Shelf-Stable Bingham Plastic Polyurethane Thermosets for Additive Manufacturing

Here, this study presents an innovative 3D-printing method for fabricating hybrid-hardness polyurethane (PU) thermosets via direct-ink writing (DIW). This method features an unprecedentedly long pot-life of at least 16 months for uncured material, achieved by employing internally-blocked polymeric uredines as the isocyanate source. This innovation not only extends pot life but also broadens the pre-print processing temperature range. Surface-modified fumed silica, used as a rheology modifier, ensures the maintenance of Bingham fluid characteristics. Rigorous evaluations, including DSC, tensile tests, SEM, OM, and μ-CT, verify the material’s uniform and nearly isotropic structure, devoid of defects. DMA analysis reveals that these 3D-printed PUs withstand processing temperatures up to 240°C. The practical application of this technology is demonstrated through the successful 3D printing of a shoe sole, showcasing the ability to incorporate regions of varying hardness, highlighting the versatile property customization of this method.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Dihydroxyterephthalate—A Trojan Horse PET Counit for Facile Chemical Recycling

Abstract Here, low‐energy poly(ethylene terephthalate) (PET) chemical recycling in water: PET copolymers with diethyl 2,5‐dihydroxyterephthalate (DHTE) undergo selective hydrolysis at DHTE sites, autocatalyzed by neighboring group participation, is demonstrated. Liberated oligomeric subchains further hydrolyze until only small molecules remain. Poly(ethylene terephthalate‐ stat ‐2,5‐dihydroxyterephthalate) copolymers were synthesized via melt polycondensation and then hydrolyzed in 150–200 °C water with 0–1 wt% ZnCl 2 , or alternatively in simulated sea water. Degradation progress follows pseudo‐first order kinetics. With increasing DHTE loading, the rate constant increases monotonically while the thermal activation barrier decreases. The depolymerization products are ethylene glycol, terephthalic acid, 2,5‐dihydroxyterephthalic acid, and bis(2‐hydroxyethyl) terephthalate dimer, which could be used to regenerate virgin polymer. Composition‐optimized copolymers show a decrease of nearly 50% in the Arrhenius activation energy, suggesting a 6‐order reduction in depolymerization time under ambient conditions compared to that of PET homopolymer. This study provides new insight to the design of polymers for end‐of‐life while maintaining key properties like service temperature and mechanical properties. Moreover, this chemical recycling procedure is more environmentally friendly compared to traditional approaches since water is the only needed material, which is green, sustainable, and cheap.

36 MATERIALS SCIENCE↗