laboratory (MSL), is an international cooperative activity between NASA's Marshall Space Flight Center (MSFC) and the European Space Agency's (ESA) European Space Research and Technology Center (ESTEC). The MSL Experiment Module will accommodate several on-orbit exchangeable experiment-specific Module Inserts which provide distinct thermal processing capabilities. Module Inserts currently planned for the MSL are a Quench Module Insert, Low Gradient Furnace, and a Solidification with Quench Furnace. The second Experiment Module for the MSRR-1 configuration is a commercial device supplied by MSFC's Space Products Development (SPD) Group. Transparent furnace assemblies include capabilities for vapor transport processes and annealing of glass fiber preforms. This Experiment Module is replaceable on-orbit. This paper will describe facility capabilities, schedule to flight and research opportunities.

Cobb, S.↗

NASA NTRS2001

Contact Angles and Surface Tension of Germanium-Silicon Melts

Precise knowledge of material parameters is more and more important for improving crystal growth processes. Two important parameters are the contact (wetting) angle and the surface tension, determining meniscus shapes and surface-tension driven flows in a variety of methods (Czochralski, EFG, floating-zone, detached Bridgman growth). The sessile drop technique allows the measurement of both parameters simultaneously and has been used to measure the contact angles and the surface tension of Ge(1-x)Si(x) (0 less than or equal to x less than or equal to 1.3) alloys on various substrate materials. Fused quartz, Sapphire, glassy carbon, graphite, SiC, carbon-based aerogel, pyrolytic boron nitride (pBN), AIN, Si3N4, and polycrystalline CVD diamond were used as substrate materials. In addition, the effect of different cleaning procedures and surface treatments on the wetting behavior were investigated. Measurements were performed both under dynamic vacuum and gas atmospheres (argon or forming gas), with temperatures up to 1100 C. In some experiments, the sample was processed for longer times, up to a week, to investigate any changes of the contact angle and/or surface tension due to slow reactions with the substrate. For pure Ge, stable contact angles were found for carbon-based substrates and for pBN, for Ge(1-x)Si(x) only for pBN. The highest wetting angles were found for pBN substrates with angles around 170deg. For the surface tension of Ge, the most reliable values resulted in gamma(T) = (591- 0.077 (T-T(sub m)) 10(exp -3)N/m. The temperature dependence of the surface tension showed similar values for Ge(1-x)Si(x), around -0.08 x 10(exp -3)N/m K, and a compositional dependence of 2.2 x 10(exp -3)N/m at%Si.

Croell, A.↗

NASA NTRS2001

First Materials Science Research Rack Capabilities and Design Features

The first Materials Science Research Rack (MSRR-1) will accommodate dual Experiment Modules (EM's) and provide simultaneous on-orbit processing operations capability. The first international Materials Science Experiment Module for the MSRR-1 is an international cooperative research activity between NASA's Marshall Space Flight Center (MSFC) and the European Space Agency's (ESA) European Space Research and Technology Center. (ESTEC). This International Standard Payload Rack (ISPR) will contain the Materials Science Laboratory (MSL) developed by ESA as an Experiment Module. The MSL Experiment Module will accommodate several on-orbit exchangeable experiment-specific Module Inserts. Module Inserts currently planned are a Quench Module Insert, Low Gradient Furnace, Solidification with Quench Furnace, and Diffusion Module Insert. The second Experiment Module for the MSRR-1 configuration is a commercial device supplied by MSFC's Space Products Department (SPD). It includes capabilities for vapor transport processes and liquid metal sintering. This Experiment Module will be replaced on-orbit with other NASA Materials Science EMs.

Schaefer, D.↗

NASA NTRS2000

Materials Science Research Hardware for Application on the International Space Station: an Overview of Typical Hardware Requirements and Features

NASA's Marshall Space Flight Center (MSFC) is the lead center for Materials Science Microgravity Research. The Materials Science Research Facility (MSRF) is a key development effort underway at MSFC. The MSRF will be the primary facility for microgravity materials science research on board the International Space Station (ISS) and will implement the NASA Materials Science Microgravity Research Program. It will operate in the U.S. Laboratory Module and support U. S. Microgravity Materials Science Investigations. This facility is being designed to maintain the momentum of the U.S. role in microgravity materials science and support NASA's Human Exploration and Development of Space (HEDS) Enterprise goals and objectives for Materials Science. The MSRF as currently envisioned will consist of three Materials Science Research Racks (MSRR), which will be deployed to the International Space Station (ISS) in phases, Each rack is being designed to accommodate various Experiment Modules, which comprise processing facilities for peer selected Materials Science experiments. Phased deployment will enable early opportunities for the U.S. and International Partners, and support the timely incorporation of technology updates to the Experiment Modules and sensor devices.

Schaefer, D. A.↗

NASA NTRS2000

Detached and Floating-Zone Growth of Semiconductor Crystals on the ISS

Understanding the mechanism of detached Bridgman growth and establishing the growth of large scale germanium-silicon crystals by the float-zone technique are the key points of the project "RDGS - Reduction of Defects in Germanium-Silicon". The contact angle of the melt and the growth angle of the crystal are essential parameters which allow a controlled use of detached growth. The contact angle was determined for a variety of different substrates and melt compositions; pBN showed the highest value for pure germanium as well as for germanium-rich GeSi melts. The growth angle of Ge(sub 0.95) Si(sub 0.05) was measured to be 8.5-10.5 degrees which concurs with the values of pure germanium and silicon, respectively. The temperature dependence and the concentration dependence of the surface tension were determined for concentrations up to 10at% silicon (partial derivative (gamma)/partial derivative T=-0.08 (raised dot) 10(exp -3)N/m (raised dot) K, partial derivative (gamma)/partial derivative (C)=2.2 (raised dot) 10(exp -3)N/m (raised dot) at%). Using these values, the critical Marangoni number indicating the transition to time-dependent thermocapillary flow will be exceeded for the growth of large scale float-zone crystals onboard the ISS. Therefore, suitable tools for flow control are required.

Dold, P.↗