NASA NTRS1985

Environmental exposure effects on composite materials for commercial aircraft

The effects of environmental exposure on composite materials are determined. The environments considered are representative of those experienced by commercial jet aircraft. Initial results have been compiled for the following material systems: T300/5208, T300/5209, and T300/934. Future results will include AS-1/3501-6 and Kevlar 49/F161-188. Specimens are exposed on the exterior and interior of 737 airplanes of three airlines, and to continuous ground-level exposure at four locations. In addition, specimens are exposed in the laboratory to conditions such as: simulated ground-air-ground, weatherometer, and moisture. Residual strength results are presented for specimens exposed for up to five years at five ground-level exposure locations and on airplanes from one airline.

Coggeshall, R. L.↗

NASA NTRS1985

The 737 graphite composite flight spoiler flight service evaluation

The flight service experience of 111 graphite-epoxy spoilers on 737 transport aircraft and related ground based environmental exposure of graphite-epoxy material specimens is covered. Spoilers have been installed on 28 aircraft representing seven major airlines operating throughout the world. An extended flight service evaluation program of 15 years is presently underway. As of December 1984, a total of 2,092, 155 spoiler flight hours and 2,954,814 spoiler landings had been accumulated by this fleet.

Coggeshall, R. L.↗

NASA NTRS1982

The 737 graphite composite flight spoiler flight service evaluation

A flight service report was prepared which covers the flight service experience of 111 graphite epoxy spoilers on 737 transport aircraft and related ground based environmental exposure of graphite epoxy material specimens. Spoilers were installed on 28 aircraft representing seven major airlines operating throughout the world. Tests of removed spoilers after the seventh year of service continue to indicate modest changes in composite strength properties. Two spoilers were tested, one with 6 and one with 7 years of service, and both had residual strengths that fall within the original static strength scatter band. Both these units had typical service included discrepancies when tested. Based on visual, ultrasonic, and destructive inspection there continues to be no evidence of moisture migration into the honeycomb core and no core corrosion in the deployed units.

Coggeshall, R. L.↗